US4077904A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Olefin polymerization process and catalyst therefor
Assignee: Union Carbide Corp
•
Filing: 1976-06-29
•
Granted: 1978-03-07
•
Expires: 1996-06-29
Abstract
Abstract Catalysts for the polymerization of ethylene and the copolymerization of ethylene with other olefins have been prepared by depositing an organo-chromium compound on a silica support which has been fluorided at low temperatures.
Inventors
- 👤 Allen Noshay
- 👤 Frederick John Karol
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:13
CPC Classifications
C; C08; C08F; C08F10/00; C08F10/02
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
191 words
Catalyst composition comprising at least one organo-chromium compound having the structure: Ar.sub.1 - Cr (II) - Ar.sub.1 wherein Ar 1 is a monovalent radical selected from the group consisting of: (1) cyclopentadienyl radicals having the structure: ##STR4## wherein R is a hydrocarbon radical having 1 to about 20 carbon atoms and n is an integer having values of 0 to 5; (2) indenyl radicals having the structure: ##STR5## wherein each R a is a hydrocarbon radical having 1 to 10 carbon atoms, m is an integer having values of 0 to 4, and x is an integer having values of 0 to 3; and (3) fluorenyl radicals having the structure: ##STR6## wherein each of R b is a hydrocarbon radical having 1 to 10 carbon atoms, each of m and m" is an integer having values of 0 to 4, Y is H or R b and z is an integer having values of 0 to 1; deposited on a silica support fluorided with less than 10% by weight of a fluoridation agent, based on the weight of said support, at a temperature of about 100° C. to about 400° C.
Claim 2
Dependent Claim
191 words
Catalyst composition comprising at least one organo-chromium compound having the structure: Ar.sub.1 - Cr (II) - Ar.sub.1 wherein Ar 1 is a monovalent radical selected from the group consisting of: (1) cyclopentadienyl radicals having the structure: ##STR4## wherein R is a hydrocarbon radical having 1 to about 20 carbon atoms and n is an integer having values of 0 to 5; (2) indenyl radicals having the structure: ##STR5## wherein each R a is a hydrocarbon radical having 1 to 10 carbon atoms, m is an integer having values of 0 to 4, and x is an integer having values of 0 to 3; and (3) fluorenyl radicals having the structure: ##STR6## wherein each of R b is a hydrocarbon radical having 1 to 10 carbon atoms, each of m and m" is an integer having values of 0 to 4, Y is H or R b and z is an integer having values of 0 to 1; deposited on a silica support fluorided with less than 10% by weight of a fluoridation agent, based on the weight of said support, at a temperature of about 100° C. to about 400° C.
Claim 3
Dependent Claim
50 words
Catalyst composition claimed in claim 1 wherein the organo-chromium compound comprises a chromocene compound having the structure: ##STR7## wherein each of R and R' is a hydrocarbon radical having 1 to about 20 carbon atoms and each of n and n' is an integer having values of 0 to 5.
Claim 4
Dependent Claim
70 words
Catalyst composition claimed in claim 1 wherein the organo-chromium compound comprises a compound of the structure: Ar - Cr [II] - Ar' wherein Ar and Ar' are the same or different indenyl radicals having the structure: ##STR8## wherein each Ra is a hydrocarbon radical having 1 to 10 carbons, m is an integer having values of 0 to 4, and x is an integer having values of 0 to 3.
Claim 5
Dependent Claim
81 words
Catalyst composition claimed in claim 1 wherein the organo-chromium compound comprises a compound of the structure: Ar" - Cr [II] - Ar''' wherein Ar" and Ar''' are the same or different fluorenyl radicals having the structure: ##STR9## wherein each R b is a hydrocarbon radical having 1 to 10 carbons, each of m' and m" is an integer having values of 0 to 4, Y is H or R b and z is an integer having values of 0 to 1.
Claim 6
Dependent Claim
18 words
Catalyst composition claimed in claim 1 wherein the fluoridation agent comprises (NH 4 ) 2 SiF 6 .
Claim 7
Dependent Claim
41 words
Catalyst composition claimed in claim 5 wherein about 1 to about 9 percent by weight of (NH 4 ) 2 SiF 6 based on the weight of silica is used at a temperature of about 200° C. to about 400° C.
Claim 8
Dependent Claim
16 words
Catalyst composition claimed in claim 1 wherein the fluoridation agent comprises NH 4 BF 4 .
Claim 9
Dependent Claim
14 words
Catalyst composition claimed in claim 1 wherein the fluoridation agent comprises NH 4 F.
Claim 10
Dependent Claim
34 words
Catalyst composition claimed in claim 2 wherein the amount of chromocene compound deposited on the silica support is about 0.5 to about 10 weight percent based on the weight of the total catalyst composition.
Claim 11
Dependent Claim
23 words
Catalyst composition claimed in claim 1 wherein the silica support is fluorided at a temperature of about 200° C. to about 300° C.
Claim 12
Dependent Claim
31 words
Catalyst composition claimed in claim 1 wherein the amount of fluoridation agent used to fluoride the silica support is about 0.5 to < 10 percent based on the weight of silica.
Claim 13
Dependent Claim
81 words
Process for preparing a silica supported alpha-olefin polymerization catalyst which comprises: (a) fluoriding said silica support with less than 10 weight %, based on the weight of said support, of a fluoridation agent at a temperature of about 100° C, to about 400° C.; and (b) treating said fluorided silica support with sufficient quantities of the organo-chromium compound of claim 1 as to deposit from about 0.1 to about 3 weight percent of chromium on said support, calculated as the element.
Claim 14
Dependent Claim
22 words
Process claimed in claim 12 wherein the silica support is fluorided at a temperature of about 200° C. to about 300° C.
Claim 15
Dependent Claim
68 words
Process for preparing a silica supported alpha-olefin polymerization which comprises: (a) treating a silica support with sufficient quantities of the organo-chromium compound claimed in claim 1 as to deposit about 0.1 to about 3 weight percent of chromium on said support calculated as the element; and (b) fluoriding the treated support of (a) with a fluoridation agent at a temperature of about 100° C. to about 400° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-06 | 1981-09-05 | 1982-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-06 | 1985-09-05 | 1986-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-06 | 1989-09-05 | 1990-03-07 | $7700.00 | Window Closed / Lapsed |