Gettering device of manufacturing a color television display tube while using said gettering device, and color television display tube thus manufactured
Assignee: US Philips Corp
•
Filing: 1976-09-23
•
Granted: 1978-03-07
•
Expires: 1996-09-23
Abstract
Abstract The chemical resistance of a gettering device comprising a mixture of barium-aluminium powder and nickel powder compressed in a metal holder is considerably increased by using nickel powder having a specific surface smaller than 0.15 m 2 per gram and an average grain size smaller than 80 microns, while the barium aluminium powder has an average grain size smaller than 125 microns. The said gettering device is extremely suitable for use in the manufacture of a color display tube in which the gettering device is to be placed inside the envelope of the tube before certain parts of said envelope are sealed together at a high temperature.
Inventors
- 👤 Wilhelmus Adrianus van Gils
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 17:35
CPC Classifications
H; H01; H01J; H01J29/00; H01J29/94; H01J7/00; H01J7/14; H01J7/18; H01J7/183
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
92 words
A gettering device comprising a powder mixture of nickel and a barium-aluminium alloy, compressed in a metal holder from which barium as the gettering metal can be evaporated by heating, said mixture comprising 40 to 60% by weight of nickel powder, said nickel powder having a specific surface smaller than 0.15 m 2 per gram and an average grain size smaller than 80 microns, the barium-aluminium powder having an average grain size smaller than 125 microns, and wherein the specific surface area of said metal powder increases as the grain size decreases.
Claim 2
Dependent Claim
92 words
A gettering device comprising a powder mixture of nickel and a barium-aluminium alloy, compressed in a metal holder from which barium as the gettering metal can be evaporated by heating, said mixture comprising 40 to 60% by weight of nickel powder, said nickel powder having a specific surface smaller than 0.15 m 2 per gram and an average grain size smaller than 80 microns, the barium-aluminium powder having an average grain size smaller than 125 microns, and wherein the specific surface area of said metal powder increases as the grain size decreases.
Claim 3
Dependent Claim
29 words
A gettering device as claimed in claim 1 characterized in that the nickel powder shows a grain size distribution having an average grain size between 30 to 60 microns.
Claim 4
Dependent Claim
74 words
A gettering device as claimed in claim 1 or 2, characterized in that the nickel powder has the following grain size distribution: ______________________________________
0 percent by weight
smaller than
15 microns
0.1 - 0.2
" " 20 "
3 - 10 " " 30 "
22 - 60 " " 40 "
70 - 96 " " 50 "
86 - 99 " " 55 "
97 - 100
" " 65 "
______________________________________
Claim 5
Dependent Claim
29 words
A gettering device as claimed in any preceding claim, characterized in that 80 - 90% by weight of the barium-aluminium powder has a grain size smaller than 100 microns.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-06 | 1981-09-05 | 1982-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-06 | 1985-09-05 | 1986-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-06 | 1989-09-05 | 1990-03-07 | $7700.00 | Window Closed / Lapsed |