Process for preparing waterless printing masters
Assignee: Xerox Corp
•
Filing: 1977-03-10
•
Granted: 1978-03-07
•
Expires: 1997-03-10
Abstract
Abstract Improved waterless lithographic printing masters are provided having minimum background ink reflection density. The master comprises a crosslinked block copolymer containing elastomeric, ink releasing siloxane blocks chemically linked to organic image accepting thermoplastic blocks, said copolymer having a molecular weight for the organic blocks sufficient to provide strength and a background ink reflection density of less than 0.02 and preferably less than 0.01.
Inventors
- 👤 Thomas J. Pacansky
- 👤 Alan B. Amidon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:09
CPC Classifications
B; B41; B41N; B41N1/00; B41N1/003
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
101 words
A method of preparing a printing master comprising: a. providing a self-supporting master substrate; b. providing a block film forming ink releasing copolymer consisting of from 10 to 20 weight percent polyalphamethylstyrene having a molecular weight of between 6,000 and 11,000 and from 90 to 80 weight percent polydimethylsiloxane; c. coating said substrate with said copolymer; d. depositing an ink accepting particulate material in image configuration on said master; e. heating the master to crosslink the siloxane blocks and soften the styrene blocks; and f. allowing the coating to cool so as to bond the particulate imaging material to the master.
Claim 2
Independent Claim
101 words
A method of preparing a printing master comprising: a. providing a self-supporting master substrate; b. providing a block film forming ink releasing copolymer consisting of from 10 to 20 weight percent polyalphamethylstyrene having a molecular weight of between 6,000 and 11,000 and from 90 to 80 weight percent polydimethylsiloxane; c. coating said substrate with said copolymer; d. depositing an ink accepting particulate material in image configuration on said master; e. heating the master to crosslink the siloxane blocks and soften the styrene blocks; and f. allowing the coating to cool so as to bond the particulate imaging material to the master.
Claim 3
Dependent Claim
15 words
The process of claim 1 wherein the particulate imaging material deposited is a thermoplastic polymer.
Claim 4
Independent Claim
104 words
A method of preparing a printing master comprising: a. providing a self-supporting master substrate; b. providing a block film forming ink releasing copolymer having from 90 to 80 weight percent polydimethylsiloxane blocks and 10 to 20 weight percent polyalphamethylstyrene blocks with a molecular weight between 6,000 and 11,000; c. coating said substrate with said copolymer; d. heating the master to crosslink the siloxane blocks; e. depositing an ink accepting particulate material in image configuration on said master; f. heating the master to soften the styrene blocks; and g. allowing the coating to cool so as to bond the particulate imaging material to the master.
Claim 5
Independent Claim
104 words
A method of preparing a printing master comprising: a. providing a self-supporting master substrate; b. providing a block film forming ink releasing copolymer having from 90 to 80 weight percent polydimethylsiloxane blocks and 10 to 20 weight percent polyalphamethylstyrene blocks with a molecular weight between 6,000 and 11,000; c. coating said substrate with said copolymer; d. heating the master to crosslink the siloxane blocks; e. depositing an ink accepting particulate material in image configuration on said master; f. heating the master to soften the styrene blocks; and g. allowing the coating to cool so as to bond the particulate imaging material to the master.
Claim 6
Dependent Claim
15 words
The method of claim 3 wherein the particulate imaging material deposited is a thermoplastic polymer.
Claim 7
Dependent Claim
20 words
The method of claim 3 wherein the siloxane blocks are slightly crosslinked prior to imaging and further crosslinked after imaging.
References Cited (Backward Citations)
US3665052A
Cited
US3678125A
Cited
US3678126A
Cited
US4010687A
Cited
US3890405A
Cited
US3907562A
Cited
US3901151A
Cited
US4009032A
Cited
US4003312A
Cited
US4017581A
Cited
US4012254A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-06 | 1981-09-05 | 1982-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-06 | 1985-09-05 | 1986-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-06 | 1989-09-05 | 1990-03-07 | $7700.00 | Window Closed / Lapsed |