Resorcinol-aldehyde resins used to bind reinforcing materials such as glass fibers in shaped object form
Assignee: Shea Technology
•
Filing: 1977-07-06
•
Granted: 1978-02-28
•
Expires: 1997-07-06
Abstract
Abstract A resinous product has high resistance to flame spread, good heat release and exhibits a low smoke-developed rating when exposed to flame or to indirect or radiant heat, and is flexible, tough and resistant to cracking and embrittlement upon curing. Such a product is the condensation product of resorcinol with or without included phenol, and an admixture of paraformaldehyde and furfural or furfuryl alcohol or both. The resorcinol starting material of this invention can also suitably be used in the form of a B-stage or partially cured resin of resorcinol-phenol-formaldehyde which is then condensed with the aforesaid aldehydes or such aldehyde substance and furfuryl alcohol. The product is useful in making castings or moldings which are resistant to embrittlement or cracking upon curing, and in making tough fiberglass parts, and it can contain fillers or the like. A method of making the product and articles is provided.
Inventors
- 👤 Lawrence E. Shea
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:36
CPC Classifications
F; F16; F16L; F16L57/00; F16L57/04; C; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/26; C08; C08G; C08G16/00; C08G16/02; C08G16/025; C08G16/0256; C08G16/0262; C08G8/00; C08G8/04; C08G8/08; C08G8/20; C08G8/22; C08G8/24; C08L; C08L61/00; C08L61/04; C08L61/06; C08L61/12; C08L61/34; Y; Y10; Y10S; Y10S138/00; Y10S138/02; Y10S138/07; Y10S264/00; Y10S264/53; Y10T; Y10T428/00; Y10T428/13; Y10T428/131; Y10T428/1314; Y10T428/24; Y10T428/24149; Y10T428/31504; Y10T428/31942; Y10T428/31949; Y10T428/31957; Y10T428/3196; Y10T442/00; Y10T442/20; Y10T442/2631
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
80 words
A fire-resistive duct comprising wound glass filaments formed of rovings coated with a tough, fire-resistive resin exhibiting low flame spread and low smoke evolution under exposure to direct flame or to radient heat and being the reaction product of a partially cured resin of resorcinol, phenol and formalin, and paraformaldehyde and at least one substance chosen from the group consisting of furfural and furfuryl alcohol, said paraformaldehyde and said substance being added in amounts sufficient to provide said fire-resistive resin.
Claim 2
Dependent Claim
80 words
A fire-resistive duct comprising wound glass filaments formed of rovings coated with a tough, fire-resistive resin exhibiting low flame spread and low smoke evolution under exposure to direct flame or to radient heat and being the reaction product of a partially cured resin of resorcinol, phenol and formalin, and paraformaldehyde and at least one substance chosen from the group consisting of furfural and furfuryl alcohol, said paraformaldehyde and said substance being added in amounts sufficient to provide said fire-resistive resin.
Claim 3
Dependent Claim
98 words
A shaped hollow article comprising wound glass filaments formed of rovings coated with a tough, fire-resistive resin exhibiting low flame spread and low smoke evolution under exposure to direct flame or to radiant heat and being the reaction product of a resorcinol component chosen from the group consisting of resorcinol, a mixture of phenol and resorcinol, and a partially cured resin of resorcinol, phenol and formalin, and paraformaldehyde, and at least one substance chosen from the group consisting of furfural and furfuryl alcohol, said paraformaldehyde and said substance being added in sufficient amount to provide such fire-resistive resin.
Claim 4
Dependent Claim
98 words
A shaped hollow article comprising wound glass filaments formed of rovings coated with a tough, fire-resistive resin exhibiting low flame spread and low smoke evolution under exposure to direct flame or to radiant heat and being the reaction product of a resorcinol component chosen from the group consisting of resorcinol, a mixture of phenol and resorcinol, and a partially cured resin of resorcinol, phenol and formalin, and paraformaldehyde, and at least one substance chosen from the group consisting of furfural and furfuryl alcohol, said paraformaldehyde and said substance being added in sufficient amount to provide such fire-resistive resin.
Claim 5
Dependent Claim
63 words
A construction panel comprising a laminate of glass cloth and a fire-resistive resin which is the reaction product of 100 parts by weight of an A component which is a partially cured resin of resorcinol, phenol, and formalin, and 30 parts by weight of a B component which consists essentially of 3 parts by weight paraformaldehyde and 12 parts by weight of furfural.
Claim 6
Dependent Claim
63 words
A construction panel comprising a laminate of glass cloth and a fire-resistive resin which is the reaction product of 100 parts by weight of an A component which is a partially cured resin of resorcinol, phenol, and formalin, and 30 parts by weight of a B component which consists essentially of 3 parts by weight paraformaldehyde and 12 parts by weight of furfural.
Claim 7
Dependent Claim
14 words
The panel of claim 3 suitable for use in the interior of an airplane.
Claim 8
Dependent Claim
91 words
An article of manufacture comprising a glass fiber base impregnated with a fire-resistive resin exhibiting low flame spread and low smoke evolution under exposure to high temperatures and being the reaction product of a resorcinol component chosen from the group consisting of resorcinol, a mixture of resorcinol and phenol, and a partially cured resin of resorcinol, phenol and formalin, and paraformaldehyde plus at least one substance chosen from the group consisting of furfural and furfuryl alcohol, said paraformaldehyde and said substance being added in sufficient amounts to provide such fire-resistive resin.
Claim 9
Dependent Claim
91 words
An article of manufacture comprising a glass fiber base impregnated with a fire-resistive resin exhibiting low flame spread and low smoke evolution under exposure to high temperatures and being the reaction product of a resorcinol component chosen from the group consisting of resorcinol, a mixture of resorcinol and phenol, and a partially cured resin of resorcinol, phenol and formalin, and paraformaldehyde plus at least one substance chosen from the group consisting of furfural and furfuryl alcohol, said paraformaldehyde and said substance being added in sufficient amounts to provide such fire-resistive resin.
Claim 10
Independent Claim
165 words
A method of making a fire-resistive shaped product including tanks, ducts and pipes, which comprises: (1) coating glass roving with an admixture consisting essentially of: (a) a resorcinol component chosen from the group consisting of resorcinol, a mixture of resorcinol and phenol, and a partially cured resin of resorcinol, phenol and formalin, (b) paraformaldehyde, plus, (c) at least one substance chosen from the group consisting of furfuraldehyde and furfuryl alcohol, (d) said paraformaldehyde and said substance being each added in an amount sufficient to produce with said resorcinol component a tough, fire-resistive resin, (2) forming filaments of such coated roving, (3) winding said filaments on a form or mold to produce a shaped product, (4) curing to form of said admixture a tough, fire-resistive resin exhibiting low flame spread, good heat release and low smoke evolution when exposed to direct flame or to radiant heat and being resistant to embrittlement and cracking upon curing, and (5) removing said cured product from said form or mold.
Claim 11
Independent Claim
165 words
A method of making a fire-resistive shaped product including tanks, ducts and pipes, which comprises: (1) coating glass roving with an admixture consisting essentially of: (a) a resorcinol component chosen from the group consisting of resorcinol, a mixture of resorcinol and phenol, and a partially cured resin of resorcinol, phenol and formalin, (b) paraformaldehyde, plus, (c) at least one substance chosen from the group consisting of furfuraldehyde and furfuryl alcohol, (d) said paraformaldehyde and said substance being each added in an amount sufficient to produce with said resorcinol component a tough, fire-resistive resin, (2) forming filaments of such coated roving, (3) winding said filaments on a form or mold to produce a shaped product, (4) curing to form of said admixture a tough, fire-resistive resin exhibiting low flame spread, good heat release and low smoke evolution when exposed to direct flame or to radiant heat and being resistant to embrittlement and cracking upon curing, and (5) removing said cured product from said form or mold.
Claim 12
Dependent Claim
19 words
Method as in claim 26 wherein said resorcinol component is a partially cured resin of resorcinol, phenol and formalin.
Claim 13
Dependent Claim
46 words
Method as in claim 6 wherein said fire-resistive resin is the reaction product of a partially cured resin of 26 parts by weight phenol, 16 parts by weight resorcinol and 15-35 parts by weight formalin, 3 parts by weight paraformaldehyde, and 12 parts by weight furfural.
Claim 14
Independent Claim
120 words
The method of making a fire-resistive duct which comprises coating glass roving with an admixture consisting essentially of: (a) a partially cured resin of phenol, resorcinol and formalin, (b) paraformaldehyde, and (c) at least one second substance chosen from the group consisting of furfural and furfuryl alcohol, (d) said paraformaldehyde and said second substance being added in sufficient amounts to produce a tough, fire-resistive resin, forming filaments of such coated roving, spiral winding said filaments to form said duct and allowing said coating to cure to form a tough, fire-resistive resin exhibiting low flame spread, good heat release and low smoke evolution when exposed to direct flame or to radiant heat and being resistant to embrittlement and cracking upon curing.
Claim 15
Independent Claim
120 words
The method of making a fire-resistive duct which comprises coating glass roving with an admixture consisting essentially of: (a) a partially cured resin of phenol, resorcinol and formalin, (b) paraformaldehyde, and (c) at least one second substance chosen from the group consisting of furfural and furfuryl alcohol, (d) said paraformaldehyde and said second substance being added in sufficient amounts to produce a tough, fire-resistive resin, forming filaments of such coated roving, spiral winding said filaments to form said duct and allowing said coating to cure to form a tough, fire-resistive resin exhibiting low flame spread, good heat release and low smoke evolution when exposed to direct flame or to radiant heat and being resistant to embrittlement and cracking upon curing.
Claim 16
Independent Claim
132 words
A method of making a fire-resistive shaped product which comprises: (1) incorporating a reinforcing agent in an admixture consisting essentially of: (a) a resorcinol component chosen from the group consisting of resorcinol, a mixture of resorcinol and phenol, and a partially cured resin or resorcinol, phenol and formalin, (b)paraformaldehyde and (c) at least one substance chosen from the group consisting of furfural and furfuryl alcohol, (d) said paraformaldehyde and said substance being added in amounts sufficient to provide said fire-resistive resin, (2) forming such incorporated agent and resin into a desired shape, and (3) curing to form of said admixture a fire-resistive resin exhibiting low flame spread, good heat release and low smoke evolution when exposed to direct flame or to radiant heat and being resistant to embrittlement and cracking upon curing.
Claim 17
Independent Claim
132 words
A method of making a fire-resistive shaped product which comprises: (1) incorporating a reinforcing agent in an admixture consisting essentially of: (a) a resorcinol component chosen from the group consisting of resorcinol, a mixture of resorcinol and phenol, and a partially cured resin or resorcinol, phenol and formalin, (b)paraformaldehyde and (c) at least one substance chosen from the group consisting of furfural and furfuryl alcohol, (d) said paraformaldehyde and said substance being added in amounts sufficient to provide said fire-resistive resin, (2) forming such incorporated agent and resin into a desired shape, and (3) curing to form of said admixture a fire-resistive resin exhibiting low flame spread, good heat release and low smoke evolution when exposed to direct flame or to radiant heat and being resistant to embrittlement and cracking upon curing.
References Cited (Backward Citations)
US4053447A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-27 | 1981-08-29 | 1982-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-27 | 1985-08-29 | 1986-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-27 | 1989-08-29 | 1990-02-28 | $7700.00 | Window Closed / Lapsed |