Synthetic resin composition-method and product
Assignee: Shea Technology
•
Filing: 1976-06-01
•
Granted: 1977-10-11
•
Expires: 1996-06-01
Abstract
Abstract A resinous product has high resistance to flame spread, good heat release and exhibits a low smoke-developed rating when exposed to flame or to indirect or radiant heat, and is flexible, tough and resistant to cracking and embrittlement upon curing. Such a product is the condensation product of resorcinol with or without included phenol, and an admixture of paraformaldehyde and furfural or furfuryl alcohol or both. The resorcinol starting material of this invention can also suitably be used in the form of a B-stage or partially cured resin or resorcinol-phenol-formaldehyde which is then condensed with the aforesaid aldehydes or such aldehyde substance and furfuryl alcohol. The product is useful in making castings or moldings which are resistant to embrittlement or cracking upon curing, and in making tough fiberglass parts, and it can contain fillers or the like. A method of making the product and articles is provided.
Inventors
- 👤 Lawrence E. Shea
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:42
CPC Classifications
C; C08; C08G; C08G16/00; C08G16/02; C08G16/025; C08G16/0256; C08G16/0262; C08G8/00; C08G8/04; C08G8/06; C08G8/08; C08G8/24; C08L; C08L61/00; C08L61/04; C08L61/06; C08L61/12; C08L61/34; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24149; Y10T442/00; Y10T442/60; Y10T442/693; Y10T442/696
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
106 words
A tough, fire-resistive resin exhibiting low flame spread, good heat release and low smoke evolution when exposed to direct flame or to radiant heat and being resistant to embrittlement and cracking upon curing, consisting essentially of the reaction product of: a. at least one resorcinol component chosen from the group consisting of resorcinol, a mixture of resorcinol and phenol, and a partially cured resin of phenol, resorcinol and formaldehyde, b. paraformaldehyde, and c. at least one second substance chosen from the group consisting of furfural and furfuryl alcohol, d. said paraformaldehyde and said second substance being added in sufficient amounts to produce said tough, fire-resistive resin.
Claim 2
Dependent Claim
106 words
A tough, fire-resistive resin exhibiting low flame spread, good heat release and low smoke evolution when exposed to direct flame or to radiant heat and being resistant to embrittlement and cracking upon curing, consisting essentially of the reaction product of: a. at least one resorcinol component chosen from the group consisting of resorcinol, a mixture of resorcinol and phenol, and a partially cured resin of phenol, resorcinol and formaldehyde, b. paraformaldehyde, and c. at least one second substance chosen from the group consisting of furfural and furfuryl alcohol, d. said paraformaldehyde and said second substance being added in sufficient amounts to produce said tough, fire-resistive resin.
Claim 3
Dependent Claim
32 words
A resin as in claim 1 containing from 8% to 40% based on the weight of the resorcinol component, of paraformaldehyde and said second substance, and containing at least 2% of paraformaldehyde.
Claim 4
Dependent Claim
11 words
Resin as in claim 2 containing from 2% to 15% paraformaldehyde.
Claim 5
Dependent Claim
14 words
Resin as in claim 2 containing from 5% to 30% of said second substance.
Claim 6
Dependent Claim
11 words
Resin as in claim 2 containing 3% paraformaldehyde and 12% furfural.
Claim 7
Dependent Claim
10 words
Resin as in claim 1 containing paraformaldehyde and furfuryl alcohol.
Claim 8
Dependent Claim
12 words
Resin as in claim 6 containing 8% paraformaldehyde and 10% furfuryl alcohol.
Claim 9
Dependent Claim
22 words
Resin as in claim 2 containing paraformaldehyde and furfural and wherein the amount of paraformaldehyde is not over 50% that of furfural.
Claim 10
Dependent Claim
19 words
Resin as in claim 1 wherein said resorcinol component is a partially cured resin of resorcinol, phenol, and formaldehyde.
Claim 11
Dependent Claim
36 words
Resin as in claim 1 containing a minor amount, about the same amount as of said second substance (c), of a substance chosen from the group consisting of methanol, ethanol, a polyhydric alcohol and a glycol.
Claim 12
Dependent Claim
112 words
A tough, fire-resistive resin exhibiting low flame spread, low heat release and low smoke evolution when exposed to direct flame or to radiant heat and being resistant to embrittlement and cracking upon curing, consisting essentially of the reaction product of: a. a partially cured resorcinol resin containing 8 to 35 parts by weight of resorcinol, 15 to 40 parts by weight of phenol, and 15 to 35 parts by weight of formalin, and b. paraformaldehyde and furfural in a total amount of 8 to 40%, based on the weight of the resorcinol resin and containing at least 2% paraformaldehyde, the amount of paraformaldehyde being not over 50% of the amount of furfural.
Claim 13
Dependent Claim
112 words
A tough, fire-resistive resin exhibiting low flame spread, low heat release and low smoke evolution when exposed to direct flame or to radiant heat and being resistant to embrittlement and cracking upon curing, consisting essentially of the reaction product of: a. a partially cured resorcinol resin containing 8 to 35 parts by weight of resorcinol, 15 to 40 parts by weight of phenol, and 15 to 35 parts by weight of formalin, and b. paraformaldehyde and furfural in a total amount of 8 to 40%, based on the weight of the resorcinol resin and containing at least 2% paraformaldehyde, the amount of paraformaldehyde being not over 50% of the amount of furfural.
Claim 14
Dependent Claim
11 words
Resin as in claim 11 containing 3% paraformaldehyde and 12% furfural.
Claim 15
Independent Claim
103 words
The method of making a fire-resistive resin exhibiting low flame spread, low heat release, and low smoke evolution under high temperature conditions and being resistant to cracking and embrittlement upon curing, which comprises preparing an admixture of a resorcinol component and furfuryl alcohol, then adding paraformaldehyde to said admixture and thoroughly blending, and allowing to cure, said furfuryl alcohol and said paraformaldehyde being present in an amount of from 10 to 40% and containing at least 2% paraformaldehyde, based on the weight of said resorcinol component, said paraformaldehyde being present in an amount of up to 50% of the amount of said alcohol.
Claim 16
Independent Claim
103 words
The method of making a fire-resistive resin exhibiting low flame spread, low heat release, and low smoke evolution under high temperature conditions and being resistant to cracking and embrittlement upon curing, which comprises preparing an admixture of a resorcinol component and furfuryl alcohol, then adding paraformaldehyde to said admixture and thoroughly blending, and allowing to cure, said furfuryl alcohol and said paraformaldehyde being present in an amount of from 10 to 40% and containing at least 2% paraformaldehyde, based on the weight of said resorcinol component, said paraformaldehyde being present in an amount of up to 50% of the amount of said alcohol.
Claim 17
Dependent Claim
45 words
Method as in claim 13 wherein there is also intimately mixed with said admixture a minor amount, about the same amount as of said furfuryl alcohol, of at least one substance chosen from the group consisting of methanol, ethanol, a polyhydric alcohol and a glycol.
Claim 18
Independent Claim
77 words
The method of making a fire-resistive resin exhibiting low flame spread, low heat release and low smoke evolution and being resistant to embrittlement and cracking upon curing, which comprises preparing an admixture of paraformaldehyde and furfural, comminuting to disperse said paraformaldehyde in said furfural, introducing a resorcinol component into said admixture and thoroughly blending, and allowing the mass so obtained to cure, said furfural and said paraformaldehyde being present in sufficient amounts to form such fire-resistive resin.
Claim 19
Independent Claim
77 words
The method of making a fire-resistive resin exhibiting low flame spread, low heat release and low smoke evolution and being resistant to embrittlement and cracking upon curing, which comprises preparing an admixture of paraformaldehyde and furfural, comminuting to disperse said paraformaldehyde in said furfural, introducing a resorcinol component into said admixture and thoroughly blending, and allowing the mass so obtained to cure, said furfural and said paraformaldehyde being present in sufficient amounts to form such fire-resistive resin.
Claim 20
Dependent Claim
42 words
Method as in claim 15 wherein there is also intimately mixed with said admixture a minor amount, about the same amount as of said furfural, of at least one substance chosen from the group consisting of methanol, ethanol, polyhydric alcohol, and glycol.
Claim 21
Dependent Claim
10 words
Method as in claim 16 wherein said substance is ethanol.
Claim 22
Dependent Claim
11 words
Method as in claim 16 wherein said substance is polyethylene glycol.
Claim 23
Dependent Claim
11 words
Method as in claim 16 wherein said substance is neopentyl glycol.
Claim 24
Dependent Claim
92 words
A fire-resistant molded body comprising a reaction product of a resorcinol component chosen from the group consisting of resorcinol, a mixture of resorcinal and phenol, and a partially cured resin of resorcinol, phenol, and formaldehyde, and paraformaldehyde plus at least one substance chosen from the group consisting of furfural and furfuryl alcohol, and including fiberglass, said paraformaldehyde and said substance being added in sufficient amounts to provide a tough, flexible resin of low flame spread and smoke evolution when compared with red oak wood and having satisfactory resistance to cracking and embrittlement.
Claim 25
Dependent Claim
92 words
A fire-resistant molded body comprising a reaction product of a resorcinol component chosen from the group consisting of resorcinol, a mixture of resorcinal and phenol, and a partially cured resin of resorcinol, phenol, and formaldehyde, and paraformaldehyde plus at least one substance chosen from the group consisting of furfural and furfuryl alcohol, and including fiberglass, said paraformaldehyde and said substance being added in sufficient amounts to provide a tough, flexible resin of low flame spread and smoke evolution when compared with red oak wood and having satisfactory resistance to cracking and embrittlement.
References Cited (Backward Citations)
US1802390A
Cited
US3312650A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-10 | 1981-04-11 | 1981-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-10 | 1985-04-11 | 1985-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-10 | 1989-04-11 | 1989-10-11 | $7700.00 | Window Closed / Lapsed |