Process for making instant shaped foams
Assignee: Monsanto Research Corp
•
Filing: 1976-04-30
•
Granted: 1978-02-21
•
Expires: 1996-04-30
Abstract
Abstract In a process for rapidly producing a substantially uniform, elongated, cellular thermoplastic article comprising rapidly discharging from a vessel a pressurized gel of a solid thermoplastic amorphous polymer and a gaseous solvent in an amount in the range of from about 25-100% by weight of said polymer, said solvent being capable of forming a flowable gel with the polymer when subjected to superatomospheric pressure, the improvement for shaping the article comprising restraining sufficiently the speed of flow of the gel from the vessel through a die to form the desired shaped article with the gel at ambient temperature in said vessel.
Inventors
- 👤 Charles E. McClung
- 👤 James L. Schwendeman
- 👤 Ival O. Salyer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 13:42
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/34; B29C44/36; B29C44/46; B29C44/50; B29C44/507; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10S264/06; Y10S264/13
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
129 words
In a process for rapidly producing a substantially uniform, elongated, cellular, thermoplastic article comprising rapidly discharging from a vessel a pressurized gel of a solid thermoplastic amorphous polymer and a gaseous solvent in the range of about 25-100% by weight of said polymer, said polymer having a solubility parameter between 8.4 and 10.4 and an intrinsic viscosity value between 0.5 and 5.0, and said solvent being capable of forming a flowable gel with the polymer when subjected to super-atmospheric pressure, the improvement for shaping the article comprising restraining sufficiently the speed of flow of the gel from the vessel through the die to allow the die to shape the article, said gel being present in said vessel at a temperature in the range of about -10° to 50° C.
Claim 2
Dependent Claim
129 words
In a process for rapidly producing a substantially uniform, elongated, cellular, thermoplastic article comprising rapidly discharging from a vessel a pressurized gel of a solid thermoplastic amorphous polymer and a gaseous solvent in the range of about 25-100% by weight of said polymer, said polymer having a solubility parameter between 8.4 and 10.4 and an intrinsic viscosity value between 0.5 and 5.0, and said solvent being capable of forming a flowable gel with the polymer when subjected to super-atmospheric pressure, the improvement for shaping the article comprising restraining sufficiently the speed of flow of the gel from the vessel through the die to allow the die to shape the article, said gel being present in said vessel at a temperature in the range of about -10° to 50° C.
Claim 3
Dependent Claim
25 words
A process of claim 1 wherein said gel contains a water-soluble surfactant in sufficient amount to promote the flow of the gel from the vessel.
Claim 4
Dependent Claim
27 words
A process of claim 1 wherein for homogeneous polymer solutions a nucleating agent is contained in said gel in sufficient amount to promote uniformity of cell size.
Claim 5
Dependent Claim
22 words
A process of claim 1 wherein a screen is placed before the die to restrain the speed of flow of the gel.
Claim 6
Dependent Claim
26 words
A process of claim 4 wherein a center portion of said screen is blocked to give a shaped article with an opening through the center thereof.
Claim 7
Dependent Claim
33 words
A process of claim 4 wherein a center portion of the screen is blocked by a tapered end of a mandrel to give a shaped article with an opening through the center thereof.
Claim 8
Dependent Claim
11 words
A process of claim 1 wherein said thermoplastic polymer is polystyrene.
Claim 9
Dependent Claim
37 words
A process of claim 1 wherein to promote processability of said article another solvent boiling above about 20° C is present in said gel in an amount of about 3 to 30% by weight of said polymer.
Claim 10
Dependent Claim
11 words
A process of claim 8 wherein said other solvent is tetrachloroethylene.
Claim 11
Dependent Claim
14 words
A process of claim 1 wherein said gaseous solvent boils below about 0° C.
Claim 12
Dependent Claim
60 words
A process of claim 1 wherein said gel contains a water-soluble surfactant in sufficient amount to promote the flow of the gel from said vessel, said gaseous solvent boils below about 0° C. and to promote processability of said article another solvent boiling above about 20° C. in an amount of about 3 to 30% by weight of said polymer.
Claim 13
Dependent Claim
11 words
A process of claim 11 wherein said other solvent is tetrachloroethylene.
Claim 14
Dependent Claim
21 words
A process of claim 12 wherein a screen is placed before the die to restrain the speed of flow of gel.
Claim 15
Dependent Claim
11 words
A process of claim 13 wherein said thermoplastic polymer is polystyrene.
References Cited (Backward Citations)
US2450436A
Cited
US2576977A
Cited
US3102865A
Cited
US3227784A
Cited
US3461193A
Cited
US3523916A
Cited
US3785919A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-20 | 1981-08-22 | 1982-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-20 | 1985-08-22 | 1986-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-20 | 1989-08-22 | 1990-02-21 | $7700.00 | Window Closed / Lapsed |