Antimony oxide pigment and process of manufacture
Assignee: Kerr McGee Chemical Corp
•
Filing: 1977-04-18
•
Granted: 1978-02-21
•
Expires: 1997-04-18
Abstract
Abstract The present invention provides a process for the surface treatment of antimony oxide for use as a pigment in paints or plastics wherein a hydrous oxide or mixture of oxides is precipitated onto the antimony oxide pigment. Specifically, this invention concerns the precipitation of hydrous oxides of titania, alumina or silica. In operation, the pH of an aqueous slurry of antimony oxide is adjusted to be within a specified pH range and the coating of the antimony oxide is effected by adding an amount of the hydrous oxide to cause precipitation of the hydrous oxide upon the antimony oxide pigment. The present invention contemplates an improved antimony oxide pigment having a first coating of amorphous alumina and a second coating of boehmite alumina. The present invention also contemplates an improved antimony oxide pigment having a first coating of titania and a second coating of alumina.
Inventors
- 👤 David Charles Thomas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:12
CPC Classifications
C; C09; C09C; C09C1/00; C09C1/0096; C09C3/00; C09C3/06; C09C3/063; C01; C01P; C01P2004/00; C01P2004/80; C01P2004/82; C01P2004/84; C01P2006/00; C01P2006/60
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
63 words
A coated antimony oxide pigment comprising: an antimony oxide pigment; a first coating comprising at least one member selected from the group of titania, predominately amorphous alumina or silica, on the antimony oxide pigment; and a second coating comprising at least one member selected from the group of alumina, predominately boehmite alumina, or silica on the antimony oxide pigment over the first coating.
Claim 2
Dependent Claim
63 words
A coated antimony oxide pigment comprising: an antimony oxide pigment; a first coating comprising at least one member selected from the group of titania, predominately amorphous alumina or silica, on the antimony oxide pigment; and a second coating comprising at least one member selected from the group of alumina, predominately boehmite alumina, or silica on the antimony oxide pigment over the first coating.
Claim 3
Dependent Claim
39 words
A coated antimony oxide pigment comprising: an antimony oxide pigment; a first coating of predominately amorphous alumina on the antimony oxide pigment; and a second coating of predominately boehmite alumina on the antimony oxide pigment over the first coating.
Claim 4
Dependent Claim
39 words
A coated antimony oxide pigment comprising: an antimony oxide pigment; a first coating of predominately amorphous alumina on the antimony oxide pigment; and a second coating of predominately boehmite alumina on the antimony oxide pigment over the first coating.
Claim 5
Dependent Claim
132 words
A process comprising: providing an aqueous slurry of antimony oxide pigment; adjusting the pH of the slurry to a level within a range of from about 1.0 to about 3.5; adding a first amount of an alumina coating agent to the slurry to form a first coating of amphorous alumina on the pigment and to increase the pH of the slurry to a level within a range of from about 8.0 to about 9.0; adding a second amount of the alumina coating agent to the slurry to form a second coating of boehmite alumina on the pigment and over the first coating; and maintaining the pH of the slurry at a level within a range of from about 8.0 to about 9.0 while adding the second amount of the alumina coating agent.
Claim 6
Dependent Claim
132 words
A process comprising: providing an aqueous slurry of antimony oxide pigment; adjusting the pH of the slurry to a level within a range of from about 1.0 to about 3.5; adding a first amount of an alumina coating agent to the slurry to form a first coating of amphorous alumina on the pigment and to increase the pH of the slurry to a level within a range of from about 8.0 to about 9.0; adding a second amount of the alumina coating agent to the slurry to form a second coating of boehmite alumina on the pigment and over the first coating; and maintaining the pH of the slurry at a level within a range of from about 8.0 to about 9.0 while adding the second amount of the alumina coating agent.
Claim 7
Dependent Claim
38 words
The process of claim 3, after adding the second amount of alumina coating agent, defined further to include the step of: digesting the slurry at a temperature within a range of from about 40° to about 100° C.
Claim 8
Dependent Claim
45 words
The process of claim 4, after digesting the slurry defined further to include the steps of: filtering the slurry to recover the coated antimony oxide pigment; washing the coated antimony oxide pigment; drying the coated antimony oxide pigment; and milling the coated antimony oxide pigment.
Claim 9
Dependent Claim
77 words
The process of claim 3 wherein the first amount of alumina coating agent is sufficient to provide the first coating within a range of from about 0.25 percent to about 1.5 percent by weight based on the weight of the pigment, and the second amount of alumina coating agent is sufficient to provide the second coating within a range of from about 0.25 percent to about 1.5 percent by weight based on the weight of the pigment.
Claim 10
Dependent Claim
49 words
The process of claim 3 wherein adjusting the pH of the slurry to a level within a range of from about 1.0 to about 3.5 is further defined as: adjusting the pH of the slurry to a level within a preferred range of from about 2.5 to about 3.0.
Claim 11
Dependent Claim
113 words
A process comprising: providing an aqueous slurry of antimony oxide pigment; adding acid to the slurry to adjust the pH of the slurry to a level within the range of from about 1.0 to about 3.5; adding a first amount of sodium aluminate solution to the slurry until the pH of the slurry is at a level within a range of from about 8.0 to about 9.0; adding a second amount of sodium aluminate solution to the slurry; and adding acid to the slurry while adding the second amount of sodium aluminate solution to maintain the pH of the slurry at a level within a range of from about 8.0 to about 9.0.
Claim 12
Dependent Claim
113 words
A process comprising: providing an aqueous slurry of antimony oxide pigment; adding acid to the slurry to adjust the pH of the slurry to a level within the range of from about 1.0 to about 3.5; adding a first amount of sodium aluminate solution to the slurry until the pH of the slurry is at a level within a range of from about 8.0 to about 9.0; adding a second amount of sodium aluminate solution to the slurry; and adding acid to the slurry while adding the second amount of sodium aluminate solution to maintain the pH of the slurry at a level within a range of from about 8.0 to about 9.0.
Claim 13
Dependent Claim
12 words
The process of claim 8 wherein the acid is concentrated sulfuric acid.
Claim 14
Dependent Claim
49 words
The process of claim 8 wherein the first amount of sodium aluminate is sufficient to effect a precipitation of alumina on the antimony oxide pigment at a level within a range of from about 0.25 percent to about 1.5 percent by weight based on the weight of the pigment.
Claim 15
Dependent Claim
49 words
The process of claim 10 wherein the second amount of sodium aluminate is sufficient to effect a precipitation of alumina on the antimony oxide pigment at a level within a range of from about 0.25 percent to about 1.5 percent by weight based on the weight of the pigment.
Claim 16
Dependent Claim
41 words
The process of claim 8, after adding the second amount of sodium aluminate solution to the slurry defined further to include the step of: digesting the slurry at a temperature within a range of from about 40° to about 100° C.
Claim 17
Dependent Claim
45 words
The process of claim 12, after digesting the slurry defined further to include the steps of: filtering the slurry to recover the coated antimony oxide pigment; washing the coated antimony oxide pigment; drying the coated antimony oxide pigment; and milling the coated antimony oxide pigment.
Claim 18
Dependent Claim
36 words
A coated antimony oxide pigment comprising: an antimony oxide pigment; a first coating of titania on the antimony oxide pigment; and a second coating of alumina on the antimony oxide pigment and over the first coating.
Claim 19
Dependent Claim
36 words
A coated antimony oxide pigment comprising: an antimony oxide pigment; a first coating of titania on the antimony oxide pigment; and a second coating of alumina on the antimony oxide pigment and over the first coating.
Claim 20
Dependent Claim
121 words
A process comprising: providing an aqueous slurry of antimony oxide pigment; adjusting the pH of the slurry to a level within a range of from about 9.0 to about 10.0; adding an amount of a titania coating agent to the slurry to form a first coating of titania on the pigment; adjusting the pH of the slurry to a level within a range of from about 7.0 to about 9.0; adding an amount of an alumina coating agent to the slurry to form a second coating of alumina on the pigment and over the first coating; maintaining the pH of the slurry at a level within a range of from about 7.0 to about 12.0 while adding the alumina coating agent.
Claim 21
Dependent Claim
121 words
A process comprising: providing an aqueous slurry of antimony oxide pigment; adjusting the pH of the slurry to a level within a range of from about 9.0 to about 10.0; adding an amount of a titania coating agent to the slurry to form a first coating of titania on the pigment; adjusting the pH of the slurry to a level within a range of from about 7.0 to about 9.0; adding an amount of an alumina coating agent to the slurry to form a second coating of alumina on the pigment and over the first coating; maintaining the pH of the slurry at a level within a range of from about 7.0 to about 12.0 while adding the alumina coating agent.
Claim 22
Dependent Claim
35 words
The process of claim 15, after adding the alumina coating agent, defined further to include the step of: digesting the slurry at a temperature within a range of from about 40° to about 100° C.
Claim 23
Dependent Claim
45 words
The process of claim 16, after digesting the slurry, defined further to include the steps of: filtering the slurry to recover the coated antimony oxide pigment; washing the coated antimony oxide pigment; drying the coated antimony oxide pigment; and milling the coated antimony oxide pigment.
Claim 24
Dependent Claim
79 words
The process of claim 15 wherein the titania coating agent is added in an amount sufficient to provide a first coating within a range of from about 0.5 percent to about 1.5 percent by weight based on the weight of the pigment and the alumina coating agent is added in an amount sufficient to provide a second coating within a range of from about 0.5 percent to about 3.0 percent by weight based on the weight of the pigment.
Claim 25
Dependent Claim
52 words
The process of claim 18 wherein the titania coating agent is added, defined further as: the titania coating agent is added in an amount sufficient to provide a first coating within a preferred range of from about 0.5 percent to about 1.0 percent by weight based on the weight of the pigment.
Claim 26
Dependent Claim
52 words
The process of claim 19 wherein the alumina coating agent is added, defined further as: the alumina coating agent is added in an amount sufficient to provide a second coating within a preferred range of from about 1.0 percent to about 1.8 percent by weight based on the weight of the pigment.
Claim 27
Dependent Claim
122 words
A process comprising: providing an aqueous slurry of antimony oxide; adding base to the slurry to adjust the pH of the slurry to a level within a range of from about 9.0 to about 10.0; adding an amount of titania solution to the slurry until the pH of the slurry is at a level less than about 3.0; adding base to the slurry to adjust the pH of the slurry to a level within a range of from about 7.0 to about 9.0; adding an amount of sodium aluminate solution to the slurry; and maintaining the pH of the slurry at a level within a range of from about 7.0 to about 12.0 while adding the sodium aluminate solution to the slurry.
Claim 28
Dependent Claim
122 words
A process comprising: providing an aqueous slurry of antimony oxide; adding base to the slurry to adjust the pH of the slurry to a level within a range of from about 9.0 to about 10.0; adding an amount of titania solution to the slurry until the pH of the slurry is at a level less than about 3.0; adding base to the slurry to adjust the pH of the slurry to a level within a range of from about 7.0 to about 9.0; adding an amount of sodium aluminate solution to the slurry; and maintaining the pH of the slurry at a level within a range of from about 7.0 to about 12.0 while adding the sodium aluminate solution to the slurry.
Claim 29
Dependent Claim
11 words
The process of claim 21 wherein the base is sodium hydroxide.
Claim 30
Dependent Claim
38 words
The process of claim 21, after adding the sodium aluminate solution to the slurry, defined further to include the step of: digesting the slurry at a temperature within a range of from about 40° to about 100° C.
Claim 31
Dependent Claim
45 words
The process of claim 23, after digesting the slurry, defined further to include the steps of: filtering the slurry to recover the coated antimony oxide pigment; washing the coated antimony oxide pigment; drying the coated antimony oxide pigment; and milling the coated antimony oxide pigment.
Claim 32
Dependent Claim
57 words
The process of claim 21 wherein the titania solution is added, defined further as: the titania solution is added in an amount sufficient to effect a precipitation of titania on the antimony oxide pigment at a level within a range of from about 0.5 percent to 1.5 percent by weight based on the weight of the pigment.
Claim 33
Dependent Claim
58 words
The process of claim 25 wherein the sodium aluminate is added, defined further as: the sodium aluminate solution is added in an amount sufficient to effect a precipitation of alumina on the titania coated antimony oxide pigment within a range of from about 0.5 percent to about 3.0 percent by weight based on the weight of the pigment.
Claim 34
Dependent Claim
60 words
The process of claim 26 wherein the titania solution is added is further defined as: the titania solution is added in an amount sufficient to effect a precipitation of titania on the antimony oxide pigment at a level within a preferred range of from about 0.5 percent to about 1.0 percent by weight based on the weight of the pigment.
Claim 35
Dependent Claim
60 words
The process of claim 27 wherein the sodium aluminate solution is added is further defined as: the sodium aluminate solution is added in an amount sufficient to effect a precipitation of alumina on the titania coated antimony oxide within a preferred range of from about 1.0 percent to about 1.8 percent by weight based on the weight of the pigment.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-20 | 1981-08-22 | 1982-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-20 | 1985-08-22 | 1986-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-20 | 1989-08-22 | 1990-02-21 | $7700.00 | Window Closed / Lapsed |