Abstract
Abstract The present invention provides an improved process for coating titanium dioxide with precipitated alumina (aluminum oxide) for use as a pigment in plastics wherein a first coating of amorphous alumina is precipitated onto the titanium dioxide and then a second coating of crystalline alumina is precipitated over the first coating. In operation, the pH of an aqueous slurry of titanium dioxide pigment is adjusted to be within a first pH range as the first alumina coating is effected by adding an amount of sodium aluminate to the aqueous slurry and then the pH of the slurry is adjusted to be within a second pH range while a second amount of sodium aluminate is added to form the second coating over the first coating. The present invention also contemplates an improved titanium dioxide pigment having a first coating of amorphous alumina and a second coating of boehmite alumina.
Inventors
- 👤 Edward Conley Murray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 21:16
CPC Classifications
C; C09; C09C; C09C1/00; C09C1/36; C09C1/3607; C09C1/3653; C09C1/3661; C01; C01P; C01P2004/00; C01P2004/80; C01P2004/82; C01P2004/84
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
40 words
A coated titanium dioxide pigment, comprising: a titanium dioxide pigment; a first coating of predominantly amorphous alumina on the titanium dioxide pigment; and a second coating of predominantly boehmite alumina on the titanium dioxide pigment and over the first coating.
Claim 2
Dependent Claim
40 words
A coated titanium dioxide pigment, comprising: a titanium dioxide pigment; a first coating of predominantly amorphous alumina on the titanium dioxide pigment; and a second coating of predominantly boehmite alumina on the titanium dioxide pigment and over the first coating.
Claim 3
Dependent Claim
125 words
A process, comprising: providing an aqueous slurry of titanium dioxide pigment; adjusting the pH of the slurry to a level below about 2.0; adding a first amount of an alumina coating agent to the slurry to form a first coating of amorphous alumina on the pigment and to increase the pH of the slurry to a level within a range of from about 8.0 to about 9.0; adding a second amount of the alumina coating agent to the slurry to form a second coating of boehmite alumina on the pigment and over the first coating; and maintaining the pH of the slurry at a level within a range of from about 8.0 to about 9.0 while adding the second amount of the alumina coating agent.
Claim 4
Dependent Claim
125 words
A process, comprising: providing an aqueous slurry of titanium dioxide pigment; adjusting the pH of the slurry to a level below about 2.0; adding a first amount of an alumina coating agent to the slurry to form a first coating of amorphous alumina on the pigment and to increase the pH of the slurry to a level within a range of from about 8.0 to about 9.0; adding a second amount of the alumina coating agent to the slurry to form a second coating of boehmite alumina on the pigment and over the first coating; and maintaining the pH of the slurry at a level within a range of from about 8.0 to about 9.0 while adding the second amount of the alumina coating agent.
Claim 5
Dependent Claim
39 words
The process of claim 2, after adding the second amount of alumina coating agent, defined further to include the step of: digesting the slurry at a temperature within a range of from about 120° F to about 140° F.
Claim 6
Dependent Claim
39 words
The process of claim 3, after digesting the slurry, defined further to include the steps of: filtering the slurry to recover the coated titanium dioxide pigment; drying the coated titanium dioxide pigment; and milling the coated titanium dioxide pigment.
Claim 7
Dependent Claim
76 words
The process of claim 2 wherein the first amount of alumina coating of alumina coating agent is sufficient to provide the first coating within a range of from about 0.3% to about 0.7% by weight based on the weight of the pigment, and the second amount of alumina coating agent is sufficient to provide the second coating within a range of from about 0.3% to about 0.7% by weight based on the weight of the pigment.
Claim 8
Dependent Claim
108 words
A process, comprising: providing an aqueous slurry of titanium dioxide pigment; adding acid to the slurry to adjust the pH of the slurry to a level of less than about 2.0; adding a first amount of sodium aluminate solution to the slurry until the pH of the slurry is at a level within a range of from about 8.0 to about 9.0; adding a second amount of sodium aluminate solution to the slurry; and adding acid to the slurry while adding the second amount of sodium aluminate solution to maintain the pH of the slurry at a level within a range of from about 8.0 to about 9.0.
Claim 9
Dependent Claim
108 words
A process, comprising: providing an aqueous slurry of titanium dioxide pigment; adding acid to the slurry to adjust the pH of the slurry to a level of less than about 2.0; adding a first amount of sodium aluminate solution to the slurry until the pH of the slurry is at a level within a range of from about 8.0 to about 9.0; adding a second amount of sodium aluminate solution to the slurry; and adding acid to the slurry while adding the second amount of sodium aluminate solution to maintain the pH of the slurry at a level within a range of from about 8.0 to about 9.0.
Claim 10
Dependent Claim
12 words
The process of claim 6 wherein the acid is concentrated sulfuric acid.
Claim 11
Dependent Claim
46 words
The process of claim 6 wherein the first amount of sodium aluminate is sufficient to effect a precipitation of alumina on the titanium dioxide pigment at a level within a range of from about 0.3% to about 0.7% weight based on the weight of the pigment.
Claim 12
Dependent Claim
46 words
The process of claim 8 wherein the second amount of sodium aluminate is adequate to effect a precipitation of alumina on the titanium dioxide pigment at a level within a range of from about 0.3% to about 0.7% weight based on the weight of the pigment.
Claim 13
Dependent Claim
42 words
The process of claim 6, after adding the second amount of sodium aluminate solution to the slurry, defined further to include the step of: digesting the slurry at a temperature within a range of from about 120° F to about 140° F.
Claim 14
Dependent Claim
44 words
The process of claim 10, after digesting the slurry, defined further to include the steps of: filtering the slurry to recover the coated titanium dioxide; drying the coated titanium dioxide; and milling the coated titanium dioxide as required to provide a plastics grade pigment.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-09 | 1980-11-08 | 1981-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-09 | 1984-11-08 | 1985-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-09 | 1988-11-08 | 1989-05-10 | $7700.00 | Window Closed / Lapsed |