Metallic filler material
Assignee: RTX Corp
•
Filing: 1976-11-24
•
Granted: 1978-02-14
•
Expires: 1996-11-24
Abstract
Abstract In filling voids in or between metallic articles, as in the repair of cracks or other surface defects in castings, the void is filled with a powder mix which upon heat treatment fills the void. The filler powder mix is a blend of at least two distinct powder components and in terms of overall composition preferably corresponds to that of article being repaired. The components comprising the mix are selected to provide a transient liquid phase and isothermal resolidification of a portion of the mix at the temperature below the article melting point. A subsequent heat treatment is preferably utilized for homogenization.
Inventors
- 👤 David S. Duvall
- 👤 William A. Owczarski
- 👤 Daniel F. Paulonis
- 👤 Robert P. Schaefer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:56
CPC Classifications
B; B23; B23P; B23P6/00; B23P6/002; B23P6/007; B22; B22F; B22F1/00; B22F1/09; B23K; B23K35/00; B23K35/02; B23K35/0222; B23K35/0244; B23K35/22; B23K35/24; B23K35/30; B23K35/3033
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
138 words
A metallic filler material mix for filling cavities in and between metal articles which comprise: a first, finely-divided homogeneous particulate component substantially corresponding in composition to that of the metal articles; a second, finely-divided homogeneous particulate component having as its basis the same basis metal as that of the articles and containing a melting point depressent such as boron in a quantity substantially exceeding that present in the metal articles; the first and second particulate components being intimately blended to form a powder mix which has an overall composition approximating that of the metal articles, a portion of the mix exhibiting a capability of forming a liquid phase while another portion of the mix remains unliquefied at a processing temperature below the melting point of the articles, the mix being characterized by isothermal resolidification at the processing temperature.
Claim 2
Dependent Claim
138 words
A metallic filler material mix for filling cavities in and between metal articles which comprise: a first, finely-divided homogeneous particulate component substantially corresponding in composition to that of the metal articles; a second, finely-divided homogeneous particulate component having as its basis the same basis metal as that of the articles and containing a melting point depressent such as boron in a quantity substantially exceeding that present in the metal articles; the first and second particulate components being intimately blended to form a powder mix which has an overall composition approximating that of the metal articles, a portion of the mix exhibiting a capability of forming a liquid phase while another portion of the mix remains unliquefied at a processing temperature below the melting point of the articles, the mix being characterized by isothermal resolidification at the processing temperature.
Claim 3
Dependent Claim
31 words
The filler material mix according to claim 1 wherein: the ratio, by weight, of the quantity of the first particulate component to the second particulate component in the mix exceeds unity.
Claim 4
Dependent Claim
23 words
The filler material mix according to claim 3 wherein: the ratio of the first component to the second component is 3/1 - 8/1.
Claim 5
Dependent Claim
42 words
The filler material mix according to claim 2 wherein: the ratio of the first component to a second component is sufficiently high to provide sufficient viscosity of the mix at the processing temperature that unmelted particulate matter remains distributed through the mix.
Claim 6
Dependent Claim
20 words
The filler material mix according to claim 2 wherein: the second particulate component contains, by weight, about 1-3 percent boron.
Claim 7
Dependent Claim
25 words
The filler material mix according to claim 3 wherein: the average particle size of the first particulate component exceeds that of the second particulate component.
Claim 8
Dependent Claim
21 words
The filler material mix according to claim 3 wherein: the particulate component have as their basis ingredient nickel, cobalt or iron.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-13 | 1981-08-15 | 1982-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-13 | 1985-08-15 | 1986-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-13 | 1989-08-15 | 1990-02-14 | $7700.00 | Window Closed / Lapsed |