Polyurethane-urea elastomers based on propylene oxide-tetrahydrofuran copolymers
Assignee: Bridgestone Firestone Inc
•
Filing: 1976-04-07
•
Granted: 1978-01-31
•
Expires: 1996-04-07
Abstract
Abstract A polyurethane-urea elastomer is prepared by reacting a copolymer of propylene oxide and tetrahydrofuran having hydroxyl end groups with an organic polyisocyanate and the isocyanate-terminated polymer is then reacted with an aromatic diamine in either bulk or solution process.
Inventors
- 👤 Tristram Walker Bethea
- 👤 Shingo Futamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 07:50
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/4854; C08G18/08; C08G18/10
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
205 words
A polyurethane-urea elastomer, comprising, the reaction product of propylene oxide-tetrahydrofuran copolymers, polyisocyanates and aromatic diamine chain extenders, said copolymers having a molecular weight of from about 300 to about 10,000 and containing from about 5 percent to about 75 percent of propylene oxide based upon the total weight of said copolymer, said copolymers containing hydroxyl end groups, said polyisocyanates reacted with said hydroxyl terminated copolymers to form prepolymers having isocyanate end groups, the equivalent ratio of said isocyanate groups of said polyisocyanates to said hydroxyl end groups ranging from about 1.25 to about 3.0, said aromatic diamines having from 6 to about 20 carbon atoms and selected from the class consisting of shielded aromatic diamines and non-shielded aromatic diamines, said prepolymer containing said isocyanate end groups chain extended through either bulk polymerization by reaction with said shielded aromatic diamines or through a solution polymerization by reaction with said non-shielded diamines to produce said polyurethane-urea elastomers, the equivalent ratio of amine groups of said aromatic diamines to said isocyanate end groups ranging from about 0.8 to about 1.2, said copolymer containing hydroxyl end groups having a low viscosity, said polyurethane-urea elastomers having good tensile strength at ambient temperatures and at 100° C, and good flex properties.
Claim 2
Dependent Claim
205 words
A polyurethane-urea elastomer, comprising, the reaction product of propylene oxide-tetrahydrofuran copolymers, polyisocyanates and aromatic diamine chain extenders, said copolymers having a molecular weight of from about 300 to about 10,000 and containing from about 5 percent to about 75 percent of propylene oxide based upon the total weight of said copolymer, said copolymers containing hydroxyl end groups, said polyisocyanates reacted with said hydroxyl terminated copolymers to form prepolymers having isocyanate end groups, the equivalent ratio of said isocyanate groups of said polyisocyanates to said hydroxyl end groups ranging from about 1.25 to about 3.0, said aromatic diamines having from 6 to about 20 carbon atoms and selected from the class consisting of shielded aromatic diamines and non-shielded aromatic diamines, said prepolymer containing said isocyanate end groups chain extended through either bulk polymerization by reaction with said shielded aromatic diamines or through a solution polymerization by reaction with said non-shielded diamines to produce said polyurethane-urea elastomers, the equivalent ratio of amine groups of said aromatic diamines to said isocyanate end groups ranging from about 0.8 to about 1.2, said copolymer containing hydroxyl end groups having a low viscosity, said polyurethane-urea elastomers having good tensile strength at ambient temperatures and at 100° C, and good flex properties.
Claim 3
Dependent Claim
64 words
A polyurethane-urea elastomer according to claim 1, wherein said polyisocyanates have the formula: R(N=C=X).sub.n where R is an aliphatic chain containing from 1 to about 20 carbon atoms, a cycloaliphatic ring containing from 4 to about 20 carbon atoms, an aromatic nucleus containing from 6 to about 20 carbon atoms, and combinations thereof, X is oxygen or sulfur, and n is 2 or 3.
Claim 4
Dependent Claim
35 words
A polyurethane-urea elastomer according to claim 2, wherein said non-shielded aromatic diamines are selected from the group consisting of p-phenylene diamine, m-phenylene diamine, 4,4'-methylenebis(2-methoxyaniline), 4,4'-methylenebis(N-methylaniline), 2,4-toluene diamine, 2,6-toluene diamine, benzidine, 3,3'-dimethylbenzidine, 3,3'-dimethoxybenzidine, and 4,4'-methylene dianiline.
Claim 5
Dependent Claim
25 words
A polyurethane-urea elastomer according to claim 3, wherein said aromatic diamines are selected from the class consisting of p-phenylene diamine, 2,6-toluene diamine, and 4,4'-methylene dianiline.
Claim 6
Dependent Claim
52 words
A polyurethane-urea elastomer according to claim 2, wherein said equivalent ratio of isocyanate groups of said polyisocyanates to said hydroxyl end groups ranges from about 1.5 to about 2.5 and said equivalent ratio of amine groups of said aromatic diamines to said isocyanate end groups ranges from about 0.9 to about 1.1.
Claim 7
Dependent Claim
54 words
A polyurethane-urea elastomer according to claim 5, wherein a compound selected from the class consisting of a polyol and water is added in the preparation of said copolymer so that the copolymers contain hydroxyl end groups, the amount of said polyol ranging from about 0.005 to about 3.0 moles per 1,000 grams of monomers.
Claim 8
Dependent Claim
138 words
A polyurethane-urea elastomer according to claim 6, wherein said shielded diamines are selected from the group consisting of dichlorobenzidine, methylene bis(2-chloroaniline), a complex of 4,4'-methylene dianiline and a salt, the ratio of said dianiline to said salt being from about 3 moles to 1 mole, and a complex of racemic 2,3-di(4-aminophenyl) butane and a salt, the ratio of said butane to said salt being about 3 moles to 1 mole, said salt of said dianiline complex selected from the class consisting of sodium chloride, sodium bromide, sodium iodide, sodium nitrite, lithium chloride, lithium bromide, lithium iodide, lithium nitrate and sodium cyanide, said salt of said butane compounds selected from the class consisting of sodium chloride, sodium bromide, sodium iodide, potassium chloride, potassium bromide, potassium iodide, rubidium chloride, rubidium bromide, rubidium iodide, cesium chloride, cesium bromide and cesium iodide.
Claim 9
Dependent Claim
51 words
A polyurethane-urea elastomer according to claim 7, wherein said equivalent ratio of isocyanate groups of said polyisocyanates to said hydroxyl end groups ranges from about 1.5 to about 2.5 and the equivalent ratio of amine groups of said aromatic diamine to said isocyanate groups ranges from about 0.9 to about 1.1.
Claim 10
Dependent Claim
102 words
A polyurethane-urea elastomer according to claim 8, wherein said copolymer is made by the copolymerization of tetrahydrofuran and propylene oxide monomers, a compound selected from the group consisting of water and a polyol being added to said copolymerization so that said copolymer contains hydroxyl end groups, the amount of said polyol and water ranging from about 0.05 to about 1.5 moles per 1,000 grams of monomers, said polyol selected from the groups consisting of diols having from 2 to about 20 carbon atoms, triols having from 3 to about 26 carbon atoms and tetraols having from 4 to about 20 carbon atoms.
Claim 11
Dependent Claim
21 words
A polyurethane-urea elastomer according to claim 8, wherein said copolymers contain from about 15 to about 50 percent of propylene oxide.
Claim 12
Dependent Claim
21 words
A polyurethane-urea polymer according to claim 10, wherein said preferred shielded diamines are said complex of 4,4'-methylene dianiline and a salt.
Claim 13
Dependent Claim
13 words
A polyurethane-urea polymer according to claim 11, wherein said salt is sodium chloride.
Claim 14
Dependent Claim
44 words
A polyurethane-urea polymer according to claim 12, wherein said equivalent ratio of isocyanate groups of said polyisocyanate to said hydroxyl end groups ranges from about 1.75 to about 2.25 and said copolymers contains from about 25 percent to about 40 percent of propylene oxide.
Claim 15
Dependent Claim
34 words
A polyurethane-urea polymer according to claim 13, wherein said diisocyanates are selected from the class consisting of 4,4'-diphenylmethane diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 1,5-naphthalene diisocyanate, 1,4-benzene diisocyanate, 3,3'-dimethoxy-4,4'-biphenyl diisocyanate, m-phenylene diisocyanate, and xylylene diisocyanate.
Claim 16
Dependent Claim
19 words
A polyurethane-urea polymer according to claim 7, wherein said polymer is cast in the form of a tire carcass.
Claim 17
Dependent Claim
21 words
A polyurethane-urea polymer according to claim 14, wherein the molecular weight of said copolymers range from about 750 to about 2,000.
Claim 18
Dependent Claim
34 words
A polyurethane-urea elastomer according to claim 11 including a plasticizer, said plasticizer ranging up to 50 parts per 100 parts of a prepolymer made from said polyisocyanates and said copolymers containing hydroxyl end groups.
Claim 19
Dependent Claim
13 words
A polyurethane-urea elastomer according to claim 17, wherein said plasticizer is dioctyl phthalate.
References Cited (Backward Citations)
US3404131A
Cited
US3425999A
Cited
US3489723A
Cited
US3681290A
Cited
USRE28424E
Cited
US3755261A
Cited
US3891606A
Cited
US3888831A
Cited
US3899438A
Cited
US3900447A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-30 | 1981-08-01 | 1982-01-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-30 | 1985-08-01 | 1986-01-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-30 | 1989-08-01 | 1990-01-31 | $7700.00 | Window Closed / Lapsed |