Process for concentrating and recovering gallium
Assignee: Teck Metals Ltd
•
Filing: 1976-07-08
•
Granted: 1978-01-31
•
Expires: 1996-07-08
Abstract
Abstract Gallium and other values are recovered from phosphorus-furnace flue-dust by treating dust with sulfuric acid to form a solution and a residue. The residue may be treated for recovery of values. Zinc is precipitated from the solution as zinc ammonium sulfate hexahydrate and an alkaline material is added to precipitate a gallium concentrate and to form a gallium-free solution, which may be treated for recovery of sulfate and phosphate values. The gallium concentrate may be upgraded by mixing concentrate with lime to precipitate calcium phosphate and by subsequently adding sodium hydroxide to redissolve coprecipitated gallium and aluminum compounds. Residual precipitate is recycled and the solution is neutralized to precipitate an upgraded concentrate. Aluminum may be removed as calcium aluminate. Upgraded concentrate may be dissolved in alkaline solution and the solution electrolyzed for deposition and recovery of gallium.
Inventors
- 👤 Thomas L. Charlton
- 👤 Robert F. Redden
- 👤 Horst E. Hirsch
- 👤 Shou C. Liang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:40
CPC Classifications
C; C22; C22B; C22B58/00; C22B7/00; C22B7/02; C25; C25C; C25C1/00; C25C1/22; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
107 words
A process for treating phosphorus-furnace flue dust containing gallium and zinc which comprises the steps of: 1. treating flue dust with sulfuric acid for formation of a leach solution and a leach residue; 2. separating the leach solution from the leach residue; 3. precipitating zinc in the leach solution in the presence of ammonium sulfate as zinc ammonium sulfate hexahydrate; 4. separating precipitated zinc from the solution; 5. adding an alkaline material to said solution for precipitation of a first gallium concentrate and formation of a first gallium-free solution; and 6. separating first gallium concentrate from said first gallium-free solution for recovery of said first gallium concentrate.
Claim 2
Dependent Claim
107 words
A process for treating phosphorus-furnace flue dust containing gallium and zinc which comprises the steps of: 1. treating flue dust with sulfuric acid for formation of a leach solution and a leach residue; 2. separating the leach solution from the leach residue; 3. precipitating zinc in the leach solution in the presence of ammonium sulfate as zinc ammonium sulfate hexahydrate; 4. separating precipitated zinc from the solution; 5. adding an alkaline material to said solution for precipitation of a first gallium concentrate and formation of a first gallium-free solution; and 6. separating first gallium concentrate from said first gallium-free solution for recovery of said first gallium concentrate.
Claim 3
Dependent Claim
38 words
A process as claimed in claim 1, wherein flue dust is subjected to pretreatment prior to treating dust with sulfuric acid which comprises a reduction of particle sizes of flue dust to sizes not larger than one centimeter.
Claim 4
Dependent Claim
36 words
A process as claimed in claim 1, wherein flue dust is subjected to pretreatment prior to treating dust with sulfuric acid which comprises wet-grinding flue dust in an aqueous slurry and separating ground dust from liquid.
Claim 5
Dependent Claim
80 words
A proces as claimed in claim 1, wherein the treatment of flue dust with sulfuric acid comprises the steps of: 1. mixing flue dust with sulfuric acid in an amount sufficient to provide free acid in the resulting leach solution in the range of 15 to 25%; 2. heating the mixture to a temperature in the range of 60° to 100° C.; and 3. agitating the mixture for a period of time in the range of one-half to 6 hours.
Claim 6
Dependent Claim
90 words
A process as claimed in claim 1, wherein the treatment of flue dust with sulfuric acid comprises the steps of: 1. mixing the flue dust with a limited amount of concentrated sulfuric acid; 2. heating the mixture to a temperature of at least 100° C.; 3. agitating the mixture for a period of time at least 15 minutes; and 4. leaching the mixture in an aqueous solution whereby said limited amount of sulfuric acid causes a free acid concentration in the leach solution in the range of 1 to 4%.
Claim 7
Dependent Claim
109 words
A process as claimed in claim 1, wherein the treatment of flue dust with sulfuric acid comprises the steps of: 1. mixing flue dust with a limited amount of concentrated sulfuric acid in a blunger; 2. maintaining the resulting mixture at a temperature in the range of 100° to 250° C. for a period of time in the range of 15 minutes to 2 hours; and 3. leaching the said mixture in an aqueous solution at a temperature in the range of 60° to 100° C. whereby said limited amount of sulfuric acid causes a free acid concentration in the leach solution in the range of 1 to 4%.
Claim 8
Dependent Claim
31 words
A process as claimed in claim 1 wherein zinc ammonium sulfate hexahydrate is precipitated in the leach solution in the presence of a concentration of at least 100 g/l ammonium sulfate.
Claim 9
Dependent Claim
77 words
A process as claimed in claim 1, wherein zinc ammonium sulfate hexahydrate is precipitated by adjusting the specific gravity of the leach solution in the range of 1.2 to 1.5, adding ammonium sulfate in an amount sufficient to provide a concentration of ammonium sulfate in solution in the range of 100 to 200 g/l, heating the solution to a temperature in the range of 60° to 100° C. and cooling the solution to 25° C. or lower.
Claim 10
Dependent Claim
74 words
A process as claimed in claim 1, wherein zinc ammonium sulfate hexahydrate is precipitated by adjusting the specific gravity of the leach solution in the range of 1.2 to 1.5, adding sulfuric acid and ammonia until the solution contains ammonium sulfate in the range of 100 to 200 g/l, maintaining the pH of the solution in the range of 1 to 2 during said addition and cooling the solution to 25° C. or lower.
Claim 11
Dependent Claim
94 words
A process as claimed in claim 1, wherein zinc ammonium sulfate hexahydrate is precipitated by adjusting the specific gravity of the leach solution in the range of 1.2 to 1.5, forming a precipitate by adding sulfuric acid and ammonia in controlled amounts until the solution contains ammonium sulfate in the range of 100 to 200 g/l, maintaining the pH of the solution at 1.5 during said addition, cooling the solution to 25° C. or lower, separating the precipitate, washing the precipitate with solution containing at least 100 g/l ammonium sulfate and recovering the precipitate.
Claim 12
Dependent Claim
74 words
A proces as claimed in claim 1, wherein the solution from step (4) is adjusted in specific gravity to a value in the range of 1.15 to 1.30, said solution is heated to a temperature in the range of 60° to 100° C. and the pH of said solution is raised to a value in the range of 3.5 to 5.0 by adding an alkaline material chosen from the group ammonia and ammonium hydroxide.
Claim 13
Dependent Claim
18 words
A process as claimed in claim 1, wherein said leach residue is treated for the recovery of values.
Claim 14
Dependent Claim
19 words
A process as claimed in claim 1, wherein said first gallium-free solution is treated for the recovery of values.
Claim 15
Dependent Claim
181 words
A process for treating phosphorus-furnace flue dust containing gallium, zinc and aluminum which comprises the steps of: 1. treating flue dust with sulfuric acid for formation of a leach solution and a leach residue; 2. separating leach solution from leach residue; 3. precipitating zinc in the leach solution in the presence of ammonium sulfate as zinc ammonium sulfate hexahydrate; 4. separating precipitated zinc from the solution; 5. adding an alkaline material to said solution for the precipitation of a first gallium concentrate and the formation of a first gallium-free solution; 6. separating first gallium concentrate from first gallium-free solution; 7. mixing first gallium concentrate containing phosphate in a slurry with lime in an amount which is at least stoichiometric to the phosphate content of the concentrate to form a precipitate comprising calcium phosphate and coprecipitated gallium and aluminum compounds in a gallate-aluminate solution, adding an amount of a suitable alkaline material sufficient to raise the pH of the slurry to at least 11 whereby coprecipitated gallium and aluminum compounds are redissolved in the gallate-aluminate solution and whereby a residual precipitate remains;
Claim 16
Dependent Claim
181 words
A process for treating phosphorus-furnace flue dust containing gallium, zinc and aluminum which comprises the steps of: 1. treating flue dust with sulfuric acid for formation of a leach solution and a leach residue; 2. separating leach solution from leach residue; 3. precipitating zinc in the leach solution in the presence of ammonium sulfate as zinc ammonium sulfate hexahydrate; 4. separating precipitated zinc from the solution; 5. adding an alkaline material to said solution for the precipitation of a first gallium concentrate and the formation of a first gallium-free solution; 6. separating first gallium concentrate from first gallium-free solution; 7. mixing first gallium concentrate containing phosphate in a slurry with lime in an amount which is at least stoichiometric to the phosphate content of the concentrate to form a precipitate comprising calcium phosphate and coprecipitated gallium and aluminum compounds in a gallate-aluminate solution, adding an amount of a suitable alkaline material sufficient to raise the pH of the slurry to at least 11 whereby coprecipitated gallium and aluminum compounds are redissolved in the gallate-aluminate solution and whereby a residual precipitate remains;
Claim 17
Dependent Claim
44 words
separating said residual precipitate from said gallate-aluminate solution; 9. neutralizing said gallate-aluminate solution with acid for precipitation of upgraded gallium concentrate and formation of a second gallium-free solution; and 10. separating upgraded gallium concentrate from second gallium-free solution for recovery of upgraded gallium concentrate.
Claim 18
Dependent Claim
44 words
separating said residual precipitate from said gallate-aluminate solution; 9. neutralizing said gallate-aluminate solution with acid for precipitation of upgraded gallium concentrate and formation of a second gallium-free solution; and 10. separating upgraded gallium concentrate from second gallium-free solution for recovery of upgraded gallium concentrate.
Claim 19
Dependent Claim
58 words
A process for treating phosphorus-furnace flue dust containing gallium, zinc and aluminum as claimed in claim 2 which comprises the steps of: 1. adding a suitable calcium compound to said gallate-aluminate solution of step (8) in claim 2 in an amount at least stoichiometric to the amount of aluminum in said solution for the precipitation of calcium aluminate;
Claim 20
Dependent Claim
47 words
separating precipitated aluminate from the gallate solution prior to neutralizing in step (9) in claim 2; 3. dissolving said upgraded concentrate in an alkaline solution; 4. electrolyzing alkaline solution of said upgraded concentrate for deposition of gallium and formation of spent electrolyte; and 5. recovering deposited gallium.
Claim 21
Dependent Claim
29 words
A process as claimed in claim 15, wherein the residual precipitate of step (1) of claim 3 is recycled to sulfuric acid treatment of step (1) of claim 2.
Claim 22
Dependent Claim
82 words
A process as claimed in claim 15, wherein calcium aluminate is precipitated from said gallate-aluminate solution with a slurry of a calcium compound chosen from the group of lime and calcium hydroxide in an amount of from one to two times the stoichiometric amount required to precipitate calcium aluminate at a temperature in the range of 60° to 100° C. and at a pH of at least 10, and wherein said solution and said slurry are reacted for at least two hours.
Claim 23
Dependent Claim
58 words
A process as claimed in claim 15, wherein upgraded gallium concentrate is recovered by adding sulfuric acid to said gallate-aluminate solution in an amount sufficient to lower the pH to a value of about 6, whereby said concentrate is precipitated, maintaining the solution at a temperature in the range of 60° to 100° C. and recovering said concentrate.
Claim 24
Dependent Claim
19 words
A process as claimed in claim 15 wherein said first gallium-free solution is treated for the recovery of values.
Claim 25
Dependent Claim
95 words
A process as claimed in claim 14, wherein the slurry of first concentrate and lime of step (7) is agitated for a first period of at least one hour at a temperature in the range of 60° to 100° C. wherein said suitable alkaline compound is an aqueous solution of sodium hydroxide which is subsequently added in an amount sufficient to raise to and maintain the pH of the slurry at a value in the range of 11 to 12 and wherein said slurry is agitated for a second period of at least one hour.
Claim 26
Dependent Claim
22 words
A process as claimed in claim 14, wherein spent electrolyte is recycled for redissolving calcium gallate and calcium aluminate in step (7).
Claim 27
Dependent Claim
29 words
A process as claimed in claim 14, wherein the residual precipitate of step (8) of claim 2 is recycled to sulfuric acid treatment of step (1) of claim 1.
Claim 28
Dependent Claim
58 words
A process as claimed in claim 14, wherein upgraded gallium concentrate is recovered by adding sulfuric acid to said gallate-alumunate solution in an amount sufficient to lower the pH to a value of about 6, whereby said concentrate is precipitated, maintaining the solution at a temperature in the range of 60° to 100° C. and recovering said concentrate.
Claim 29
Dependent Claim
43 words
A process as claimed in claim 14, wherein calcium aluminate is precipitated from the gallate-aluminate solution from step (2) by adding a slurry of a calcium compound chosen from the group of lime and calcium hydroxide and removing said aluminate from the solution.
References Cited (Backward Citations)
US1855455A
Cited
US2557326A
Cited
US2582376A
Cited
US2582377A
Cited
US2582378A
Cited
US3170857A
Cited
US3904497A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-30 | 1981-08-01 | 1982-01-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-30 | 1985-08-01 | 1986-01-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-30 | 1989-08-01 | 1990-01-31 | $7700.00 | Window Closed / Lapsed |