Master alloy for powders
Assignee: Ford Motor Co
•
Filing: 1976-07-06
•
Granted: 1978-01-31
•
Expires: 1996-07-06
Abstract
Abstract A master alloy powder is formulated for admixture to an iron based powder to provide liquid phase sintering and production of a substantially homogeneous product having the characteristics of a wrought alloy product. The master alloy powder contains at least two elements selected from the group consisting of manganese, nickel molybdenum, chromium, copper, carbon and iron. The master powder may contain additions of silicon up to 5% and rare earth metals up to 2%, either of which assist to speed up diffusion and create a more favorable liquidus-solidus relationship within the master alloy powder.
Inventors
- 👤 Stanislaw Mocarski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 10:58
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0264; C22C33/0207
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
149 words
For use in a method of making sintered alloy steel parts by the compaction and sintering of admixed powders to obtain alloying, a low melting master powder admixture of alloying ingredients to be added to an iron based powder except for the addition of a desired quantity of graphite, the master powder admixture consisting of at least two but up to all of the powder elements selected from the group consisting of manganese, nickel, molybdenum, chromium, copper and iron, with molybdenum being in the range of 5-15% by weight of the master powder admixture when selected along with the absence of copper, and iron being less than 20% by weight of said master powder admixture when selected, said selected elements being proportioned within said master powder admixture to possess a liquidus temperature residing between 1800°-2250° F and a melting range for all ingredients of no greater than 350° F.
Claim 2
Dependent Claim
149 words
For use in a method of making sintered alloy steel parts by the compaction and sintering of admixed powders to obtain alloying, a low melting master powder admixture of alloying ingredients to be added to an iron based powder except for the addition of a desired quantity of graphite, the master powder admixture consisting of at least two but up to all of the powder elements selected from the group consisting of manganese, nickel, molybdenum, chromium, copper and iron, with molybdenum being in the range of 5-15% by weight of the master powder admixture when selected along with the absence of copper, and iron being less than 20% by weight of said master powder admixture when selected, said selected elements being proportioned within said master powder admixture to possess a liquidus temperature residing between 1800°-2250° F and a melting range for all ingredients of no greater than 350° F.
Claim 3
Dependent Claim
38 words
The low melting admixture of claim 1, in which manganese, when selected, is in the range of 36-75% by weight of the admixture and nickel, when selected, is in the range of 10-30% by weight of the admixture.
Claim 4
Dependent Claim
22 words
The low melting admixture of claim 2, in which manganese and nickel are respectively maintained in the ranges of 40-56% and 14-30%.
Claim 5
Dependent Claim
35 words
The admixture of claim 1, which consists only of manganese in the range of 36-75% and Nickel in the range of 10-30% each by weight of the admixture, except for wetting agents and diffusion promoters.
Claim 6
Dependent Claim
32 words
The admixture in claim 1, which consists only of manganese about 72%, nickel about 14% and copper about 14%, each by weight of the admixture, except for wetting agents and diffusion promoters.
Claim 7
Dependent Claim
41 words
The low melting admixture of claim 1, which further consists of an auxiliary wetting element selected from the group consisting of: silicon in the range of 1-5%, rare earths in the range of 0.2-1.5%, and yttrium in the range of 0.05-0.20%.
Claim 8
Dependent Claim
23 words
The low melting admixture of claim 1, which consists essentially of about 40-44% manganese, 25-30% nickel, 0-15% chromium, 5-11% molybdenum, and 10-19% iron.
Claim 9
Dependent Claim
75 words
The low melting admixture of claim 1, in which said molybdenum and iron when both selected are no greater than 30% taken together by weight of the admixture, said elements being selected to melt as a combination substantially lower than the melting temperature of the iron based powder to which the admixture is blended, said elements further being selected to provide wetting of substantially each particle of the iron base powder by the melted admixture.
Claim 10
Dependent Claim
28 words
The low melting admixture of claim 1, in which the iron content is about twice the molybdenum content to obtain the lowest melting point when molybdenum is selected.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-30 | 1981-08-01 | 1982-01-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-30 | 1985-08-01 | 1986-01-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-30 | 1989-08-01 | 1990-01-31 | $7700.00 | Window Closed / Lapsed |