Process for upgrading ores containing baddeleyite

Claim 2

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion comprising of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is corresponding increased, ii. magnetically treating the acid leached product of (i) by high intensity magnetic separation iii. and recovering non-magnetic purified particulate baddeleyite.

Claim 3

A process according to claim 1 wherein step (i) is carried out with liquid strong mineral acid of which the main acid component is selected from the group consisting of hydrochloric acid, sulphuric acid and nitric acid and combinations of such acids with one another.

Claim 4

A process of claim 2 wherein the total acid concentration is between 2 and 7 Normal.

Claim 5

A process according to claim 2 wherein step (i) is carried out at a temperature of at least 70° C.

Claim 6

A process according to claim 3 wherein the total acid concentration is between 2N and 7N and which contains at least 6 gram/liter of nitrate ion.

Claim 7

A process according to claim 5 wherein the process of step (i) is carried out at at least 85° C in the presence of between 6 and 150 g/liter of nitrate.

Claim 8

A process according to claim 1 wherein said strong mineral acid in step (i) is essentially fluoride-free.

Claim 9

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is corresponding increased, ii. gravity separating the acid leached product of (i) iii. and recovering non-magnetic purified particulate baddeleyite.

Claim 10

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is corresponding increased, ii. gravity separating the acid leached product of (i) iii. and recovering non-magnetic purified particulate baddeleyite.

Claim 11

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is corresponding increased, ii. magnetically treating and gravity separating the acid leached product of (i) iii. and recovering non-magnetic purified particulate baddeleyite.

Claim 12

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is corresponding increased, ii. magnetically treating and gravity separating the acid leached product of (i) iii. and recovering non-magnetic purified particulate baddeleyite.

Claim 13

A process as claimed in claim 9 carried out on baddeleyite at a temperature of at least 85° C with an acid leach liquid containing between 6 and 150 gram/liter of nitrate ion.

Claim 14

A process as claimed in claim 9 wherein the leaching liberates ilmenite and baddeleyite particles from one another, those particles being then separated by high intensity magnetic separation.

Claim 15

A process as claimed in claim 11, wherein leching is carried out in two stages, namely one wherein the leach liquor is essentially hydrochloric acid containing also nitrate ion and one wherein the leach liquor is essentially sulphuric acid containing also nitrate ion.

Claim 16

A process as claimed in claim 12 wherein leaching with hydrochloric acid precedes leaching with said sulphuric acid.

Claim 17

A process as claimed in claim 13 wherein concentrated sulphuric acid is gradually added in the course of leaching to a leach liquor consisting of aqueous hydrochloric acid containing nitrate.

Claim 18

A process as claimed in claim 9 wherein at least half the mineral material being treated has a particle size larger than 0.15 mm.

Claim 19

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with strong mineral acid of which the main acid component is selected from the group consisting of hydrochloric acid, sulphuric acid, and nitric acid and combinations of such acids with one another, of which the total acid concentration is between 2N and 7N at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is correspondingly increased and ii. recovering the thus separated baddeleyite crystals from the acid leach:

Claim 20

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with strong mineral acid of which the main acid component is selected from the group consisting of hydrochloric acid, sulphuric acid, and nitric acid and combinations of such acids with one another, of which the total acid concentration is between 2N and 7N at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is correspondingly increased and ii. recovering the thus separated baddeleyite crystals from the acid leach:

Claim 21

A process for upgrading of ore containing baddeleyite in the form of crystals from composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with a. a substantially fluoride free mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is corresponding increased, then with b. a mineral acid containing fluoride ion under othewise similar reaction conditions as in step (a) ii. magnetically treating the acid leached product of (i) by high intensity magnetic separation iii. and recovering non-magnetic purified particular baddeleyite.

Claim 22

A process for upgrading of ore containing baddeleyite in the form of crystals from composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with a. a substantially fluoride free mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is corresponding increased, then with b. a mineral acid containing fluoride ion under othewise similar reaction conditions as in step (a) ii. magnetically treating the acid leached product of (i) by high intensity magnetic separation iii. and recovering non-magnetic purified particular baddeleyite.

Claim 23

A process for upgrading of ore containing baddeleyite in the form of crystals from composite ore particles of the ore comprising the steps of i. comminuting an ore comprising the zirconium ore mineral baddeleyite, thereby to provide composite ore particles in admixture with minerals including apatite and magnetite, ii. removing the bulk of magnetite and apatite from the comminuted composite ore particles to provide a concentrate composed of particles, the major portion of which have diameters of 0.074 to 0.5 mm as determined by screen analysis, iii. subjecting said concentrate to gravity concentration to yield: a. a particulate baddeleyite concentrate containing zirconium and hafnium oxides as the major portion, b. a middling fraction of particulate material (R) containing zirconium and hafnium oxides in lesser concentration than the concentrate and including composite ore particles containing baddeleyite c. a tailings fraction of particulate material (S) containing only such portions of zirconium and hafnium oxide which escaped recovery in the concentrate and middling fractions, and iv. comminuting said middling fraction and recycling it in gravity concentration to yield additional baddeleyite concentrate, such concentrate which includes the concentrate of (iii)a) being composed of particles more than half of which by weight are greater than 0.15 millimeters in size v. leaching said composite ore particles of (iv) supra, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperarture not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is correspondingly increased, vi. magnetically treating the acid leached product of (i) by high intensity magnetic separation vii. and recovering non-magnetic purified particulate baddeleyite.

Claim 24

A process for upgrading of ore containing baddeleyite in the form of crystals from composite ore particles of the ore comprising the steps of i. comminuting an ore comprising the zirconium ore mineral baddeleyite, thereby to provide composite ore particles in admixture with minerals including apatite and magnetite, ii. removing the bulk of magnetite and apatite from the comminuted composite ore particles to provide a concentrate composed of particles, the major portion of which have diameters of 0.074 to 0.5 mm as determined by screen analysis, iii. subjecting said concentrate to gravity concentration to yield: a. a particulate baddeleyite concentrate containing zirconium and hafnium oxides as the major portion, b. a middling fraction of particulate material (R) containing zirconium and hafnium oxides in lesser concentration than the concentrate and including composite ore particles containing baddeleyite c. a tailings fraction of particulate material (S) containing only such portions of zirconium and hafnium oxide which escaped recovery in the concentrate and middling fractions, and iv. comminuting said middling fraction and recycling it in gravity concentration to yield additional baddeleyite concentrate, such concentrate which includes the concentrate of (iii)a) being composed of particles more than half of which by weight are greater than 0.15 millimeters in size v. leaching said composite ore particles of (iv) supra, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperarture not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is correspondingly increased, vi. magnetically treating the acid leached product of (i) by high intensity magnetic separation vii. and recovering non-magnetic purified particulate baddeleyite.

Claim 25

A process for upgrading of ore containing baddeleyite in the form of crystals from composite ore particles of the ore comprising the steps of i. comminuting an ore comprising the zirconium ore mineral baddeleyite, thereby to provide composite ore particles in admixture with minerals including apatite and magnetite, ii. removing the bulk of magnetite and apatite from the comminuted composite ore particles to provide a concentrate composed of particles, the major portion of which have diameters of 0.074 to 0.5 mm as determined by screen analysis, iii. subjecting said concentrate to gravity concentration to yield: a. a particulate baddeleyite concentrate containing zirconium and hafnium oxides as the major portion, b. a middling fraction of particulate material (R) containing zirconium and hafnium oxides in lesser concentration than the concentrate and including composite ore particles containing baddeleyite c. a tailings fraction of particulate material (S) containing only such portions of zirconium and hafnium oxide which escaped recovery in the concentrate and middling fractions, and iv. leaching said middling fraction composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with a mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is correspondingly increased, v. magnetically treating the acid leached product of (i) by high intensity magnetic separation vi. and recovering non-magnetic purified particularate baddeleyite.

Claim 26

A process for upgrading of ore containing baddeleyite in the form of crystals from composite ore particles of the ore comprising the steps of i. comminuting an ore comprising the zirconium ore mineral baddeleyite, thereby to provide composite ore particles in admixture with minerals including apatite and magnetite, ii. removing the bulk of magnetite and apatite from the comminuted composite ore particles to provide a concentrate composed of particles, the major portion of which have diameters of 0.074 to 0.5 mm as determined by screen analysis, iii. subjecting said concentrate to gravity concentration to yield: a. a particulate baddeleyite concentrate containing zirconium and hafnium oxides as the major portion, b. a middling fraction of particulate material (R) containing zirconium and hafnium oxides in lesser concentration than the concentrate and including composite ore particles containing baddeleyite c. a tailings fraction of particulate material (S) containing only such portions of zirconium and hafnium oxide which escaped recovery in the concentrate and middling fractions, and iv. leaching said middling fraction composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with a mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is correspondingly increased, v. magnetically treating the acid leached product of (i) by high intensity magnetic separation vi. and recovering non-magnetic purified particularate baddeleyite.

Claim 27

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. comminuting an ore comprising the zirconium ore mineral baddeleyite, thereby to provide composite ore particles in admixture with minerals including apatite and magnetite, ii. removing the bulk of magnetite and apatite from the comminuted ore particles to provide a preconcentrate composed of particles, the major portion of which have diameters of 0.074 to 0.5 mm as determined by screen analysis. iii. subjecting said preconcentrate to gravity concentration to yield: a. a particulate baddeleyite concentrate containing zirconium and hafnium oxides as the major portion, b. a middling fraction of particulate material (R) containing zirconium and hafnium oxides in lesser concentration than the concentrate and including composite ore particles containing baddeleyite, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral and materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, c. a tailings fraction of particulate material (S) containing only such portions of zirconium and hafnium oxide which escaped recovery in the concentrate and middling fraction, iv. subjecting said middling fraction to leaching with mineral acid to physically release the baddeleyite in particulate form from said other mineral of the composite particles, also in particulate form, thereby converting the major portion of those particles in said middling fraction which prior to said leaching are in a size range of 0.2 through 0.15 mm diameter, so as to after said leaching be in a size range of 0.15 to 0.074 mm diameter as determined by screen analysis; v. recycling the product of step (iv) to step (iii), and

Claim 28

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. comminuting an ore comprising the zirconium ore mineral baddeleyite, thereby to provide composite ore particles in admixture with minerals including apatite and magnetite, ii. removing the bulk of magnetite and apatite from the comminuted ore particles to provide a preconcentrate composed of particles, the major portion of which have diameters of 0.074 to 0.5 mm as determined by screen analysis. iii. subjecting said preconcentrate to gravity concentration to yield: a. a particulate baddeleyite concentrate containing zirconium and hafnium oxides as the major portion, b. a middling fraction of particulate material (R) containing zirconium and hafnium oxides in lesser concentration than the concentrate and including composite ore particles containing baddeleyite, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral and materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, c. a tailings fraction of particulate material (S) containing only such portions of zirconium and hafnium oxide which escaped recovery in the concentrate and middling fraction, iv. subjecting said middling fraction to leaching with mineral acid to physically release the baddeleyite in particulate form from said other mineral of the composite particles, also in particulate form, thereby converting the major portion of those particles in said middling fraction which prior to said leaching are in a size range of 0.2 through 0.15 mm diameter, so as to after said leaching be in a size range of 0.15 to 0.074 mm diameter as determined by screen analysis; v. recycling the product of step (iv) to step (iii), and

Claim 29

subjecting the concentrate of step (iii) which includes reconcentrated product of combined steps (v) and (i) to high intensity magnetic separation to remove particles therefrom which are attracted under the conditions of said high intensity magnetic separation, and to leave behind purified baddeleyite composite ore particles and recovering non-magnetic purified particulate baddeleyite.

Claim 30

subjecting the concentrate of step (iii) which includes reconcentrated product of combined steps (v) and (i) to high intensity magnetic separation to remove particles therefrom which are attracted under the conditions of said high intensity magnetic separation, and to leave behind purified baddeleyite composite ore particles and recovering non-magnetic purified particulate baddeleyite.

Claim 31

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is corresponding increased, ii. passing the acid leached product of (i) through an elastrostatic field gradient, iii. and recovering non-attracted purified particulate baddeleyite passed through said field.

Claim 32

A process for upgrading of ore containing baddeleyite in the form of crystals from the composite ore particles of the ore comprising the steps of i. leaching said composite ore particles, the major portion of said composite particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: A. baddeleyite crystals B. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and C. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original value and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is corresponding increased, ii. passing the acid leached product of (i) through an elastrostatic field gradient, iii. and recovering non-attracted purified particulate baddeleyite passed through said field.

Claim 33

A process for upgrading of ore containing baddeleyite in the form of crystals from composite ore particles of the ore comprising the steps of 1. i. comminuting an ore comprising the zirconium ore mineral baddeleyite, thereby to provide composite ore particles in admixture with minerals including apatite and magnetite, ii. removing the bulk of magnetite and apatite from the comminuted composite ore particles to provide a preconcentrate composed of particles, the major portion of which have diameters of 0.074 to 0.5 mm as determined by screen analysis, iii. subjecting said preconcentrate to leaching with mineral acid to physically release the baddeleyite in particulate form from said other mineral of the composite particles, also in particulate form, iv. subjecting said preconcentrate to gravity concentration to yield: a. a particulate baddeleyite concentrate containing zirconium and hafnium oxides as the major portion, b. a middling fraction of particulate material (R) containing zirconium and hafnium oxides in lesser concentration than the concentrate and including composite ore particles containing baddeleyite, c. a tailings fraction of particulate material (S) containing only such portions of zirconium and hafnium oxide which escaped recovery in the concentrate and middling fraction, v. recycling the product (b) of step (iv) to the beginning of step (iv), and

Claim 34

A process for upgrading of ore containing baddeleyite in the form of crystals from composite ore particles of the ore comprising the steps of 1. i. comminuting an ore comprising the zirconium ore mineral baddeleyite, thereby to provide composite ore particles in admixture with minerals including apatite and magnetite, ii. removing the bulk of magnetite and apatite from the comminuted composite ore particles to provide a preconcentrate composed of particles, the major portion of which have diameters of 0.074 to 0.5 mm as determined by screen analysis, iii. subjecting said preconcentrate to leaching with mineral acid to physically release the baddeleyite in particulate form from said other mineral of the composite particles, also in particulate form, iv. subjecting said preconcentrate to gravity concentration to yield: a. a particulate baddeleyite concentrate containing zirconium and hafnium oxides as the major portion, b. a middling fraction of particulate material (R) containing zirconium and hafnium oxides in lesser concentration than the concentrate and including composite ore particles containing baddeleyite, c. a tailings fraction of particulate material (S) containing only such portions of zirconium and hafnium oxide which escaped recovery in the concentrate and middling fraction, v. recycling the product (b) of step (iv) to the beginning of step (iv), and

Claim 35

i. leaching said concentrate of step (iv) (a) which includes preconcentrated product of combined steps (v) and (iv), the major portion of said concentrate particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: a. baddeleyite crystals b. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and c. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original valve and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is correspondingly increased, ii. magnetically treating the acid leached product of (i) by high intensity magnetic separation, iii. and recovering non-magnetic purified particulate baddeleyite.

Claim 36

i. leaching said concentrate of step (iv) (a) which includes preconcentrated product of combined steps (v) and (iv), the major portion of said concentrate particles having a diameter of between 0.1 and 0.5 mm as determined by screen analysis, the composite particles in said portion consisting of: a. baddeleyite crystals b. other mineral materials selected from the group consisting of paramagnetic and ferromagnetic minerals of iron, of titanium comprising ilmenite, and of radioactive minerals comprising those of thorium and uranium, and c. a carbonatitic or siliceous or carbonatitic and siliceous cement bonding said baddeleyite to said other mineral materials, with mineral acid at elevated temperature not exceeding acid reflux temperature to dissolve said cement until said baddeleyite is separated from said other mineral materials and the size composition of the mineral material between 0.2 and 0.15 millimeters is reduced to less than half its original valve and material in the size range of 0.15 millimeters to 0.074 millimeters in diameter is correspondingly increased, ii. magnetically treating the acid leached product of (i) by high intensity magnetic separation, iii. and recovering non-magnetic purified particulate baddeleyite.