Process of shot peening and cleaning and preparing shot pellets therefor
Assignee: Individual
•
Filing: 1977-03-09
•
Granted: 1978-01-10
•
Expires: 1997-03-09
Abstract
Abstract A process of compression stressing shot pellets to increase the fatigue strength or resistance thereof to brittle fractures by impact of the pellets during shot peening and cleaning operations wherein the elastic radial tensile stress at the surface of the pellets is maintained at a safe low value during initial compression stressing and preparation for and performance of peening and cleaning operations. The process entails subjecting the pellets initially to compression stresses of sufficiently low value to avoid the spontaneous formation of superficial or surface cracks in pellets formed of notch sensitive material and then subjecting the pellets to stresses normal in shot peening and cleaning operations. The compression stresses occurring at the surface of the pellets in the initial step of the process minimize the likelihood of formation of surface cracks in the pellets when subsequently subjected to the greater impact forces to which the pellets are subject during peening and cleaning operations, thus increasing the life of the pellets.
Inventors
- 👤 John C. Straub
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:53
CPC Classifications
C; C21; C21D; C21D7/00; C21D7/02; C21D7/04; C21D7/06; B; B24; B24C; B24C1/00; B24C1/10; B24C11/00; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49636; Y10T29/49643; Y10T29/49679; Y10T29/49694
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
116 words
In a process of compression stressing shot pellets for use in shot peening and cleaning operations, the step of imparting residual compressive stresses to substantially the entire surface of each pellet before use thereof in a peening or cleaning operation, said stresses being imparted to said pellets by impact of a value less than that to which the pellets are subjected in peening and cleaning operations and so related to the hardness and notch sensitivity of the metal of the pellets as to stress the surfaces of the pellets without creating cracks in the surfaces of the pellets and to produce a distribution of residual stresses in the pellets favorable to increase of fatigue strength thereof.
Claim 2
Dependent Claim
116 words
In a process of compression stressing shot pellets for use in shot peening and cleaning operations, the step of imparting residual compressive stresses to substantially the entire surface of each pellet before use thereof in a peening or cleaning operation, said stresses being imparted to said pellets by impact of a value less than that to which the pellets are subjected in peening and cleaning operations and so related to the hardness and notch sensitivity of the metal of the pellets as to stress the surfaces of the pellets without creating cracks in the surfaces of the pellets and to produce a distribution of residual stresses in the pellets favorable to increase of fatigue strength thereof.
Claim 3
Dependent Claim
37 words
The method defined in claim 1, wherein the shot pellets are impacted against a member of at least substantially equal hardness at a velocity in the order of 24 feet per second to 30 feet per second.
Claim 4
Dependent Claim
50 words
The method defined in claim 1, wherein the shot pellets are formed of metal of hardenss in the range of 45 to 62 Rc and are impacted against a member of substantially similar hardness at a velocity in the order of 24 feet per second to 30 feet per second.
Claim 5
Dependent Claim
46 words
The method defined in claim 1, and the additional step of further compression stressing the surfaces of said initially stressed pellets at an intensity substantially greater than the intensity of said initial stressing thereof and of a value to prevent formation of cracks in the pellets.
Claim 6
Dependent Claim
61 words
The method defined in claim 4, wherein the shot pellets are of a diameter in the range from 0.011 inches to 0.066 inches and are projected against a work piece in the additional step at a velocity in the range from 233 feet per second to 90 feet per second selected in inverse proportion to the diameter of the shot pellets.
Claim 7
Independent Claim
88 words
The method of increasing the fatigue life of metal shot pellets which comprises compression substantially the entire surfaces of said pellets at a low intensity in a first step and thereafter further compression stressing the surfaces of said pellets in a second step at an intensity substantially greater than the intensity of said initial stressing thereof, said first step compression stressing being of an intensity to prevent the formation of cracks in the pellets during the first step and during higher intensity compression stressing in the second step.
Claim 8
Independent Claim
88 words
The method of increasing the fatigue life of metal shot pellets which comprises compression substantially the entire surfaces of said pellets at a low intensity in a first step and thereafter further compression stressing the surfaces of said pellets in a second step at an intensity substantially greater than the intensity of said initial stressing thereof, said first step compression stressing being of an intensity to prevent the formation of cracks in the pellets during the first step and during higher intensity compression stressing in the second step.
Claim 9
Dependent Claim
61 words
The method defined in claim 6, wherein the first compression stressing of the pellets is of a magnitude to produce plastic flow at the surfaces of the pellets sufficient to protect the surfaces of the pellets against occurrence of cracks during the second compression stressing of the pellets in which a greater depth of compressive stress in the pellets is produced.
References Cited (Backward Citations)
US2077639A
Cited
US2758360A
Cited
US3073022A
Cited
US3316748A
Cited
US3204320A
Cited
US3271992A
Cited
GB1320748A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-09 | 1981-07-11 | 1982-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-09 | 1985-07-11 | 1986-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-09 | 1989-07-11 | 1990-01-10 | $7700.00 | Window Closed / Lapsed |