Ceramics of silicon nitride
Assignee: Toyota Central R&D Labs Inc
•
Filing: 1977-04-08
•
Granted: 1978-01-03
•
Expires: 1997-04-08
Abstract
Abstract Ceramic products composed essentially of a novel silicon nitride solid solution, which have high heat resistance, high abrasion resistance and low thermal expansion are obtained by sintering mixed powders of silicon nitride, alumina and aluminum nitride. The sintering includes heating said mixed powders at a temperature between 1650° C and 2000° C under a high pressure or no pressure. During the heating most of the alumina and aluminum nitride are occluded in silicon nitride and said ceramics products composed of silicon nitride solid solution are formed.
Inventors
- 👤 Osami Kamigaito
- 👤 Yoichi Oyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:36
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/597
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
87 words
A high heat resistant and high abrasion resistant ceramic comprising a silicon nitride solid solution, wherein said silicon nitride solid solution is formed by sintering a powdered mixture consisting of from 10 mol percent to 80 mol percent of silicon nitride, from 10 mol percent to 88 mol percent of alumina and from 2 mol percent to 70 mol percent of aluminum nitride at a temperature from about 1650° C to about 2000° C in a non-oxidizing atmosphere for a time between about 10 to 40 minutes.
Claim 2
Dependent Claim
87 words
A high heat resistant and high abrasion resistant ceramic comprising a silicon nitride solid solution, wherein said silicon nitride solid solution is formed by sintering a powdered mixture consisting of from 10 mol percent to 80 mol percent of silicon nitride, from 10 mol percent to 88 mol percent of alumina and from 2 mol percent to 70 mol percent of aluminum nitride at a temperature from about 1650° C to about 2000° C in a non-oxidizing atmosphere for a time between about 10 to 40 minutes.
Claim 3
Dependent Claim
24 words
The ceramic of claim 1 wherein said sintering is carried out under a pressure between about 100 kg/cm 2 and 300 kg/cm 2 .
Claim 4
Dependent Claim
43 words
The ceramic of claim 1 wherein said mixture consists of from 20 mol percent to 78 mol percent of silicon nitride, from 20 mol percent to 78 mol percent of alumina and from 2 mol percent to 40 mol percent of aluminum nitride.
Claim 5
Dependent Claim
43 words
The ceramic of claim 2 wherein said mixture consists of from 20 mol percent to 78 mol percent of silicon nitride, from 20 mol percent to 78 mol percent of alumina and from 2 mol percent to 40 mol percent of aluminum nitride.
Claim 6
Dependent Claim
233 words
A high heat resistant and high abrasion resistant ceramic comprising a silicon nitride solid solution, wherein said silicon nitride solid solution is formed by sintering a powdered mixture consisting of silicon nitride, alumina and aluminum nitride, the amounts thereof being defined by and included in a polygonal area on a triangular coordinate diagram of silicon nitride, alumina and aluminum nitride, the polygon having five apexes of which the first one being defined by a first ratio of 80 mol percent of silicon nitride, 10 mol percent of alumina and 10 mol percent of aluminum nitride, the second one being defined by a second ratio of 20 mol percent of silicon nitride, 10 mol percent of alumina and 70 mol percent of aluminum nitride, the third one being defined by a third ratio of 10 mol percent of silicon nitride, 20 mol percent of alumina and 70 mol percent of aluminum nitride, the fourth one being defined by a fourth ratio of 10 mol percent of silicon nitride, 88 mol percent of alumina and 2 mol percent of aluminum nitride, and a fifth one being defined by a fifth ratio of 80 mol percent of silicon nitride, 18 mol percent of alumina and 2 mol percent of aluminum nitride and sintering said mixture at a temperature between 1650° C and 2000° C in a non-oxidizing atmosphere for a time between 10 and 40 minutes.
Claim 7
Dependent Claim
233 words
A high heat resistant and high abrasion resistant ceramic comprising a silicon nitride solid solution, wherein said silicon nitride solid solution is formed by sintering a powdered mixture consisting of silicon nitride, alumina and aluminum nitride, the amounts thereof being defined by and included in a polygonal area on a triangular coordinate diagram of silicon nitride, alumina and aluminum nitride, the polygon having five apexes of which the first one being defined by a first ratio of 80 mol percent of silicon nitride, 10 mol percent of alumina and 10 mol percent of aluminum nitride, the second one being defined by a second ratio of 20 mol percent of silicon nitride, 10 mol percent of alumina and 70 mol percent of aluminum nitride, the third one being defined by a third ratio of 10 mol percent of silicon nitride, 20 mol percent of alumina and 70 mol percent of aluminum nitride, the fourth one being defined by a fourth ratio of 10 mol percent of silicon nitride, 88 mol percent of alumina and 2 mol percent of aluminum nitride, and a fifth one being defined by a fifth ratio of 80 mol percent of silicon nitride, 18 mol percent of alumina and 2 mol percent of aluminum nitride and sintering said mixture at a temperature between 1650° C and 2000° C in a non-oxidizing atmosphere for a time between 10 and 40 minutes.
Claim 8
Dependent Claim
134 words
The ceramic as defined in claim 5 wherein the composition of said mixture falls within the polygon having four apexes of which the first one is defined by a first ratio of 78 mol percent of silicon nitride, 20 mol percent of alumina and 2 mol percent of aluminum nitride, the second one being defined by a second ratio of 40 mol percent of silicon nitride, 20 mol percent of alumina and 40 mol percent of aluminum nitride, the third one being defined by a third ratio of 20 mol percent of silicon nitride, 40 mol percent of alumina and 40 mol percent aluminum nitride, and the fourth one being defined by a fourth ratio of 20 mol percent of silicon nitride, 78 mol percent of alumina and 2 mol percent of aluminum nitride.
Claim 9
Independent Claim
82 words
A method of producing a high heat-resistant and high abrasion-resistant ceramic comprising a silicon nitride solid solution comprising the steps of forming a powdered mixture of from 10 mol percent to 80 mol percent of silicon nitride, from 10 mol percent to 88 mol percent of alumina and from 2 mol percent to 70 mol percent of aluminum nitride and sintering said mixture at a temperature from 1650° C to 2000° C in a non-oxidizing atmosphere for from 10 to 40 minutes.
Claim 10
Independent Claim
82 words
A method of producing a high heat-resistant and high abrasion-resistant ceramic comprising a silicon nitride solid solution comprising the steps of forming a powdered mixture of from 10 mol percent to 80 mol percent of silicon nitride, from 10 mol percent to 88 mol percent of alumina and from 2 mol percent to 70 mol percent of aluminum nitride and sintering said mixture at a temperature from 1650° C to 2000° C in a non-oxidizing atmosphere for from 10 to 40 minutes.
Claim 11
Dependent Claim
25 words
The method of claim 7 wherein said sintering is carried out under a pressure from between about 100 kg/cm 2 and 300 kg/cm 2 .
Claim 12
Dependent Claim
42 words
The method of claim 7 wherein said mixture comprises from 20 mol percent to 78 mol percent of silicon nitride, from 20 mol percent to 78 mol percent of alumina and from 2 mol percent to 40 mol percent of aluminum nitride.
References Cited (Backward Citations)
GB970639A
Cited
US3837871A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-02 | 1981-07-04 | 1982-01-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-02 | 1985-07-04 | 1986-01-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-02 | 1989-07-04 | 1990-01-03 | $7700.00 | Window Closed / Lapsed |