US4064194A
Expired / Lapsed
US
⏱️ 0.0 years remaining
High solids urethane coatings
Assignee: Lilly Industries Inc
•
Filing: 1976-05-28
•
Granted: 1977-12-20
•
Expires: 1996-05-28
Abstract
Abstract A two-package urethane forming coating composition comprises a hydroxyl-bearing polymer having ethylenic unsaturation dispersed in fugitive solvent; and a multi-isocyanate dispersed in fugitive solvent. The coating composition cures by heating with an in situ reaction of the hydroxyl-isocyanate reaction in combination with an in situ free-radical addition polymerization through the ethylenic unsaturation.
Inventors
- 👤 James M. Evans
- 👤 Donald R. Stevenson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:29
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/67; C08G18/6795; C08G18/68
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
141 words
A two-package, urethane-forming coating composition formulated by combining said two packages, an applied film of said coating composition being curable upon heating to form a heat-cured urethane film, which comprises: said first package comprising a hydroxyl-bearing polymer having ethylenic unsaturation and having a molecular weight not substantially greater than about 3,000, and said polymer being dispersed in fugitive organic solvent; and said second package comprising a multi-isocyanate compound having a multiplicity of isocyanate groups and being dispersed in fugitive organic solvent, the total proportion of said fugitive solvents in both said packages being not substantially greater than about 30% by volume of said coating composition, said applied film of said coating composition curable upon heating by in situ formation of urethane linkages by the hydroxyl-isocyanate reaction in combination with in situ free-radical addition polymerization through said ethylenic unsaturation of said polymer.
Claim 2
Dependent Claim
141 words
A two-package, urethane-forming coating composition formulated by combining said two packages, an applied film of said coating composition being curable upon heating to form a heat-cured urethane film, which comprises: said first package comprising a hydroxyl-bearing polymer having ethylenic unsaturation and having a molecular weight not substantially greater than about 3,000, and said polymer being dispersed in fugitive organic solvent; and said second package comprising a multi-isocyanate compound having a multiplicity of isocyanate groups and being dispersed in fugitive organic solvent, the total proportion of said fugitive solvents in both said packages being not substantially greater than about 30% by volume of said coating composition, said applied film of said coating composition curable upon heating by in situ formation of urethane linkages by the hydroxyl-isocyanate reaction in combination with in situ free-radical addition polymerization through said ethylenic unsaturation of said polymer.
Claim 3
Dependent Claim
14 words
The coating composition of claim 1 wherein said hydroxyl-bearing polymer is a polyol-bearing polymer.
Claim 4
Dependent Claim
46 words
The coating composition of claim 1 wherein a portion of said fugitive solvent of package one is replaced with an ethlenically unsaturated diluent reactive with said ethylenic unsaturation of said hydroxyl-bearing polymer and at least a portion of said diluent cures into said film upon heating.
Claim 5
Dependent Claim
18 words
The coating composition of claim 3 wherein said ethylenically unsaturated diluent is an acrylic and/or allyl functional diluent.
Claim 6
Dependent Claim
47 words
The coating composition of claim 1 wherein a portion of said fugitive solvent of package two is replaced with a non-hydroxyl-bearing ethylenically unsaturated diluent reactive with said ethylenic unsaturation of said hydroxyl-bearing polymer and at least a portion of said diluent cures into said film upon heating.
Claim 7
Dependent Claim
19 words
The coating composition of claim 5 wherein said non-hydroxyl-bearing ethylenically unsaturated diluent is an acrylic and/or allyl functional diluent.
Claim 8
Dependent Claim
35 words
The coating composition of claim 1 wherein the total of said fugitive solvent in said coating composition is sufficient so that the viscosity of said coating composition is not substantially greater than about 500 centipoises.
Claim 9
Dependent Claim
17 words
The coating composition of claim 7 wherein said viscosity is between about 50 and about 500 centipoises.
Claim 10
Dependent Claim
17 words
The coating composition of claim 8 wherein said viscosity is between about 100 and about 200 centipoises.
Claim 11
Dependent Claim
21 words
A substrate having the coating composition of claim 1 coated thereon as a film and said film having been heat cured.
Claim 12
Dependent Claim
138 words
A process for coating a substrate with a film of a two-package heat-curable, urethane-forming coating composition which comprises: applying said coating composition to said substrate, said coating composition comprising: a first package of a hydroxyl-bearing polymer having ethylenic unsaturation and having a molecular weight not substantially greater than about 3,000, said polymer being dispersed in fugitive organic solvent; and a second package of a multi-isocyanate compound having a multiplicity of isocyanate groups and being dispersed in fugitive organic solvent, the total proportion of said fugitive solvents being not substantially greater than about 30% by volume of said coating composition; and heating said coated substrate to cure said film of said coating composition by in situ formation of urethane linkages by the hydroxyl-isocyanate reaction in combination with in situ free-radical addition polymerization through said ethylenic unsaturation of said polymer.
Claim 13
Dependent Claim
138 words
A process for coating a substrate with a film of a two-package heat-curable, urethane-forming coating composition which comprises: applying said coating composition to said substrate, said coating composition comprising: a first package of a hydroxyl-bearing polymer having ethylenic unsaturation and having a molecular weight not substantially greater than about 3,000, said polymer being dispersed in fugitive organic solvent; and a second package of a multi-isocyanate compound having a multiplicity of isocyanate groups and being dispersed in fugitive organic solvent, the total proportion of said fugitive solvents being not substantially greater than about 30% by volume of said coating composition; and heating said coated substrate to cure said film of said coating composition by in situ formation of urethane linkages by the hydroxyl-isocyanate reaction in combination with in situ free-radical addition polymerization through said ethylenic unsaturation of said polymer.
Claim 14
Dependent Claim
31 words
The process of claim 1 wherein the total proportion of said fugitive solvent is sufficient so that the viscosity of said coating composition is not substantially greater than about 500 centipoises.
Claim 15
Dependent Claim
26 words
The process of claim 11 wherein said coated substrate is heated at a temperature of not substantially greater than about 400° F. to cure said coating.
Claim 16
Dependent Claim
50 words
The process of claim 11 wherein a portion of said fugitive solvent of said package one is replaced with an ethylenically unsaturated diluent reactive with said ethylenic unsaturation of said polymer and at least a portion of said diluent cures into said film of said coating composition by said heating.
Claim 17
Dependent Claim
51 words
The process of claim 11 wherein a portion of said fugitive solvent of said package two is replaced with a non-hydroxyl-bearing ethylenically unsaturated diluent reactive with said ethylenic unsaturation of said polymer and at least a portion of said diluent cures into said film of said coating composition by said heating.
References Cited (Backward Citations)
US3367992A
Cited
US3502500A
Cited
US3878036A
Cited
US3855379A
Cited
US3824201A
Cited
US3837892A
Cited
US3856757A
Cited
US3966681A
Cited
US3886111A
Cited
US3991024A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-19 | 1981-06-20 | 1981-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-19 | 1985-06-20 | 1985-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-19 | 1989-06-20 | 1989-12-20 | $7700.00 | Window Closed / Lapsed |