Catalyst for the purification of the exhaust gases of internal combustion engines
Assignee: Francaise Oxycatalyse SA
•
Filing: 1975-12-12
•
Granted: 1977-12-20
•
Expires: 1995-12-12
Abstract
Abstract New catalysts are described which are useful over a wide temperature range for purifying exhaust gases from internal combustion engines burning gasoline. The new catalysts are of composite form comprising a water-gas type catalyst and at least one platinum group metal such as platinum, palladium or ruthenium. As water-gas catalyst, use can be made of a mixture or iron oxide and chromium oxide. By using such composite catalysts on a common refractory substrate, nitrogen oxides, carbon monoxide and unburnt hydrocarbons can be removed to a substantial degree in a single stage.
Inventors
- 👤 Jean Louis Emile Pomot
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 02:30
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/945; B01J; B01J23/00; B01J23/70; B01J23/89; B01J23/8933; B01J23/8993; B01J37/00; B01J37/02; B01J37/024; F; F02; F02B; F02B1/00; F02B1/02; F02B1/04; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
139 words
A pollution removing catalytic complex for exhaust gases of gasoline-operated internal-combustion engines and like gases containing unburnt hydrocarbons, oxygen, carbon monoxide, at least one oxide of nitrogen and water vapor, said catalytic complex comprising an intimate admixture on a porous substrate designed to be fitted in the path of said exhaust gases, said intimate admixture consisting essentially of: a. a first catalyst component suitable for liberating hydrogen through the reaction of carbon monoxide and water, said first catalyst component consisting essentially of a mixture of iron oxide and a chromium oxide; and b. a second catalyst component capable of catalyzing the reaction of the thus-liberated hydrogen with oxides of nitrogen, said second catalyst component being carried on the surface of said first catalyst component and consisting essentially of ruthenium and at least one of the metals platinum and palladium.
Claim 2
Dependent Claim
139 words
A pollution removing catalytic complex for exhaust gases of gasoline-operated internal-combustion engines and like gases containing unburnt hydrocarbons, oxygen, carbon monoxide, at least one oxide of nitrogen and water vapor, said catalytic complex comprising an intimate admixture on a porous substrate designed to be fitted in the path of said exhaust gases, said intimate admixture consisting essentially of: a. a first catalyst component suitable for liberating hydrogen through the reaction of carbon monoxide and water, said first catalyst component consisting essentially of a mixture of iron oxide and a chromium oxide; and b. a second catalyst component capable of catalyzing the reaction of the thus-liberated hydrogen with oxides of nitrogen, said second catalyst component being carried on the surface of said first catalyst component and consisting essentially of ruthenium and at least one of the metals platinum and palladium.
Claim 3
Dependent Claim
36 words
A catalyst according to claim 1, wherein the catalyst component (b) is present in a proportion between 0.05 and 0.15% with respect to the sum of the weight of the porous substrate and catalyst component (a).
Claim 4
Dependent Claim
40 words
A catalyst according to claim 1, wherein the catalyst component (b) is ruthenium which is present in a proportion between 0.01 and 0.05% with respect of the sum of the weight of the porous substrate and the catalyst component (a).
Claim 5
Dependent Claim
60 words
A catalyst according to claim 1, wherein said substrate comprises at least one monolithic block of alumina having a plurality of channels with a diameter of a few millimetres, said block having a porosity between 35 and 45%, an expanded surface of between 0.8 and 1 m 2 /g and a specific surface between 40 and 90 m 2 /g.
Claim 6
Dependent Claim
31 words
A catalyst according to claim 1 wherein the iron oxide and chromium oxide together are present in a proportion of 5 - 15% based on the weight of the porous substrate.
Claim 7
Dependent Claim
13 words
A catalyst of claim 1 wherein said porous substrate is chemically inert alumina.
Claim 8
Dependent Claim
15 words
A catalyst of claim 1, wherein said first component contains 80 to 95% iron oxide.
Claim 9
Dependent Claim
15 words
A catalyst of claim 1, wherein said first component contains 86 to 90% iron oxide.
Claim 10
Dependent Claim
29 words
A catalytic complex of claim 6, wherein said porous alumina substrate presents a porosity between 30 and 70% and a specific surface between 200 and 300 m 2 /g.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-19 | 1981-06-20 | 1981-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-19 | 1985-06-20 | 1985-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-19 | 1989-06-20 | 1989-12-20 | $7700.00 | Window Closed / Lapsed |