Process for agglomerating expanded perlite fines
Assignee: General Refractories Co
•
Filing: 1976-06-28
•
Granted: 1977-12-20
•
Expires: 1996-06-28
Abstract
Abstract Expanded lightly milled perlite fines are mixed with aqueous alkali metal silicates and the wet mixture is dried at temperatures of from 600° F up to 1400° F in a moving air stream to form agglomerates which are useful as filteraids. The agglomerates may be heat treated in an indirect fired rotary kiln to further reduce the water solubility, and may be separated into size factions either before or after the heat treatment.
Inventors
- 👤 John B. Gilmour
- 👤 Praful K. A. Mehta
- 👤 Melvin J. Mirliss
- 👤 Richard B. Nielsen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:51
CPC Classifications
B; B01; B01J; B01J20/00; B01J20/02; B01J20/10; B01J20/103; B01J20/106; B01D; B01D37/00; B01D37/02; B01D39/00; B01D39/14; B01D39/20; B01D39/2068; B01D39/2072; B01D39/2075; C; C04; C04B; C04B18/00; C04B18/02; C04B18/027; Y; Y10; Y10S; Y10S106/00; Y10S106/02
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
106 words
A process for producing an improved perlite filter aid which comprises mixing finely divided expanded perlite particles with an aqueous solution of alkali metal silicate to form a composition having perlite: alkali metal silicate: water in the ratio of about 100:1:5 to about 100:10:100, removing the free moisture and drying the mixture by suspending said composition in a moving gas stream at a temperature of from about 600° F to less than about 1400° F, whereby the perlite particles form dry agglomerates, and heat treating said dry agglomerates by indirect firing at about 1100° to about 1300° F to increase the water insolubility of the agglomerates.
Claim 2
Dependent Claim
106 words
A process for producing an improved perlite filter aid which comprises mixing finely divided expanded perlite particles with an aqueous solution of alkali metal silicate to form a composition having perlite: alkali metal silicate: water in the ratio of about 100:1:5 to about 100:10:100, removing the free moisture and drying the mixture by suspending said composition in a moving gas stream at a temperature of from about 600° F to less than about 1400° F, whereby the perlite particles form dry agglomerates, and heat treating said dry agglomerates by indirect firing at about 1100° to about 1300° F to increase the water insolubility of the agglomerates.
Claim 3
Dependent Claim
20 words
The process of claim 1 wherein the ratio of perlite: alkali metal silicate: water ranges from about 100:2:15 to 100:8:50.
Claim 4
Dependent Claim
32 words
The process of claim 2 wherein the finely divided perlite particles are mixed with the alkali metal silicate to form a composition having the perlite: alkali metal silicate: water ratio of 100:5:35.
Claim 5
Dependent Claim
19 words
The process of claim 1 which comprises the further step of classifying the heat treated agglomerates by air separation.
Claim 6
Dependent Claim
32 words
The process of claim 1 wherein the finely divided perlite particles are mixed with the alkali metal silicate to form a composition having the perlite: alkali metal silicate: water ratio of 100:2:35.
Claim 7
Dependent Claim
32 words
The process of claim 4 wherein the finely divided perlite particles are mixed with the alkali metal silicate to form a composition having the perlite: alkali metal silicate: water ratio of 100:2:35.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-19 | 1981-06-20 | 1981-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-19 | 1985-06-20 | 1985-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-19 | 1989-06-20 | 1989-12-20 | $7700.00 | Window Closed / Lapsed |