Metal flake product suited for the production of metal powder for powder metallurgical purposes, and a process for manufacturing the product
Assignee: SKF Nova AB
•
Filing: 1976-05-17
•
Granted: 1977-12-20
•
Expires: 1996-05-17
Abstract
Abstract A steel flake product, suitable for being crushed or ground to form a steel powder for powder metallurgical purposes, consists of a plurality of relatively thin, brittle and easily crushed, substantially dendrite-free steel flakes of amorphous to compact-grained structure. Such steel flakes are produced by causing molten steel to form at least one discrete, relatively thin flake-shaped layer on a relatively cold metal surface of great cooling capacity, moving rapidly and substantially across the direction of delivery of the molten steel. Due to the great cooling capacity the layer is made to solidify extremely rapidly.
Inventors
- 👤 Bengt G. S. Lundgren
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 21:54
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/002; B22F9/008; B22F1/00; B22F1/06; B22F1/068; B22F1/08; B22F9/02; B22F9/06; B22F9/08; B22F9/10; C; C22; C22C; C22C45/00; B22F2998/00; Y; Y10; Y10S; Y10S75/00; Y10S75/954; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
38 words
A steel flake product suited for the production of steel powder for powder metallugical purposes, characterized in that it consists of a plurality of thin, brittle and easily crushed, substantially dendrite-free steel flakes of amorphous to compact-grained structure.
Claim 2
Dependent Claim
38 words
A steel flake product suited for the production of steel powder for powder metallugical purposes, characterized in that it consists of a plurality of thin, brittle and easily crushed, substantially dendrite-free steel flakes of amorphous to compact-grained structure.
Claim 3
Dependent Claim
19 words
A steel flake product according to claim 1, in which the flakes have a hardness of at least HRC=60.
Claim 4
Dependent Claim
19 words
A steel flake product according to claim 1, in which the flakes' thickness is at most about 0.5 mm.
Claim 5
Dependent Claim
17 words
A steel flake product according to claim 3, in which the flakes' thickness is about 0.1 mm.
Claim 6
Dependent Claim
49 words
A steel flake product according to claim 3, in which the ratio of the flakes' length to thickness is at least 100, the ratio of the flakes' width to thickness is at least about 20, and the ratio of the flakes' length to width is at most about 5.
Claim 7
Dependent Claim
134 words
A process for manufacturing a steel flake product suited for the production of steel powder for powder metallurgical purposes, which comprises causing molten steel, which is of such a composition that rapid cooling of thin layers of the melt produces brittle crushable films, to impinge, in a vacuum or protective gas, upon a cold metal surface of great cooling capacity maintained at a temperature at least 200° C. lower than the solidification temperature of the molten steel and moving rapidly and substantially across the direction of delivery of the molten steel, to form a discrete, thin flake-shaped layer of molten steel on the metal surface, thereby causing the thin layer to solidify rapidly on the cold metal surface to form thin, brittle and easily crushed substantially dendrite-free steel flakes of amorphous to compact-grained structure.
Claim 8
Dependent Claim
134 words
A process for manufacturing a steel flake product suited for the production of steel powder for powder metallurgical purposes, which comprises causing molten steel, which is of such a composition that rapid cooling of thin layers of the melt produces brittle crushable films, to impinge, in a vacuum or protective gas, upon a cold metal surface of great cooling capacity maintained at a temperature at least 200° C. lower than the solidification temperature of the molten steel and moving rapidly and substantially across the direction of delivery of the molten steel, to form a discrete, thin flake-shaped layer of molten steel on the metal surface, thereby causing the thin layer to solidify rapidly on the cold metal surface to form thin, brittle and easily crushed substantially dendrite-free steel flakes of amorphous to compact-grained structure.
Claim 9
Dependent Claim
25 words
A process according to claim 6, in which the cooling rate is at least about 10 4 ° C/s in the temperature range of solidification.
Claim 10
Dependent Claim
19 words
A process according to claim 7, in which the cooling rate is at least about 10 6 ° C/s.
Claim 11
Dependent Claim
19 words
A process according to claim 6, wherein the flakes produced have a thickness of at most about 0.5 mm.
Claim 12
Dependent Claim
17 words
A process according to claim 9, wherein the flakes produced have a thickness of about 0.1 mm.
Claim 13
Dependent Claim
46 words
A process according to claim 9, wherein the ratio of the flakes' length to thickness is at least 100, the ratio of the flakes' width to thickness is at least about 20, and the ratio of the flakes' length to width is at most about 5.
Claim 14
Dependent Claim
18 words
A process according to claim 6, in which the flakes produced have a hardness of at least HRC=60.
References Cited (Backward Citations)
US3151971A
Cited
DE2127563A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-19 | 1981-06-20 | 1981-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-19 | 1985-06-20 | 1985-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-19 | 1989-06-20 | 1989-12-20 | $7700.00 | Window Closed / Lapsed |