Process for manufacturing ceramic cutting tool materials
Assignee: Nippon Tungsten Co Ltd
•
Filing: 1976-01-21
•
Granted: 1977-12-20
•
Expires: 1996-01-21
Abstract
Abstract Sintering of a mixture of alumina and titanium carbide has been difficult heretofore, but by the intermediary action of titanium oxides, sintering of a powder mixture consisting of alumina and titanium carbide by hot-pressing at a comparatively lower temperature than that used in conventional processes becomes possible. Various procedures in which the above principle is applied, the powder mixture to be used therein and the materials produced thereby which are to be used for manuacturing cutting tools are disclosed.
Inventors
- 👤 Kazuki Ogawa
- 👤 Michito Miyahara
- 👤 Mitsuhiko Furukawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:53
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/645; C04B35/01; C04B35/10; C04B35/111; C04B35/515; C04B35/56; C04B35/5607; C04B35/5611; C04B35/65
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
95 words
A process for manufacturing ceramic cutting tool materials which comprises mixing and thoroughly blending titanium carbide powder, titania powder and alumina powder to form a powder mixture consisting of 19-70% titanium carbide by weight, 1-10% titania by weight and the remainder alumina and having greatly improved sinterability and hot-pressing the thus prepared mixture at a temperature of 1500°-1700° C to form a sintered body of the mixture having a fine, dense structure as well as high mechanical strength due to the intermedial action of titanium oxide which enhances the binding between alumina and titanium carbide.
Claim 2
Dependent Claim
95 words
A process for manufacturing ceramic cutting tool materials which comprises mixing and thoroughly blending titanium carbide powder, titania powder and alumina powder to form a powder mixture consisting of 19-70% titanium carbide by weight, 1-10% titania by weight and the remainder alumina and having greatly improved sinterability and hot-pressing the thus prepared mixture at a temperature of 1500°-1700° C to form a sintered body of the mixture having a fine, dense structure as well as high mechanical strength due to the intermedial action of titanium oxide which enhances the binding between alumina and titanium carbide.
Claim 3
Dependent Claim
73 words
A process for manufacturing the ceramic cutting tool materials according to claim 1 wherein said titanium carbide is at least a member selected from the group consisting of powdered titanium carbide, powdered titanium carbide of which the exterior surface of the particles is at least partially oxidized to form titanium oxide thereon, and powdered titania of which the exterior surface of the particles is at least partially carburized to form titanium carbide thereon.
Claim 4
Dependent Claim
71 words
A process for manufacturing the ceramic cutting tool materials according to claim 1 wherein said titania is at least a member selected from the group consisting of powdered titania, powdered titania of which the exterior surface of the particles is at least partially carburized to form titanium carbide thereon and powdered titanium carbide of which the exterior surface of the particles is at least partially oxidized to form titanium oxide thereon.
Claim 5
Dependent Claim
49 words
A process for manufacturing the ceramic cutting tool materials according to claim 1 wherein said powdered alumina and said powdered titania are preliminarly mixed, and the thus formed mixture is preliminarily roasted, to which said powdered titanium carbide is added, mixed and thoroughly blended to form said powder mixture.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-19 | 1981-06-20 | 1981-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-19 | 1985-06-20 | 1985-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-19 | 1989-06-20 | 1989-12-20 | $7700.00 | Window Closed / Lapsed |