Polymeric shaped articles
Assignee: Imperial Chemical Industries Ltd
•
Filing: 1976-01-09
•
Granted: 1977-12-13
•
Expires: 1996-01-09
Abstract
Abstract A shaped polymeric article of a gel-polymerisate of a homogeneous mixture comprising A. FROM 5% TO 95% BY WEIGHT OF POLYURETHANE PRECURSORS COMPRISING AT LEAST ONE POLYFUNCTIONAL COMPOUND AND AT LEAST ONE POLYISOCYANATE OF THE STRUCTURE <IMAGE> I where X is a divalent radical, preferably -CH2-, said precursors being capable of forming a cross-linked polyurethane having a glass-rubber transition temperature of at least 25 DEG C, preferably at least 35 DEG C, and B. FROM 95% TO 5% BY WEIGHT OF CURED POLYESTER RESIN PRECURSORS, COMPRISING I. AT LEAST ONE ETHYLENICALLY UNSATURATED POLYESTER, AND II. AT LEAST ONE VINYL MONOMER.
Inventors
- 👤 Francis Gowland Hutchinson
- 👤 Richard George Cleveland Henbest
- 👤 Margaret Kenley Leggett
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 04:22
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/67; C08G18/68; C08G18/40; C08G18/4009; C08L; C08L75/00; C08L75/04
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
235 words
A tractable shaped article capable of being further shaped and cured into an intractable shaped article, said tractable shaped article consisting essentially of a homogeneously prepared mixture which has been polymerized to a degree that a tractable partially polymerized article is obtained, said homogeneously prepared mixture consisting essentially of: a. from 5% to 95% by weight of polyurethane precursors free of ethylenic unsaturation comprising 1. at least one polyol or hydroxy-terminated polyester containing hydroxy groups reactive with isocyanate groups wherein the hydroxy groups of said polyol or polyester polyurethane precursors are the only polyurethane precursor substituents reactive with isocyanate groups, and 1. at least one polyisocyanate of the structure ##STR3## wherein X is a divalent radical containing at most three atoms in the chain between the phenyl groups in said structure, or a mixture comprising at least 40% by weight of the total polyisocyanate of at least one other polyisocyanate, said polyurethane precursors being capable of forming if cured alone in the absence of precursors of cured polyester resin a cross-linked polyurethane having a glass-rubber transition temperature of at least 25° C, as measured with a DuPont 900 thermal analyzer, the rate of heating the sample being 20° C per minute, at least one of said polyol, hydroxy-terminated polyester or other polyisocyanate being tri-functional or of higher functionality; and b. from 95% to 5% by weight of precursors of cured polyester resin consisting essentially of
Claim 2
Dependent Claim
235 words
A tractable shaped article capable of being further shaped and cured into an intractable shaped article, said tractable shaped article consisting essentially of a homogeneously prepared mixture which has been polymerized to a degree that a tractable partially polymerized article is obtained, said homogeneously prepared mixture consisting essentially of: a. from 5% to 95% by weight of polyurethane precursors free of ethylenic unsaturation comprising 1. at least one polyol or hydroxy-terminated polyester containing hydroxy groups reactive with isocyanate groups wherein the hydroxy groups of said polyol or polyester polyurethane precursors are the only polyurethane precursor substituents reactive with isocyanate groups, and 1. at least one polyisocyanate of the structure ##STR3## wherein X is a divalent radical containing at most three atoms in the chain between the phenyl groups in said structure, or a mixture comprising at least 40% by weight of the total polyisocyanate of at least one other polyisocyanate, said polyurethane precursors being capable of forming if cured alone in the absence of precursors of cured polyester resin a cross-linked polyurethane having a glass-rubber transition temperature of at least 25° C, as measured with a DuPont 900 thermal analyzer, the rate of heating the sample being 20° C per minute, at least one of said polyol, hydroxy-terminated polyester or other polyisocyanate being tri-functional or of higher functionality; and b. from 95% to 5% by weight of precursors of cured polyester resin consisting essentially of
Claim 3
Dependent Claim
87 words
at least one ethylenically unsaturated polyester containing in each molecule at least two hydroxy or carboxylic acid groups reactive with isocyanate groups, and 4. at least one vinyl monomer containing at least one ethylenically unsaturated group which will react with ethylenically unsaturated groups in the polyester, said precursors of cured polyester resin comprising from 40-90% by weight of (3) and from 60-10% by weight of (4) and said vinyl monomer being selected from the group consisting of styrene, methyl methacrylate, divinyl benzene, diallyl phthalate and vinyl toluene.
Claim 4
Dependent Claim
87 words
at least one ethylenically unsaturated polyester containing in each molecule at least two hydroxy or carboxylic acid groups reactive with isocyanate groups, and 4. at least one vinyl monomer containing at least one ethylenically unsaturated group which will react with ethylenically unsaturated groups in the polyester, said precursors of cured polyester resin comprising from 40-90% by weight of (3) and from 60-10% by weight of (4) and said vinyl monomer being selected from the group consisting of styrene, methyl methacrylate, divinyl benzene, diallyl phthalate and vinyl toluene.
Claim 5
Dependent Claim
233 words
A process for preparing a tractable shaped article of simple profile capable of being further shaped and cured into an intractable shaped article, said process comprising the steps of: A. preparing a homogeneous mixture consisting essentially of a. from 5% to 95% by weight of polyurethane precursors free of ethylenic unsaturation comprising 1. at least one polyol or hydroxy-terminated polyester containing hydroxy groups reactive with isocyanate groups wherein the hydroxy groups of said polyol or polyester polyurethane precursors are the only polyurethane precursor substituents reactive with isocyanate groups, and 2. at least one polyisocyanate of the structure ##STR4## wherein X is a divalent radical containing at most three atoms in the chain between the phenyl groups in said structure, or a mixture comprising at least 40% by weight of the total polyisocyanate of at least one polyisocyanate having the structure I with at least one other polyisocyanate, said polyurethane precursors being capable of forming if cured alone in the absence of precursors of cured polyester resin a cross-linked polyurethane having a glass-rubber transition temperature of at least 25° C, as measured with a DuPont 900 thermal analyzer, the rate of heating the sample being 20° C per minute, at least one of said polyol, hydroxy-terminated polyester or other polyisocyanate being tri-functional or of higher functionality; and b. from 95% to 5% by weight of precursors of cured polyester resin consisting essentially of 3.
Claim 6
Dependent Claim
233 words
A process for preparing a tractable shaped article of simple profile capable of being further shaped and cured into an intractable shaped article, said process comprising the steps of: A. preparing a homogeneous mixture consisting essentially of a. from 5% to 95% by weight of polyurethane precursors free of ethylenic unsaturation comprising 1. at least one polyol or hydroxy-terminated polyester containing hydroxy groups reactive with isocyanate groups wherein the hydroxy groups of said polyol or polyester polyurethane precursors are the only polyurethane precursor substituents reactive with isocyanate groups, and 2. at least one polyisocyanate of the structure ##STR4## wherein X is a divalent radical containing at most three atoms in the chain between the phenyl groups in said structure, or a mixture comprising at least 40% by weight of the total polyisocyanate of at least one polyisocyanate having the structure I with at least one other polyisocyanate, said polyurethane precursors being capable of forming if cured alone in the absence of precursors of cured polyester resin a cross-linked polyurethane having a glass-rubber transition temperature of at least 25° C, as measured with a DuPont 900 thermal analyzer, the rate of heating the sample being 20° C per minute, at least one of said polyol, hydroxy-terminated polyester or other polyisocyanate being tri-functional or of higher functionality; and b. from 95% to 5% by weight of precursors of cured polyester resin consisting essentially of 3.
Claim 7
Dependent Claim
101 words
at least one ethylenically unsaturated polyester containing in each molecule at least two hydroxy or carboxylic acid groups reactive with isocyanate groups, and 4. at least one vinyl monomer containing at least one ethylenically unsaturated group which will react with ethylenically unsaturated groups in the polyester, said precursors of cured polyester resins comprising from 40-90% by weight of (3) and from 60-10% by weight of (4) and said vinyl monomer being selected from the group consisting of styrene, methyl methacrylate, divinyl benzene, diallyl phthalate and vinyl toluene; B. polymerizing said mixture in a mould to a degree such that a tractable
Claim 8
Dependent Claim
101 words
at least one ethylenically unsaturated polyester containing in each molecule at least two hydroxy or carboxylic acid groups reactive with isocyanate groups, and 4. at least one vinyl monomer containing at least one ethylenically unsaturated group which will react with ethylenically unsaturated groups in the polyester, said precursors of cured polyester resins comprising from 40-90% by weight of (3) and from 60-10% by weight of (4) and said vinyl monomer being selected from the group consisting of styrene, methyl methacrylate, divinyl benzene, diallyl phthalate and vinyl toluene; B. polymerizing said mixture in a mould to a degree such that a tractable
Claim 9
Dependent Claim
236 words
partially polymerized article is obtained. 3. A process for preparing a tractable shaped article capable of being further shaped and cured into an intractable shaped article, said process comprising the steps of: A. preparing a homogeneous mixture consisting essentially of a. from 5% to 95% by weight of polyurethane precursors free of ethylenic unsaturation comprising 1. at least one polyol or hydroxy-terminated polyester containing hydroxy groups reactive with isocyanate groups wherein the hydroxy groups of said polyol or polyester polyurethane precursors are the only polyurethane precursor substituents reactive with isocyanate groups, and 2. at least one polyisocyanate compound of the structure ##STR5## wherein X is a divalent radical containing at most three atoms in the chain between the phenyl groups in said structure, or a mixture comprising at least 40% by weight of the total polyisocyanate of at least one polyisocyanate having the structure I with at least one other polyisocyanate, said polyurethane precursors being capable of forming if cured alone in the absence of precursors of cured polyester resin a cross-linked polyurethane having a glass-rubber transition temperature of at least 25° C, as measured with a DuPont 900 thermal analyzer, the rate of heating the sample being 20° C per minute, at least one of said polyol, hydroxy-terminated polyester or other polyisocyanate being tri-functional or of higher functionality; and b. from 95% to 5% by weight of precursors of cured polyester resin consisting essentially of
Claim 10
Dependent Claim
236 words
partially polymerized article is obtained. 3. A process for preparing a tractable shaped article capable of being further shaped and cured into an intractable shaped article, said process comprising the steps of: A. preparing a homogeneous mixture consisting essentially of a. from 5% to 95% by weight of polyurethane precursors free of ethylenic unsaturation comprising 1. at least one polyol or hydroxy-terminated polyester containing hydroxy groups reactive with isocyanate groups wherein the hydroxy groups of said polyol or polyester polyurethane precursors are the only polyurethane precursor substituents reactive with isocyanate groups, and 2. at least one polyisocyanate compound of the structure ##STR5## wherein X is a divalent radical containing at most three atoms in the chain between the phenyl groups in said structure, or a mixture comprising at least 40% by weight of the total polyisocyanate of at least one polyisocyanate having the structure I with at least one other polyisocyanate, said polyurethane precursors being capable of forming if cured alone in the absence of precursors of cured polyester resin a cross-linked polyurethane having a glass-rubber transition temperature of at least 25° C, as measured with a DuPont 900 thermal analyzer, the rate of heating the sample being 20° C per minute, at least one of said polyol, hydroxy-terminated polyester or other polyisocyanate being tri-functional or of higher functionality; and b. from 95% to 5% by weight of precursors of cured polyester resin consisting essentially of
Claim 11
Dependent Claim
110 words
at least one ethylenically unsaturated polyester containing in each molecule at least two hydroxy or carboxylic acid groups reactive with isocyanate groups, and 4. at least one vinyl monomer containing at least one ethylenically unsaturated group which will react with ethylenically unsaturated groups in the polyester, said precursors of cured polyester comprising from 40-90% by weight of (3) and from 60-10% by weight of (4) and said vinyl monomer being selected from the group consisting of styrene, methyl methacrylate, divinyl benzene, diallyl phthalate and vinyl toluene; B. shaping said mixture and reacting said polyurethane precursors without substantial reaction between said polyester and vinyl monomer to obtain said shaped tractable article.
Claim 12
Dependent Claim
110 words
at least one ethylenically unsaturated polyester containing in each molecule at least two hydroxy or carboxylic acid groups reactive with isocyanate groups, and 4. at least one vinyl monomer containing at least one ethylenically unsaturated group which will react with ethylenically unsaturated groups in the polyester, said precursors of cured polyester comprising from 40-90% by weight of (3) and from 60-10% by weight of (4) and said vinyl monomer being selected from the group consisting of styrene, methyl methacrylate, divinyl benzene, diallyl phthalate and vinyl toluene; B. shaping said mixture and reacting said polyurethane precursors without substantial reaction between said polyester and vinyl monomer to obtain said shaped tractable article.
Claim 13
Dependent Claim
31 words
A tractable shaped article as claimed in claim 1 in which the polyurethane precursors are capable of forming a cross-linked polyurethane having a glass-rubber transition temperature of at least 35° C.
Claim 14
Dependent Claim
35 words
A tractable shaped article as claimed in claim 1 which is a gel-polymerisate of from 40 to 60% by weight of polyurethane precursors and from 60 to 40% by weight of cured polyester resin precursors.
Claim 15
Dependent Claim
33 words
A tractable shaped article as claimed in claim 1 which is a gel-polymerisate of 50% by weight or greater of polyurethane precursors and 50% by weight or less of precursors cured polyester resin.
Claim 16
Dependent Claim
35 words
A tractable shaped article as claimed in claim 1 which is a gel-polymerisate of from 50 to 80% by weight of polyurethane precursors and from 50 to 20% by weight of cured polyester resin precursors.
Claim 17
Dependent Claim
41 words
A tractable shaped article as claimed in claim 1 in which the molar proportion of groups reactive with isocyanate groups in the polyfunctional compound plus ethylenically unsaturated polyester, to isocyanate groups in the polyisocyanate is in the range 0.8:1 to 1.1:1.
Claim 18
Dependent Claim
21 words
A tractable shaped article as claimed in claim 8 in which the molar proportion is in the range 0.9:1 to 1:1.
Claim 19
Dependent Claim
44 words
A tractable shaped article as claimed in claim 1 in which the precursors of cured polyester resin comprise from 50 to 70% by weight of at least one ethylenically unsaturated polyester and from 50 to 30% by weight of at least one vinyl monomer.
Claim 20
Dependent Claim
32 words
A tractable shaped article as claimed in claim 1 in which the polyisocyanate is a compound having the structure ##STR6## where n is a whole number in the range 1 to 3.
Claim 21
Dependent Claim
16 words
A tractable shaped article as claimed in claim 11 in which the polyisocyanate is 4:4'-diphenylmethane diisocyanate.
Claim 22
Dependent Claim
21 words
A tractable shaped article as claimed in claim 12 in which the polyisocyanate is 4:4'-diphenylmethane diisocyanate in admixture with other polyisocyanates.
Claim 23
Dependent Claim
16 words
A tractable shaped article as claimed in claim 1 in which the polyisocyanate is 4:4'-diphenylether diisocyanate.
Claim 24
Dependent Claim
18 words
A tractable shaped article as claimed in claim 1 in which the component (a) (1) is a polyol.
Claim 25
Dependent Claim
26 words
A tractable shaped article as claimed in claim 15 in which the polyol is selected from the group consisting of oxypropylated trimethylol propane and oxypropylated glycerol.
Claim 26
Dependent Claim
18 words
A tractable shaped article as claimed in claim 1 in which the component (a) (1) is a polyester.
Claim 27
Dependent Claim
50 words
A tractable shaped article as claimed in claim 17 in which the polyester is selected from the group consisting of a condensate of adipic acid with glycerol and either ethylene glycol or propylene glycol, and a condensate of adipic acid with trimethylol propane and either diethylene glycol or propylene glycol.
Claim 28
Dependent Claim
73 words
A tractable shaped article as claimed in claim 1 in which the ethylenically unsaturated polyester is selected from the group consisting of a condensate of isophthalic acid and fumaric acid with propylene glycol, a condensate of phthalic acid or anhydride and fumaric acid with propylene glycol, cyclohexane-1:4-diol or neopentyl glycol, and a condensate of propylene glycol with either fumaric acid or a mixture of phthalic acid or anhydride and maleic acid or anhydride.
Claim 29
Dependent Claim
13 words
A tractable shaped article as claimed in claim 1 which contains fibre reinforcement.
Claim 30
Dependent Claim
35 words
A tractable shaped article as claimed in claim 20 in which the fibre reinforcement is present in a proportion of 5% to 50% by weight of the total weight of the fibre reinforced shaped article.
Claim 31
Dependent Claim
35 words
A tractable shaped article as claimed in claim 21 in which the fibre reinforcement is present in a proportion of 20% to 50% by weight of the total weight of the fibre reinforced shaped article.
Claim 32
Dependent Claim
28 words
A tractable shaped article as claimed in claim 20 in which the reinforcement is selected from the group consisting of glass fibre, carbon fibre and poly(ethylene terephthalate) fibre.
Claim 33
Dependent Claim
25 words
A process as claimed in claim 2 in which the component (a) (1) in the polyurethane precursors has a molecular weight of 1000 or less.
Claim 34
Dependent Claim
21 words
A process as claimed in claim 24 in which the component (a) (1) has a molecular weight of 650 or less.
Claim 35
Dependent Claim
43 words
A process as claimed in claim 2 in which substantially the whole of the polymerisation is effected at a temperature which is above the heat distortion temperature as measured by the test method described in ASTM D648/56 (66 lbs/sq.in) of the resultant gel-polymerisate.
Claim 36
Dependent Claim
24 words
A process as claimed in claim 2 in which the mixture is shaped by casting the mixture into a mould or by compression moulding.
Claim 37
Dependent Claim
69 words
A process for the production of a polymeric article of complex profile which comprises the steps of a. performing a further shaping operation on a tractable shaped article of simple profile formed by partially gel-polymerising a homogeneous mixture of polyurethane precursors and cured polyester resin precursors as described in claim 1, and b. causing or allowing the thus further shaped article to retain its shape while completing the gel-polymerisation.
Claim 38
Dependent Claim
62 words
A process for the production of an intractable polymeric article of complex profile which comprises the steps of a. performing a further shaping operation on a tractable shaped article as produced according to claim 2, and b. causing or allowing the thus further shaped article to retain its shape while substantially fully reacting the vinyl monomer to form an intractable shaped article.
Claim 39
Dependent Claim
25 words
The process of claim 29 comprising raising the temperature of said further shaped article sufficient to activate the reaction of said polyester and vinyl monomer.
Claim 40
Dependent Claim
28 words
An intractable shaped article of complex profile which comprises the shaped article of claim 1 which has been further shaped and cured to form an intractable shaped article.
Claim 41
Dependent Claim
32 words
A tractable shaped article, as claimed in claim 1, wherein precursors of the cross-linked polyurethane are substantially fully reacted before any substantial reaction has taken place between the polyester and vinyl monomer.
Claim 42
Dependent Claim
20 words
A tractable shaped article, as claimed in claim 13, wherein said other polyisocyanates have a total functionality greater than 2.
Claim 43
Dependent Claim
25 words
A tractable shaped article, as claimed in claim 33, wherein said mixture of diisocyanate and other polyisocyanates have a total isocyanate functionality of approximately 2.7.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-12 | 1981-06-13 | 1981-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-12 | 1985-06-13 | 1985-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-12 | 1989-06-13 | 1989-12-13 | $7700.00 | Window Closed / Lapsed |