US4062806A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Catalytic coating composition
Assignee: EIDP Inc
•
Filing: 1976-06-21
•
Granted: 1977-12-13
•
Expires: 1996-06-21
Abstract
Abstract A composition for applying an easily removable coating of oxidative catalyst to solid substrates comprising finely divided catalytic oxidation metal solids dispersed in an aqueous solution of alkaline silicate in which is dissolved a vicinal alkane polyol. The composition contains 10-40 pbw alkaline silicate per 100 pbw of catalytic oxidation metal and other water insoluble solids and 40-125 pbw polyol per 100 pbw of alkaline silicate.
Inventors
- 👤 William Owen Roberts
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:28
CPC Classifications
C; C03; C03C; C03C8/00; B; B01; B01J; B01J37/00; B01J37/02; B01J37/0215; B01J37/0219; C03C2205/00; C03C2205/04
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
77 words
A composition for applying an oxidation catalyst coating to the surface of a solid substrate comprising (a) finely divided catalytic metal oxides dispersed in (b) an aqueous solution of alkaline silicate in which is dissolved (c) a vicinal alkane polyol, the amount of alkaline silicate corresponding to 10-40 pbw per 100 of any waterinsoluble solids in the composition and the amount of polyol corresponding to 40-125 pbw per 100 pbw alkaline silicate, dry basis, in the composition.
Claim 2
Dependent Claim
77 words
A composition for applying an oxidation catalyst coating to the surface of a solid substrate comprising (a) finely divided catalytic metal oxides dispersed in (b) an aqueous solution of alkaline silicate in which is dissolved (c) a vicinal alkane polyol, the amount of alkaline silicate corresponding to 10-40 pbw per 100 of any waterinsoluble solids in the composition and the amount of polyol corresponding to 40-125 pbw per 100 pbw alkaline silicate, dry basis, in the composition.
Claim 3
Dependent Claim
28 words
The composition of claim 1 in which the vicinal alkane polyol corresponds to the structural formula ##STR2## in which n is an integer of from 0 to 4.
Claim 4
Dependent Claim
13 words
The composition of claim 2 in which the vicinal alkane polyol is 1,2-ethanediol.
Claim 5
Dependent Claim
13 words
The composition of claim 2 in which the vicinal alkane polyol is 1,2,3-propanetriol.
Claim 6
Dependent Claim
21 words
The composition of claim 1 in which the alkaline silicate corresponds to 20-30 pbw per 100 pbw of dry water-insoluble solids.
Claim 7
Dependent Claim
23 words
The composition of claim 1 in which the vicinal alkane polyol corresponds to 50-85 pbw per 100 pbw of dry alkaline silicate solids.
Claim 8
Dependent Claim
29 words
The composition of claim 1 in which the water-insoluble solids are comprised on an admixture of 50-200 pbw finely divided inert filler per 100 pbw of catalytic metal oxides.
Claim 9
Dependent Claim
30 words
The composition of claim 1 in which the waterinsoluble solids are comprised of an admixture of 1-10 pbw of finely divided activated carbon per 100 pbw of catalytic metal oxides.
Claim 10
Dependent Claim
15 words
The composition of claim 1 in which the alkaline silicate is an alkali metal silicate.
Claim 11
Dependent Claim
14 words
The composition of claim 9 in which the alkali metal silicate is sodium silicate.
Claim 12
Independent Claim
110 words
The method of preparing a catalytic oxidation surface comprising 1. applying to the surface of a solid substrate a coating comprising (a) finely divided catalytic metal oxides dispersed in (b) an aqueous solution of alkaline silicate in which is dissolved (c) a vicinal alkane polyol, the amount of alkaline silicate corresponding to 10-40 pbw per 100 pbw of dry water-insoluble solids in the composition and the amount of polyol corresponding to 40-125 pbw per 100 pbw dry alkaline silicate, dry basis, in the composition; 2. drying the applied coating; and 3. curing the dried coating for a period of at least about 30 minutes at a temperature of 150°-280° C.
Claim 13
Independent Claim
110 words
The method of preparing a catalytic oxidation surface comprising 1. applying to the surface of a solid substrate a coating comprising (a) finely divided catalytic metal oxides dispersed in (b) an aqueous solution of alkaline silicate in which is dissolved (c) a vicinal alkane polyol, the amount of alkaline silicate corresponding to 10-40 pbw per 100 pbw of dry water-insoluble solids in the composition and the amount of polyol corresponding to 40-125 pbw per 100 pbw dry alkaline silicate, dry basis, in the composition; 2. drying the applied coating; and 3. curing the dried coating for a period of at least about 30 minutes at a temperature of 150°-280° C.
Claim 14
Dependent Claim
81 words
An assemblage for the preparation of oxidation catalyst coating compositions comprising (a) a first container of finely divided catalytic metal oxides and (b) a second container of an aqueous solution of alkaline silicate in which is dissolved vicinal alkane polyol,the amount of alkaline silicate corresponding to 10-40 pbw per 100 pbw of dry water-insoluble solids in the first container and the amount of polyol corresponding to 40-125 pbw per 100 pbw of dry alkaline silicate, dry basis, in the second container.
Claim 15
Dependent Claim
81 words
An assemblage for the preparation of oxidation catalyst coating compositions comprising (a) a first container of finely divided catalytic metal oxides and (b) a second container of an aqueous solution of alkaline silicate in which is dissolved vicinal alkane polyol,the amount of alkaline silicate corresponding to 10-40 pbw per 100 pbw of dry water-insoluble solids in the first container and the amount of polyol corresponding to 40-125 pbw per 100 pbw of dry alkaline silicate, dry basis, in the second container.
References Cited (Backward Citations)
US3658724A
Cited
US3460523A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-12 | 1981-06-13 | 1981-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-12 | 1985-06-13 | 1985-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-12 | 1989-06-13 | 1989-12-13 | $7700.00 | Window Closed / Lapsed |