Dry liquid alumina trihydrate concentrates
Assignee: Union Carbide Corp
•
Filing: 1976-09-29
•
Granted: 1977-12-13
•
Expires: 1996-09-29
Abstract
Abstract This invention is concerned with dry liquid concentrates of hydrated alumina, that is, aluminum trihydrate, coated with a substantial amount of a silane containing three hydrolyzable groups bonded to a silicon atom thereof and containing at least one monovalent group which contains a polyalkylene oxide moiety therein, and/or hydrolyzates of such silanes and/or condensates of such hydrolyzates. Such treated hydrated alumina concentrate are useful in the treatment of alumina trihydrate particles to enhance their usefulness in reinforced plastic compositions and in coatings.
Inventors
- 👤 Sidney Ethan Berger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:37
CPC Classifications
C; C08; C08K; C08K9/00; C08K9/04; C08K9/06; C09; C09C; C09C1/00; C09C1/40; C09C1/407; C09C3/00; C09C3/12; C01; C01P; C01P2004/00; C01P2004/60; C01P2004/61; C01P2004/80; C01P2006/00; C01P2006/22; C01P2006/90; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2995; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
67 words
A composition comprising aluminum trihydrate particles containing on their surfaces a concentrated amount of silane, its hydrolyzates or resulting condensate, which silane possesses at least two to about three hydrolyzable groups bonded to the silicon thereof and an organic group which contains a polyalkylene oxide group, said concentrated amount of silane being at least greater than 5 and up to about 35 weight percent of the composition.
Claim 2
Dependent Claim
67 words
A composition comprising aluminum trihydrate particles containing on their surfaces a concentrated amount of silane, its hydrolyzates or resulting condensate, which silane possesses at least two to about three hydrolyzable groups bonded to the silicon thereof and an organic group which contains a polyalkylene oxide group, said concentrated amount of silane being at least greater than 5 and up to about 35 weight percent of the composition.
Claim 3
Dependent Claim
23 words
The composition of claim 1 wherein the amount of the silane is from about 10 to about 30 weight percent of the composition.
Claim 4
Dependent Claim
88 words
The composition of claim 1 wherein the silane has the following general formula: R.sup.II (OR.sup.I).sub.a ORSiX.sub.3 wherein R can be any divalent organic group which is either oxygen or carbon bonded to the silicon atom, R I is one or more 1,2-alkylene groups each containing at least 2 carbon atoms and not more than about 4 carbon atoms; R II is hydrogen, alkyl, acyloxy or an organofunctional group; X is a hydrolyzable group; and a is a number having an average value of from 4 to about 150.
Claim 5
Dependent Claim
72 words
The composition of claim 3 wherein the silane is coreacted or comixed with a different silane, as encompassed by the following formula: R.sup.3.sub.n (SiX.sub.4-n).sub.b or the cohydrolyzate or the cocondensate of such different silane with the silane, wherein R 3 is an organic radical whose free valence is equal to the value of b, X is as defined above, n is equal to 0 or 1 and b is a positive number.
Claim 6
Dependent Claim
93 words
A process for the treatment of aluminum trihydrate particles which comprises mixing untreated aluminum trihydrate particles with treated aluminum trihydrate particles containing on their surfaces a concentrated amount of silane, its hydrolyzates or resulting condensate, which silane possesses at least two to about three hydrolyzable groups bonded to the silicon thereof and an organic group which contains a polyalkylene oxide group, said concentrated amount of silane being at least greater than 5 and up to about 35 weight percent, based on the total weight of said silane and said treated aluminum trihydrate particles.
Claim 7
Dependent Claim
93 words
A process for the treatment of aluminum trihydrate particles which comprises mixing untreated aluminum trihydrate particles with treated aluminum trihydrate particles containing on their surfaces a concentrated amount of silane, its hydrolyzates or resulting condensate, which silane possesses at least two to about three hydrolyzable groups bonded to the silicon thereof and an organic group which contains a polyalkylene oxide group, said concentrated amount of silane being at least greater than 5 and up to about 35 weight percent, based on the total weight of said silane and said treated aluminum trihydrate particles.
Claim 8
Dependent Claim
20 words
The process of claim 5 wherein said silane has the following formula: H.sub.3 CO(CH.sub.2 CH.sub.2 O).sub.7.5 OCH.sub.2 CH.sub.2 CH.sub.2 Si(OCH.sub.3).sub.3.
Claim 9
Dependent Claim
19 words
The composition of claim 1 wherein the silane has the following formula: N.sub.3 CO(CH.sub.2 CH.sub.2 0).sub.7.5 OCH.sub.2 CH.sub.2CH.sub.2 Si(OCH.sub.3).sub.3.
Claim 10
Dependent Claim
20 words
The composition of claim 1 wherein the silane has the following formula: H.sub.3 CO--CH.sub.2 CH.sub.2 O).sub.113 CH.sub.2 CH.sub.2 CH.sub.2 Si(OCH.sub.3).sub.3.
Claim 11
Dependent Claim
17 words
The composition of claim 2 wherein a has a value of from about 4 to about 120.
Claim 12
Dependent Claim
17 words
The composition of claim 4 wherein a has a value of from about 4 to about 120.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-12 | 1981-06-13 | 1981-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-12 | 1985-06-13 | 1985-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-12 | 1989-06-13 | 1989-12-13 | $7700.00 | Window Closed / Lapsed |