Glass composition which is resistant to alkali
Assignee: AGC Inc
•
Filing: 1976-04-01
•
Granted: 1977-12-13
•
Expires: 1996-04-01
Abstract
Abstract A glass composition which possesses a chemical resistance. The glass composition consists essentially of SiO 2 : 45 - 65 wt.% ZrO 2 : 10 - 20 wt.% Cr 2 O 3 : 0 - 5 wt.% SnO 2 : 0 - 5 wt.% Ro: 0 - 18 wt.% R' 2 o: 0 - 18 wt.% So 3 : 0.05 - 1 wt.% Wherein the sum of contents of Cr 2 O 3 + SnO 2 is 0.5 - 10 wt.%; the sum of contents of ZrO 2 + SnO 2 + Cr 2 O 3 is 12 - 25 wt.%; RO is selected from the group consisting of CaO, MgO, ZnO, BaO, and SrO; and R' 2 O is selected from the group consisting of K 2 O of 0 - 5 wt.%, Na 2 O of 0 - 18 wt.% and Li 2 O of 0 - 5 wt.%.
Inventors
- 👤 Yoshiro Suzuki
- 👤 Hironori Ohta
- 👤 Masuo Shirasaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:37
CPC Classifications
C; C03; C03C; C03C13/00; C03C13/001; C03C13/002; C03C3/00; C03C3/04; C03C3/076; C03C3/078
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
124 words
A glass composition consisting of SiO 2 :45-65 wt.% ZrO 2 :10-20 wt.% Cr 2 O 3 :0-5 wt.% SnO 2 :0-5 wt.% Ro:0-18 wt.% R' 2 o:0-18 wt.% So 3 :0.05-1 wt.% and less than 3 wt.% of a refining agent or impurities, wherein the sum of contents of Cr 2 O 3 + SnO 2 is 0.5-10 wt.% and the sum of contents of ZrO 2 + SnO 2 + Cr 2 O 3 is 12-25 wt.% and RO is selected from the group consisting of CaO, MgO, ZnO, BaO and SrO; and R' 2 O is selected from the group consisting of K 2 O of 0-5 wt.%, Na 2 O of 0-18 wt.% and Li 2 O of 0-5 wt.%.
Claim 2
Dependent Claim
124 words
A glass composition consisting of SiO 2 :45-65 wt.% ZrO 2 :10-20 wt.% Cr 2 O 3 :0-5 wt.% SnO 2 :0-5 wt.% Ro:0-18 wt.% R' 2 o:0-18 wt.% So 3 :0.05-1 wt.% and less than 3 wt.% of a refining agent or impurities, wherein the sum of contents of Cr 2 O 3 + SnO 2 is 0.5-10 wt.% and the sum of contents of ZrO 2 + SnO 2 + Cr 2 O 3 is 12-25 wt.% and RO is selected from the group consisting of CaO, MgO, ZnO, BaO and SrO; and R' 2 O is selected from the group consisting of K 2 O of 0-5 wt.%, Na 2 O of 0-18 wt.% and Li 2 O of 0-5 wt.%.
Claim 3
Dependent Claim
106 words
A glass composition consisting SiO 2 :45-65 wt.% ZrO 2 :10-20 wt.% Cr 2 O 3 :0-5 wt.% SnO 2 :0.5-5 wt.% Ro:0-15 wt.% R' 2 o:5-18 wt.% So 3 :0.05-1 wt.% and less than 3 wt.% of a refining agent or impurities, wherein the sum of contents of ZrO 2 + SnO 2 + Cr 2 O 3 is 12-25 wt.%; RO is selected from the group consisting of CaO, MgO, ZnO, BaO and SrO and R' 2 O is selected from the group consisting of K 2 O of 0-5 wt.%, Na 2 O of 5-18 wt.% and Li 2 O of 0-5 wt.%.
Claim 4
Dependent Claim
106 words
A glass composition consisting SiO 2 :45-65 wt.% ZrO 2 :10-20 wt.% Cr 2 O 3 :0-5 wt.% SnO 2 :0.5-5 wt.% Ro:0-15 wt.% R' 2 o:5-18 wt.% So 3 :0.05-1 wt.% and less than 3 wt.% of a refining agent or impurities, wherein the sum of contents of ZrO 2 + SnO 2 + Cr 2 O 3 is 12-25 wt.%; RO is selected from the group consisting of CaO, MgO, ZnO, BaO and SrO and R' 2 O is selected from the group consisting of K 2 O of 0-5 wt.%, Na 2 O of 5-18 wt.% and Li 2 O of 0-5 wt.%.
Claim 5
Dependent Claim
115 words
A glass composition consisting of SiO 2 :45-65 wt.% ZrO 2 :10-20 wt.% Cr 2 O 3 :0.5-5 wt.% SnO 2 :0.5-5 wt.% Ro:5-15 wt.% R' 2 o:5 - 15 wt.% So 3 :0.05 - 1 wt.% and less than 3 wt.% of a refining agent or impurities, wherein the sum of contents of ZrO 2 + SnO 2 + Cr 2 O 3 is 12 - 25 wt.%, RO is selected from the group consisting of CaO, MgO, ZnO, BaO and SrO and R' 2 O is selected from the group consisting of K 2 O of 0-3 wt.%, Na 2 O of 5-15 wt.% and Li 2 O of 0 - 3 wt.%.
Claim 6
Dependent Claim
115 words
A glass composition consisting of SiO 2 :45-65 wt.% ZrO 2 :10-20 wt.% Cr 2 O 3 :0.5-5 wt.% SnO 2 :0.5-5 wt.% Ro:5-15 wt.% R' 2 o:5 - 15 wt.% So 3 :0.05 - 1 wt.% and less than 3 wt.% of a refining agent or impurities, wherein the sum of contents of ZrO 2 + SnO 2 + Cr 2 O 3 is 12 - 25 wt.%, RO is selected from the group consisting of CaO, MgO, ZnO, BaO and SrO and R' 2 O is selected from the group consisting of K 2 O of 0-3 wt.%, Na 2 O of 5-15 wt.% and Li 2 O of 0 - 3 wt.%.
Claim 7
Dependent Claim
11 words
A glass fiber made of the glass composition of claim 1.
Claim 8
Dependent Claim
11 words
A glass fiber made of the glass composition of claim 3.
Claim 9
Dependent Claim
22 words
In a cement product comprising a Portland cement and a glass fiber, the improvement which comprises the glass fiber of claim 4.
References Cited (Backward Citations)
SU289997A1
Cited
US3375095A
Cited
US3511629A
Cited
US3846143A
Cited
US3783092A
Cited
US3861926A
Cited
US3615767A
Cited
SU455072A1
Cited
US3861927A
Cited
US3904424A
Cited
US3833388A
Cited
US3928049A
Cited
US4002482A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-12 | 1981-06-13 | 1981-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-12 | 1985-06-13 | 1985-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-12 | 1989-06-13 | 1989-12-13 | $7700.00 | Window Closed / Lapsed |