US4062153A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Silenced grinding wheel
Assignee: SLIPMATERIAL NAXOS AB
•
Filing: 1976-07-12
•
Granted: 1977-12-13
•
Expires: 1996-07-12
Abstract
Abstract The noise and vibrations produced by a grinding wheel can be reduced if the wheel is composed of two or more grinding discs joined together by means of layers of a polymer material having a thickness of at least 0.2 mm and not greater than the thickness of the grinding discs. The discs shall have a ratio of diameter to thickness of at least 10. The polymer material shall have a hardness below 90 Shore A, and a loss factor of at least 0.25.
Inventors
- 👤 Bjorn Malm
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 12:44
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B24; B24D; B24D5/00; B24D5/06; B24D5/066; B32B27/40; B32B7/00; B32B7/04; B32B7/12; B32B2250/00; B32B2250/05; B32B2250/24; B32B2375/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
72 words
Grinding wheel consisting of two or more grinding discs joined together, wherein the ratio of diameter to thickness of the discs is at least 10, said discs are joined together by means of layers of polymer material having a thickness of at least 0.2mm and not greater than the thickness of the discs, and the polymer material has a hardness below 90 Shore A and a loss factor of at least 0.25.
Claim 2
Dependent Claim
72 words
Grinding wheel consisting of two or more grinding discs joined together, wherein the ratio of diameter to thickness of the discs is at least 10, said discs are joined together by means of layers of polymer material having a thickness of at least 0.2mm and not greater than the thickness of the discs, and the polymer material has a hardness below 90 Shore A and a loss factor of at least 0.25.
Claim 3
Dependent Claim
19 words
Grinding wheel according to claim 1, wherein the hardness of the polymer material is 30 - 80 Shore A.
Claim 4
Dependent Claim
20 words
Grinding wheel according to claim 1, wherein the composite wheel has a diameter to thickness ratio of at least 4.
Claim 5
Dependent Claim
13 words
Grinding wheel according to claim 1, wherein the polymer material is a polyurethane.
Claim 6
Dependent Claim
51 words
Grinding wheel according to claim 4, wherein the polyurethane has been produced by reaction between 55 - 80, preferably 60 - 75, percent by weight castor oil, or a derivative thereof, and 20 - 45, preferably 25 - 40, percent by weight isocyanate of toluene diisocyanate or diphenyl methane diisocyanate type.
Claim 7
Dependent Claim
19 words
Grinding wheel according to claim 1, in which the loss factor of the polymer material is at least 0.4.
References Cited (Backward Citations)
US1290990A
Cited
US1970835A
Cited
US2268663A
Cited
US2353864A
Cited
GB621795A
Cited
US2690632A
Cited
US3136614A
Cited
US3271911A
Cited
US3597884A
Cited
US3838543A
Cited
US3716950A
Cited
US3919580A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-12 | 1981-06-13 | 1981-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-12 | 1985-06-13 | 1985-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-12 | 1989-06-13 | 1989-12-13 | $7700.00 | Window Closed / Lapsed |