US4061821A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Semipermeable composite membranes
Assignee: Asahi Kasei Corp
•
Filing: 1976-12-14
•
Granted: 1977-12-06
•
Expires: 1996-12-14
Abstract
Abstract A semipermeable composite membrane which shows only a small reduction of water permeability even when it is subjected to one time hot water treatment or drying treatment is provided according to the method of the present invention. Said semipermeable composite membrane consists of a porous substance and a reinforcing material embedded therein. Said porous substance has a porous region of network structure at least in one part thereof and numbers of voids in said porous region. Said reinforcing material is a fabric in case of flat type membrane or a braid having a central hollow portion in case of hollow fiber type membrane which is embedded in the wall of the membrane. Said method comprises impregnating said reinforcing material with a polymer solution and treating the impregnated reinforcing material with a coagulating liquid.
Inventors
- 👤 Fusakazu Hayano
- 👤 Yasuo Hashino
- 👤 Kiyoshi Ichikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 05:15
CPC Classifications
B; B01; B01D; B01D69/00; B01D69/12; B01D69/08; B01D69/10; B01D69/107; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2922; Y10T428/2925; Y10T428/2973; Y10T428/2975
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
102 words
A semipermeable composite membrane consisting of a porous substance and a reinforcing material made of fibrous material embedded in the wall of the porous substance, at least one part of said porous substance forming a porous region of a network structure having pore sizes in the range from 500A to 5μ; said porous region containing a number of voids having diameters of 10μ or greater; and the ratio of water permeability of said membrane after one time treatment with hot water at 80° C or after drying at 20° C to the respective water permeability before said treatment being 0.3 or higher.
Claim 2
Dependent Claim
102 words
A semipermeable composite membrane consisting of a porous substance and a reinforcing material made of fibrous material embedded in the wall of the porous substance, at least one part of said porous substance forming a porous region of a network structure having pore sizes in the range from 500A to 5μ; said porous region containing a number of voids having diameters of 10μ or greater; and the ratio of water permeability of said membrane after one time treatment with hot water at 80° C or after drying at 20° C to the respective water permeability before said treatment being 0.3 or higher.
Claim 3
Dependent Claim
29 words
A semipermeable composite membrane according to claim 1 wherein the reinforcing material made of fibrous material is a fabric and the resultant semipermeable composite membrane is of flat shape.
Claim 4
Dependent Claim
36 words
A semipermeable composite membrane according to claim 1 wherein the reinforcing material made of fibrous material is a braid having a central hollow portion and the resultant semipermeable composite membrane is of a hollow fiber shape.
Claim 5
Dependent Claim
38 words
A semipermeable composite membrane according to claim 1 wherein the water permeability after one time treatment with hot water at 80° C or after drying at 20° C is 2 m 3 /m 2 ·day·Kg/cm 2 or higher.
Claim 6
Dependent Claim
23 words
A semipermeable composite membrane according to claim 1 wherein a gradient-type porous region is included in at least one surface of said membrane.
Claim 7
Dependent Claim
20 words
A semiperemeable composite membrane according to claim 3 wherein said braid having a hollow portion is prepared by knitting monofilaments.
Claim 8
Dependent Claim
28 words
A semipermeable composite membrane according to claim 6 wherein said monofilaments are made of a polymer selected from the group consisting of polyesters, acrylonitrile polymers, nylons and polyolefins.
Claim 9
Dependent Claim
20 words
A semipermeable composite membrane according to claim 1 wherein said porous member is made of a copolymer mainly of acrylonitrile.
Claim 10
Dependent Claim
114 words
A method for producing a hollow fiber type semipermeable composite membrane containing an embedded braid having a central hollow portion which comprises feeding a polymer solution and a braid having a central hollow portion which is insoluble in the polymer solution, simultaneously to a spinning nozzle, impregnating the braid with the polymer solution inside the nozzle, taking out the braid impregnated with the polymer solution and introducing both the braid and the polymer solution into a liquid which does not dissolve the polymer to coagulate the polymer whereby a hollow fiber type semipermeable membrane consisting of a porous substance and a reinforcing material having a central hollow portion, defined in claim 1 is obtained.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-05 | 1981-06-06 | 1981-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-05 | 1985-06-06 | 1985-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-05 | 1989-06-06 | 1989-12-06 | $7700.00 | Window Closed / Lapsed |