Process for manufacturing ultrathin polymer membranes and products derived therefrom
Assignee: North Star Research and Development Institute
•
Filing: 1974-03-27
•
Granted: 1976-01-20
•
Expires: 1994-03-27
Abstract
Abstract Unsupported ultrathin polymer film is made in bulk form by floating the film on a bath, transferring the floating film to a release substrate, drying the resulting film/substrate composite, separating the film from the substrate, and retrieving the unsupported film, e.g. in the form of a convoluted roll provided with anti-blocking agent in between the convolutions. The bulk product can be made into thermal insulating material, flake-like weather modifying agents, etc.
Inventors
- 👤 Roy E. Larson
- 👤 Ralph H. Forester, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 05:28
CPC Classifications
B; B01; B01D; B01D69/00; B01D69/12; B01D69/122; B01D39/00; B01D39/02; B01D39/04; B29; B29D; B29D7/00; B29D7/01; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
130 words
A method for making unsupported ultrathin polymer film having autogenous bonding characteristics when moist comprising the steps of: a. floating an ultrathin polymer film having an ultrathin caliper less than 2.5 microns on the surface of a liquid bath capable of supporting said ultrathin polymer film; b. contacting a surface of the floating ultrathin polymer film with a surface of a flexible release substrate to form a flexible separable composite comprising said film having an exposed surface and said release substrate; c. at least partially drying said separable composite; d. applying a particulate anti-blocking agent to the exposed surface of said ultrathin polymer film portion of said composite and separating said ultrathin polymer film from said release substrate; and e. retrieving the thus-separated, unsupported ultrathin polymer film in bulk form.
Claim 2
Independent Claim
130 words
A method for making unsupported ultrathin polymer film having autogenous bonding characteristics when moist comprising the steps of: a. floating an ultrathin polymer film having an ultrathin caliper less than 2.5 microns on the surface of a liquid bath capable of supporting said ultrathin polymer film; b. contacting a surface of the floating ultrathin polymer film with a surface of a flexible release substrate to form a flexible separable composite comprising said film having an exposed surface and said release substrate; c. at least partially drying said separable composite; d. applying a particulate anti-blocking agent to the exposed surface of said ultrathin polymer film portion of said composite and separating said ultrathin polymer film from said release substrate; and e. retrieving the thus-separated, unsupported ultrathin polymer film in bulk form.
Claim 3
Dependent Claim
47 words
A method according to claim 1 wherein said retrieving step includes taking up said unsupported ultrathin film with a driven roller to form a convoluted roll, each convolution of said convoluted roll being separated from the next inner convolution by a layer of said particulate anti-blocking agent.
Claim 4
Dependent Claim
62 words
A method according to claim 1 wherein said step (b) includes bonding said ultrathin polymer film to said release layer by autogenous lamination at the interface between them with inherent cohesive forces, and wherein said release layer is selected to provide inherent cohesive forces which are weak enough to permit delamination of said separable composite without damage to said ultrathin polymer membrane.
Claim 5
Dependent Claim
23 words
A method according to claim 3 wherein said separating is carried out by treating said separable composite with said liquid or gaseous water.
Claim 6
Dependent Claim
31 words
A method according to claim 1 wherein said separable composite formed by said step (b) is passed through a drying zone in step (c) maintained at a drying temperature above 100°C.
Claim 7
Dependent Claim
23 words
A method according to claim 1 wherein said method is continuous and wherein said flexible release layer comprises a continuously moving carrier web.
Claim 8
Dependent Claim
26 words
A method according to claim 1 wherein said floating step is carried out by casting said ultrathin polymer film on the surface of said liquid bath.
Claim 9
Dependent Claim
73 words
A method according to claim 5 wherein the drying of said separable composite is carried out by: conveying said separable composite through said drying zone with said film facing upward and said release substrate facing downward, and exposing said release substrate of said separable composite to upward currents of heated air in said drying zone, whereby said release substrate is raised to a temperature in excess of 100°C. but less than about 250°C.
Claim 10
Dependent Claim
45 words
A method according to claim 2 wherein the separated, unsupported ultrathin polymer film is fed to said convoluted roll at a substantially constant linear feed rate and the linear speed of the periphery of said convoluted roll is maintained substantially equal to said feed rate.
Claim 11
Independent Claim
146 words
A method for making unsupported ultrathin polymer film having autogenous bonding characteristics when moist comprising the steps of: a. floating an ultrathin polymer film having an ultrathin caliper less than 2.5 microns on the surface of a liquid bath capable of supporting said ultrathin polymer film; b. contacting a surface of the floating ultrathin polymer film with a surface of a flexible release substrate to form a flexible separable composite comprising said film having an exposed surface and said release substrate; c. at least partially drying said separable composite; d. separating said ultrathin polymer film from said release substrate; and e. retrieving the thus-separated, unsupported ultrathin polymer film in bulk form by feeding said ultrathin polymer film to a driven roller at a linear feed rate which alternatively is increased and decreased with respect to the linear speed of the periphery of the resulting convoluted roll.
Claim 12
Independent Claim
146 words
A method for making unsupported ultrathin polymer film having autogenous bonding characteristics when moist comprising the steps of: a. floating an ultrathin polymer film having an ultrathin caliper less than 2.5 microns on the surface of a liquid bath capable of supporting said ultrathin polymer film; b. contacting a surface of the floating ultrathin polymer film with a surface of a flexible release substrate to form a flexible separable composite comprising said film having an exposed surface and said release substrate; c. at least partially drying said separable composite; d. separating said ultrathin polymer film from said release substrate; and e. retrieving the thus-separated, unsupported ultrathin polymer film in bulk form by feeding said ultrathin polymer film to a driven roller at a linear feed rate which alternatively is increased and decreased with respect to the linear speed of the periphery of the resulting convoluted roll.
References Cited (Backward Citations)
US3073733A
Cited
US3687772A
Cited
US3551244A
Cited
US3650880A
Cited
US3843436A
Cited
US3810814A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-19 | 1979-07-21 | 1980-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-19 | 1983-07-21 | 1984-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-19 | 1987-07-21 | 1988-01-20 | $7700.00 | Window Closed / Lapsed |