US4061706A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the continuous melt thermoforming of polymers
Assignee: DuPont Canada Inc
•
Filing: 1975-10-22
•
Granted: 1977-12-06
•
Expires: 1995-10-22
Abstract
Abstract A process for the continuous melt thermoforming of thermoplastic polymers is disclosed. The process comprises extruding a flat web of molten polymer in a downward direction and directly over a series of mould cavities moving at a predetermined speed thereby sequentially covering the mould cavities. A vacuum is applied to the mould cavities and the web of molten polymer is brought into contact with the surface of the mould cavity, the mould defining the mould cavity being comprised of porous metal. The polymer is cooled and the resultant article is removed from the mould. The process is controlled so that the articles thermoformed in the process are of substantially uniform thickness. In embodiments the mould cavities are located on the periphery of a continuous belt or preferably a wheel. The process may be operated with polymers of low zero shear viscosity. The preferred polymers are polyamides, especially polyhexamethylene adipamide, of relative viscosity in the range 25 to 65. Substantially inflexible open containers comprised of a polyamide having a relative viscosity in the range 25 to 65 are also disclosed. The containers may be of thickness in the range of 2 to 30 mils.
Inventors
- 👤 Peter Roe Duffield
- 👤 Peter Robin Flockton
- 👤 Rupert Martin Lillis
- 👤 Brian Maurice Turner
- 👤 Donald Edward Crowell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 10:44
CPC Classifications
B; B29; B29C; B29C51/00; B29C51/18; B29C51/20; B29C51/22; B29C51/26; B29C51/30; B29C51/36; B29C51/365
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
184 words
A process for the continuous melt thermoforming of articles of substantially uniform thickness derived from a thermoplastic polymer of low zero shear viscosity comprising the steps of: a. extruding a flat web of molten polymer in a downward direction and directly over a series of mould cavities formed by a mould surface in a mould block moving at a predetermined speed, and sequentially covering said mould cavities with said flat web, b. applying a vacuum to the mould cavities sufficient to cause the web of molten polymer to contact the surface of the mould cavity, said mould block having a lower surface and being constructed substantially entirely from porous sintered metal whereby said vacuum is uniformly transmitted between said lower surface and said mould cavities in said mould surface. c. cooling the polymer in said cavities, d. maintaining substantially uniform thickness of the articles by controlling the extrusion of the flat web of polymer, the application of vacuum, the contacting of the web of molten polymer with the mould cavities and the speed at which the mould cavities move, and e. removing the articles.
Claim 2
Dependent Claim
184 words
A process for the continuous melt thermoforming of articles of substantially uniform thickness derived from a thermoplastic polymer of low zero shear viscosity comprising the steps of: a. extruding a flat web of molten polymer in a downward direction and directly over a series of mould cavities formed by a mould surface in a mould block moving at a predetermined speed, and sequentially covering said mould cavities with said flat web, b. applying a vacuum to the mould cavities sufficient to cause the web of molten polymer to contact the surface of the mould cavity, said mould block having a lower surface and being constructed substantially entirely from porous sintered metal whereby said vacuum is uniformly transmitted between said lower surface and said mould cavities in said mould surface. c. cooling the polymer in said cavities, d. maintaining substantially uniform thickness of the articles by controlling the extrusion of the flat web of polymer, the application of vacuum, the contacting of the web of molten polymer with the mould cavities and the speed at which the mould cavities move, and e. removing the articles.
Claim 3
Dependent Claim
18 words
The process of claim 1 in which the mould cavities are located on the periphery of a wheel.
Claim 4
Dependent Claim
23 words
The process of claim 2 in which the porous metal of the mould has a pore size of not greater than 12 microns.
Claim 5
Dependent Claim
23 words
The process of claim 3 in which the metal of the mould is selected from the group consisting of bronze and stainless steel.
Claim 6
Dependent Claim
19 words
The process claim 2 in which a portion of the periphery of the wheel is made from porous metal.
Claim 7
Dependent Claim
16 words
The process of claim 1 in which the mould cavities are located on a continuous belt.
Claim 8
Dependent Claim
27 words
The process of claim 1 in which the thermoplastic polymer is selected from the group consisting of polyamides, polyesters, polyolefins, acetals, polycarbonates, polysulfones, polyacrylates and ionomeric resins.
Claim 9
Dependent Claim
13 words
The process of claim 1 in which the thermophastic polymer is a polyamide.
Claim 10
Dependent Claim
20 words
The process of claim 1 in which the thermoplastic polymer is a polyamide having a relative viscosity greater than 25.
Claim 11
Dependent Claim
24 words
The process of claim 1 in which the thermoplastic polymer is polyhexamethylene adipamide having a relative viscosity in the range 25 to 65 .
Claim 12
Dependent Claim
23 words
The process of claim 1 in which the thermoplastic polymer is polyhexamethylene adipamide having a relative viscosity in the range 25 to 50.
Claim 13
Dependent Claim
30 words
The process of claim 1 in which the thermoplastic polymer is a polyamide blended with an additive selected from the group consisting of fillers, pigments, heat stabilizers and mixtures thereof.
Claim 14
Dependent Claim
43 words
The process of claim 1 in which the thermoplastic polymer is polyhexamethylene adipamide blended with an additive selected from the group consisting of fillers, pigments, heat stabilizers and mixtures thereof, said polyhexamethylene adipamide having a relative viscosity in the range 25 to 50.
Claim 15
Dependent Claim
43 words
The process of claim 1 in which the thermoplastic polymer is polyhexamethylene adipamide blended with an additive selected from the group consisting of fillers, pigments, heat stabilizers and mixtures thereof, said polyhexamethylene adipamide having a relative viscosity in the range 30 to 45.
Claim 16
Dependent Claim
15 words
The process of claim 1 in which the moulds defining the mould cavities are cooled.
Claim 17
Dependent Claim
15 words
The process of claim 1 in which the articles produced are substantially free from distortion.
Claim 18
Dependent Claim
18 words
The process of claim 1 wherein said mould defining said mould cavity is comprised entirely of porous metal.
Claim 19
Dependent Claim
28 words
The process of claim 1 wherein a uniform vacuum is applied to the mould cavities immediately after the web of molten polymer covers all of such mould cavity.
Claim 20
Dependent Claim
27 words
The process of claim 1 wherein a uniform vacuum is applied to the mould cavities before the web of molten polymer covers all of such mould cavity.
Claim 21
Dependent Claim
12 words
The process of claim 1 in which the thermoplastic polymer is polyethylene.
References Cited (Backward Citations)
CA820769A
Cited
CA834029A
Cited
US3333032A
Cited
GB1136613A
Cited
US3381445A
Cited
US3353219A
Cited
US3453162A
Cited
GB1268571A
Cited
US3527854A
Cited
CA933714A
Cited
GB1333720A
Cited
US3685930A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-05 | 1981-06-06 | 1981-12-06 | $2000.00 | Window Closed / Lapsed |