US4058579A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing an improved boron nitride crucible
Assignee: Praxair ST Technology Inc
•
Filing: 1976-02-05
•
Granted: 1977-11-15
•
Expires: 1996-02-05
Abstract
Abstract A boron nitride crucible, suitable for the vaporization of aluminum, having a multi-walled structure comprising an outer wall and a thinner inner wall weakly bonded to the thicker outer wall. Because of this structure, the crucible is considerably more flexible than conventional single-walled crucibles and exhibits substantially improved thermal cycling characteristics and longer life. The crucible is produced by depositing pyrolytic boron nitride upon a mandrel having the shape of the desired crucible at a temperature of from about 1850° C. to about 2100° C. until a first layer of boron nitride of suitable thickness has been produced, interrupting the deposition of boron nitride upon the mandrel and lowering the temperature to below 1750° C., and then depositing additional boron nitride upon the mandrel at a temperature of from about 1850° C. to about 2100° C. to produce a second outer layer of boron nitride having a thickness greater than that of the inner layer. The steps may be repeated at least one additional time so as to deposit at least one additional layer of boron nitride upon the second boron nitride layer.
Inventors
- 👤 Robert William Lashway
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 23:19
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/583; C23; C23C; C23C14/00; C23C14/22; C23C14/24; C23C14/243; C23C16/00; C23C16/01
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
193 words
A process for producing a boron nitride crucible having a multi-walled structure comprising an outer wall and a thinner inner wall weakly bonded to the thicker outer wall, said process comprising: (1) reacting ammonia and a boron halide in vapor phase at a temperature of from about 1850° C. to about 2100° C. under a pressure no greater than about 1 mm. of mercury absolute to produce boron nitride, and depositing a first layer of said boron nitride upon a mandrel having the shape of the desired crucible; (2) interrupting the reaction between the ammonia and boron halide and the further deposition of boron nitride upon the mandrel; (3) lowering the temperature of the boron nitride layer to below 1750° C.; and (4) reacting additional ammonia and boron halide in vapor phase at a temperature of from about 1850° C. to about 2100° C. under a pressure no greater than about 1 mm. of mercury absolute to produce additional boron nitride and depositing a second layer of said boron nitride upon the first boron nitride layer, said second layer of boron nitride having a thickness greater than that of the inner first layer.
Claim 2
Dependent Claim
193 words
A process for producing a boron nitride crucible having a multi-walled structure comprising an outer wall and a thinner inner wall weakly bonded to the thicker outer wall, said process comprising: (1) reacting ammonia and a boron halide in vapor phase at a temperature of from about 1850° C. to about 2100° C. under a pressure no greater than about 1 mm. of mercury absolute to produce boron nitride, and depositing a first layer of said boron nitride upon a mandrel having the shape of the desired crucible; (2) interrupting the reaction between the ammonia and boron halide and the further deposition of boron nitride upon the mandrel; (3) lowering the temperature of the boron nitride layer to below 1750° C.; and (4) reacting additional ammonia and boron halide in vapor phase at a temperature of from about 1850° C. to about 2100° C. under a pressure no greater than about 1 mm. of mercury absolute to produce additional boron nitride and depositing a second layer of said boron nitride upon the first boron nitride layer, said second layer of boron nitride having a thickness greater than that of the inner first layer.
Claim 3
Dependent Claim
13 words
A process as in claim 1 wherein the boron halide is boron trichloride.
Claim 4
Dependent Claim
13 words
A process as in claim 2 wherein the mandrel is made of graphite.
Claim 5
Dependent Claim
24 words
A process as in claim 1 wherein the ammonia and boron halide are reacted at a pressure below about 0.5 mm. of mercury absolute.
Claim 6
Dependent Claim
13 words
A process as in claim 4 wherein the boron halide is boron trichloride.
Claim 7
Dependent Claim
13 words
A process as in claim 5 wherein the mandrel is made of graphite.
Claim 8
Dependent Claim
26 words
A process as in claim 1 wherein the ammonia and boron halide are reacted at a temperature of from about 1900° C. to about 1950° C.
Claim 9
Dependent Claim
13 words
A process as in claim 7 wherein the boron halide is boron trichloride.
Claim 10
Dependent Claim
13 words
A process as in claim 8 wherein the mandrel is made of graphite.
Claim 11
Dependent Claim
24 words
A process as in claim 7 wherein the ammonia and boron halide are reacted at a pressure below about 0.5 mm. of mercury absolute.
Claim 12
Dependent Claim
13 words
A process as in claim 10 wherein the boron halide is boron trichloride.
Claim 13
Dependent Claim
13 words
A process as in claim 11 wherein the mandrel is made of graphite.
Claim 14
Dependent Claim
239 words
A process for producing a boron nitride crucible having a multi-walled structure comprising an outer wall, an inner wall, and at least one intermediate wall, said process comprising: (1) reacting ammonia and a boron halide in vapor phase at a temperature of from about 1850° C. to about 2100° C. under a pressure no greater than about 1 mm. of mercury absolute to produce boron nitride, and depositing a first layer of said boron nitride upon a mandrel having the shape of the desired crucible; (2) interrupting the reaction between the ammonia and boron halide and the further deposition of boron nitride upon the mandrel; (3) lowering the temperature of the boron nitride layer to below 1750° C.; (4) reacting additional ammonia and boron halide in vapor phase at a temperature of from about 1850° C. to about 2100° C. under a pressure no greater than about 1 mm. of mercury absolute to produce additional boron nitride and depositing a second layer of said boron nitride upon the first boron nitride layer; and (5) repeating steps 2, 3 and 4 at least one additional time so as to deposit at least one additional layer of boron nitride upon the second boron nitride layer, all of said boron nitride layers being weakly bonded to each other, the outer layer being of greater thickness than the other layers, and the intermediate layers being of no greater thickness than the inner layer.
Claim 15
Dependent Claim
239 words
A process for producing a boron nitride crucible having a multi-walled structure comprising an outer wall, an inner wall, and at least one intermediate wall, said process comprising: (1) reacting ammonia and a boron halide in vapor phase at a temperature of from about 1850° C. to about 2100° C. under a pressure no greater than about 1 mm. of mercury absolute to produce boron nitride, and depositing a first layer of said boron nitride upon a mandrel having the shape of the desired crucible; (2) interrupting the reaction between the ammonia and boron halide and the further deposition of boron nitride upon the mandrel; (3) lowering the temperature of the boron nitride layer to below 1750° C.; (4) reacting additional ammonia and boron halide in vapor phase at a temperature of from about 1850° C. to about 2100° C. under a pressure no greater than about 1 mm. of mercury absolute to produce additional boron nitride and depositing a second layer of said boron nitride upon the first boron nitride layer; and (5) repeating steps 2, 3 and 4 at least one additional time so as to deposit at least one additional layer of boron nitride upon the second boron nitride layer, all of said boron nitride layers being weakly bonded to each other, the outer layer being of greater thickness than the other layers, and the intermediate layers being of no greater thickness than the inner layer.
Claim 16
Dependent Claim
13 words
A process as in claim 13 wherein the boron halide is boron trichloride.
References Cited (Backward Citations)
GB773702A
Cited
US3063865A
Cited
US3152006A
Cited
US3226194A
Cited
US3367826A
Cited
US3549411A
Cited
US3609829A
Cited
US3576932A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-11-14 | 1981-05-16 | 1981-11-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-11-14 | 1985-05-16 | 1985-11-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-11-14 | 1989-05-16 | 1989-11-15 | $7700.00 | Window Closed / Lapsed |