Cooking surfaces of glass-ceramic plates with layers with different values for radiation transmission
Assignee: Schott AG
•
Filing: 1976-01-28
•
Granted: 1977-11-08
•
Expires: 1996-01-28
Abstract
Abstract A glass-ceramic plate cooking surface comprises a glass-ceramic base layer which allows penetration of thermal radiation having a wave length of from 0.7 to 5 microns and a top covering layer smaller in thickness than the base layer which is tightly joined to the base layer and absorbs the radiation with wave lengths of 0.7 to 5 microns. The glass-ceramic plate cooking surface can have the heating areas indicated by design and can be provided with an additional layer to avoid asymmetric stress and strengthen the cooking surface.
Inventors
- 👤 Herwig Scheidler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:28
CPC Classifications
H; H05; H05B; H05B3/00; H05B3/68; H05B3/74; H05B3/748; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24752; Y10T428/24802; Y10T428/24926; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/26; Y10T428/263; Y10T428/31504; Y10T428/31678; Y10T428/31707; Y10T428/3171
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
96 words
A glass-ceramic cooking plate for use with heating elements on the underside of the plate, the heat energy from the heating elements being transmitted through the plate to the upper surface of the plate, said plate comprising a glass-ceramic base layer having a high transmittance value for radiation whose wave length is from 0.7 to 5 microns and a covering layer smaller in thickness than the base layer, tenaciously adhered to the top of the base layer, said covering layer absorbing substantially all radiation with wave lengths of 0.7 to 5 microns transmitted the base layer.
Claim 2
Dependent Claim
96 words
A glass-ceramic cooking plate for use with heating elements on the underside of the plate, the heat energy from the heating elements being transmitted through the plate to the upper surface of the plate, said plate comprising a glass-ceramic base layer having a high transmittance value for radiation whose wave length is from 0.7 to 5 microns and a covering layer smaller in thickness than the base layer, tenaciously adhered to the top of the base layer, said covering layer absorbing substantially all radiation with wave lengths of 0.7 to 5 microns transmitted the base layer.
Claim 3
Dependent Claim
26 words
The glass-ceramic cooking plate according to claim 1 wherein the thickness of the covering layer is at most one-tenth of the thickness of the base layer.
Claim 4
Dependent Claim
21 words
The glass-ceramic cooking plate according to claim 1 wherein the thickness of the base layer is from 3 to 5.5 mm.
Claim 5
Dependent Claim
17 words
The glass-ceramic cooking plate according to claim 1 wherein the covering layer consists of an enamel layer.
Claim 6
Dependent Claim
27 words
The glass-ceramic cooking plate according to claim 1 wherein the covering layer is constructed of a metal oxide fused into the upper surface of the base layer.
Claim 7
Dependent Claim
23 words
The cooking surface according to claim 5 wherein the metal oxide is selected from the group consisting of cobalt oxide and manganese oxide.
Claim 8
Dependent Claim
31 words
The glass-ceramic cooking plate according to claim 1 wherein the covering layer is placed only on preselected portions of the top of the base layer to advantageously indicate preferential heating zones.
Claim 9
Dependent Claim
47 words
The glass-ceramic cooking plate according to claim 1 wherein a third layer is tenaciously adhered to the underside of the base layer, the third layer being equal in size and stress condition to the covering layer and having transmittance characteristics substantially the same as the base layer.
Claim 10
Dependent Claim
37 words
The glass-ceramic cooking plate according to claim 1 wherein the third layer and the covering layer are both applied universally to the base layer under sufficient pressure to impact a permanent compressive stress to the glass-ceramic plate.
Claim 11
Dependent Claim
25 words
The glass-ceramic cooking plate according to claim 9 wherein the compressive stress is achieved by an ion exchange process after crystallization of the base layer.
Claim 12
Dependent Claim
35 words
The glass-ceramic cooking plate according to claim 9 wherein the compressive stress is attained through the application of enamel layers which have been fused onto the base layer after the crystallization of the base layer.
Claim 13
Dependent Claim
54 words
The glass-ceramic cooking plate according to claim 9 wherein the compressive stress through the three layer glass-ceramic surface is attained by treating the base layer to effect a change in the physical makeup of an additive combined with the base layer during formation thereof in the region of the surfaces of the base layer.
Claim 14
Dependent Claim
107 words
A glass-ceramic cooking plate horizontally disposed for use with heating elements on the underside of the plate, the heat energy from the heating elements being transmitted through the plate to the upper surface of the plate, said plate comprising a glass-ceramic base layer having a transmittance value of greater than 80% for radiation whose wave length is from 0.7 to 2.0 microns and a covering layer of at most one-tenth the thickness of the base layer tenaciously adhered to the top of the base layer, the covering layer having a transmittance value of less than 20% for radiation whose wave length is from 0.7 to 2 microns.
Claim 15
Dependent Claim
107 words
A glass-ceramic cooking plate horizontally disposed for use with heating elements on the underside of the plate, the heat energy from the heating elements being transmitted through the plate to the upper surface of the plate, said plate comprising a glass-ceramic base layer having a transmittance value of greater than 80% for radiation whose wave length is from 0.7 to 2.0 microns and a covering layer of at most one-tenth the thickness of the base layer tenaciously adhered to the top of the base layer, the covering layer having a transmittance value of less than 20% for radiation whose wave length is from 0.7 to 2 microns.
Claim 16
Dependent Claim
40 words
The glass-ceramic cooking plate according to claim 13 wherein the base layer has a thickness of from 3.0 to 5.5 mm and a transmittance value of greater than 90% for radiation having a wave length between 0.7 and 2.0 microns.
Claim 17
Dependent Claim
57 words
The glass-ceramic plate according to claim 13 wherein the covering layer has a transmittance value of less than 10% for radiation having a wave length of between 0.7 and 2 microns and is constructed of an oxide selected from the group consisting of cobalt oxide and manganese oxide fused into the upper surface of the base layer.
Claim 18
Dependent Claim
43 words
The glass-ceramic cooking plate according to claim 15 further comprising a third layer tenaciously adhered to the underside of the base layer having stress characteristics substantially the same as the covering layer while having transmittance characteristics substantially the same as the base layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-11-07 | 1981-05-09 | 1981-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-11-07 | 1985-05-09 | 1985-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-11-07 | 1989-05-09 | 1989-11-08 | $7700.00 | Window Closed / Lapsed |