Process for preparation of thermosetting resin powder paints
Assignee: Dai Nippon Toryo Co Ltd
•
Filing: 1975-07-07
•
Granted: 1977-11-01
•
Expires: 1995-07-07
Abstract
Abstract A process for the preparation of thermosetting resin powder paints comprising the steps of extruding a melt of a resinous composition for a thermosetting powder paint, continuously cooling the composition and forming it into a sheet, and pulverizing the formed sheet. Air blasting nozzles are directed at the sheet while it is on the cooling rolls. The adherence between the sheet and the rolls is improved, and the air blasting nozzles provide an auxiliary means for cooling the sheet.
Inventors
- 👤 Ryoji Izumi
- 👤 Shoji Kobayashi
- 👤 Toshiharu Ono
- 👤 Toru Shirato
- 👤 Akiyoshi Fujii
- 👤 Tadashi Okihara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 03:59
CPC Classifications
B; B29; B29B; B29B9/00; B29B9/02; B29B9/04; B29B9/12; B29C; B29C48/00; B29C48/001; B29C48/0011; B29C48/03; B29C48/06; B29C48/25; B29C48/88; B29C48/911; B29C48/9135; B29C48/914; B29C48/915; B29C48/917; B29C48/92; C; C09; C09D; C09D5/00; C09D5/03; B29C2948/00; B29C2948/92; B29C2948/92504; B29C2948/92704
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
202 words
A process for the production of thermosetting resin powder paints which consists of the steps (1) melting and kneading a thermosetting resinous composition which contains curing agents at a temperature higher than the softening point but lower than the curing point of the resinous composition, extruding said thermosetting resinous composition for a powder paint in the molten state from an extruder die, at temperature between 90° C and 140° C, at a rate between 100 and 600 kg/hr. (2) continuously cooling the extruded composition and forming it into a sheet under conditions to avoid curing of the resin by means of a plurality of rolls including press rolls for rolling the composition into a sheet, cooling feed rolls and withdrawal take-up rolls disposed in this order, applying air from air blasting nozzles, which nozzles are opened to face the entire surfaces of the cooling feed rolls, at a distance from the cooling feed rolls of between 20 and 150mm, at an air rate of at least 30m/sec, at a pressure of between 1.5 and4kg/cm 2 while controlling the sheet temperature at the terminal portion of the withdrawal take-up rolls between room temperature and 50° C, and (3) pulverizing the so formed sheet.
Claim 2
Dependent Claim
202 words
A process for the production of thermosetting resin powder paints which consists of the steps (1) melting and kneading a thermosetting resinous composition which contains curing agents at a temperature higher than the softening point but lower than the curing point of the resinous composition, extruding said thermosetting resinous composition for a powder paint in the molten state from an extruder die, at temperature between 90° C and 140° C, at a rate between 100 and 600 kg/hr. (2) continuously cooling the extruded composition and forming it into a sheet under conditions to avoid curing of the resin by means of a plurality of rolls including press rolls for rolling the composition into a sheet, cooling feed rolls and withdrawal take-up rolls disposed in this order, applying air from air blasting nozzles, which nozzles are opened to face the entire surfaces of the cooling feed rolls, at a distance from the cooling feed rolls of between 20 and 150mm, at an air rate of at least 30m/sec, at a pressure of between 1.5 and4kg/cm 2 while controlling the sheet temperature at the terminal portion of the withdrawal take-up rolls between room temperature and 50° C, and (3) pulverizing the so formed sheet.
Claim 3
Dependent Claim
28 words
A process according to claim 1 wherein the transportation rate of the sheet is controlled at a rate of 5 to 10 m/min. at the withdrawal take-up rolls.
Claim 4
Dependent Claim
21 words
A process according to claim 1 wherein the cooling temperature of the cooling rolls is between 15° C and 30° C.
Claim 5
Dependent Claim
20 words
The process according to claim 1 wherein the entire sheet is contacted with the surface of the cooling feed rolls.
References Cited (Backward Citations)
US3004296A
Cited
US2582294A
Cited
US2534291A
Cited
US3090076A
Cited
US3382295A
Cited
GB1079262A
Cited
US3725340A
Cited
US3732349A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-31 | 1981-05-02 | 1981-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-31 | 1985-05-02 | 1985-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-31 | 1989-05-02 | 1989-11-01 | $7700.00 | Window Closed / Lapsed |