Method for sintering ceramics
Assignee: Ford Motor Co
•
Filing: 1976-02-18
•
Granted: 1977-11-01
•
Expires: 1996-02-18
Abstract
Abstract A method of sintering green ceramic bodies comprised of polycrystalline bi- or multi-metal oxides comprising: (A) encapsulating the body to be sintered in a chamber having (i) an inner wall portion comprised of a sintered polycrystalline bi- or multi-metal oxide composition of the same type as the body being sintered such that upon heating during the sintering process volatile metal oxide constituents of said composition create an atmosphere of said constituents which surrounds the body being sintered and (ii) an outer wall portion comprised of a substantially impervious sintered ceramic which is essentially nonreactive with said polycrystalline bi- or multi-metal oxides; and (B) heating the chamber with said body encapsulated therein to a temperature and for a time necessary to sinter said body to the desired density.
Inventors
- 👤 James N. Lingscheit
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 21:52
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/113; C04B35/622; C04B35/64; H; H01; H01M; H01M10/00; H01M10/36; H01M10/39; H01M10/3909; H01M10/3918; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
159 words
A method for sintering a green ceramic body comprised of polycrystalline bi- or multi-metal oxides comprising: A. encapsulating said body in a chamber having inner and outer wall portions, said inner wall portion being i. adjacent to said body being sintered and ii. comprised of a sintered polycrystalline bi- or multi-metal oxide composition of the same type as said body being sintered such that upon heating during the sintering process volatile metal oxide constituents of said composition create an atmosphere of said constituents which surrounds said body being sintered, and said outer wall portion being i. adjacent to, contiguous with and integrally bonded to the entire outer surface of said inner wall portion and ii. comprised of a substantially impervious sintered ceramic which is essentially nonreactive with said polycrystalline bi- or multi-metal oxides; and B. heating said chamber with said body encapsulated therein to a temperature and for a time necessary to sinter said body to the desired density.
Claim 2
Independent Claim
159 words
A method for sintering a green ceramic body comprised of polycrystalline bi- or multi-metal oxides comprising: A. encapsulating said body in a chamber having inner and outer wall portions, said inner wall portion being i. adjacent to said body being sintered and ii. comprised of a sintered polycrystalline bi- or multi-metal oxide composition of the same type as said body being sintered such that upon heating during the sintering process volatile metal oxide constituents of said composition create an atmosphere of said constituents which surrounds said body being sintered, and said outer wall portion being i. adjacent to, contiguous with and integrally bonded to the entire outer surface of said inner wall portion and ii. comprised of a substantially impervious sintered ceramic which is essentially nonreactive with said polycrystalline bi- or multi-metal oxides; and B. heating said chamber with said body encapsulated therein to a temperature and for a time necessary to sinter said body to the desired density.
Claim 3
Dependent Claim
33 words
A process in accordance with claim 1 wherein said body being sintered and said inner wall portion of said chamber are comprised of a composition selected from beta-type alumina and modified beta-type alumina.
Claim 4
Dependent Claim
20 words
A process in accordance with claim 2 wherein said outer wall portion of said chamber is comprised of alpha alumina.
Claim 5
Dependent Claim
31 words
A process in accordance with claim 2 wherein said body being sintered and said inner wall portion of said chamber are comprised of a composition selected from β"-alumina and modified β"-alumina.
Claim 6
Dependent Claim
20 words
A process in accordance with claim 4 wherein said outer wall portion of said chamber is comprised of alpha alumina.
Claim 7
Dependent Claim
97 words
A process in accordance with claim 1 wherein said chamber has been formed by cladding a sintered polycrystalline bi- or multi-metal oxide inner wall portion with said outer wall portion by bonding said sintered inner wall portion to a sintered impervious ceramic body section of said outer wall portion with a ceramic cement comprised of the same chemical composition as said ceramic body section and heating the composite to sinter said cement such that said outer wall portion, which consists of said ceramic body section and said sintered cement, is integrally bonded to said inner wall portion.
Claim 8
Dependent Claim
31 words
A process in accordance with claim 6 wherein said ceramic body section of said outer wall portion and said sintered ceramic cement of said outer wall portion are comprised of alpha-alumina.
Claim 9
Dependent Claim
35 words
A process in accordance with claim 1 wherein said chamber is a tube, the open end of which is sealed with an essentially impervious sintered ceramic of the same composition as said outer wall portion.
Claim 10
Dependent Claim
25 words
A process in accordance with claim 1 wherein said chamber comprises a furnace muffle through which said ceramic body being sintered may be moved continuously.
Claim 11
Dependent Claim
57 words
A process in accordance with claim 9 wherein said chamber comprises the longitudinally extending walls of said furnace muffle and encapsulation of said body is completed by substantially impervious ceramic bodies of the same composition as said outer wall portion, which bodies are adapted to move through said furnace muffle with said green ceramic body confined therebetween.
Claim 12
Dependent Claim
14 words
A process in accordance with claim 1 wherein said green ceramic body is tubular.
Claim 13
Dependent Claim
14 words
A process in accordance with claim 1 wherein said green ceramic body is rod-like.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-31 | 1981-05-02 | 1981-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-31 | 1985-05-02 | 1985-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-31 | 1989-05-02 | 1989-11-01 | $7700.00 | Window Closed / Lapsed |