Production of β-alumina ceramic tubes
Assignee: Electricity Council
•
Filing: 1972-05-09
•
Granted: 1976-04-13
•
Expires: 1992-05-09
Abstract
Abstract Tubes of beta alumina ceramic are produced by forming a tube of compressed finely divided powder material, e.g. finely divided crystalline beta alumina or finely divided powders which together will form on heating the required ceramic. This tube is passed at a uniform rate through an electric inductive furnace of open-ended tubular form having a short zone at 1600 DEG -1900 DEG C so that the tube is rapidly raised to the sintering temperature and, after a short period in the sintering zone is rapidly cooled.
Inventors
- 👤 Ivor Wynn Jones
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 03:49
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/01; C04B35/10; C04B35/111; C04B35/113; Y; Y10; Y10S; Y10S65/00; Y10S65/04
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
180 words
A method of producing a tube of β alumina ceramic comprising the steps of compressing into the shape of a tube powdered β alumina ceramic or a powdered mixture of materials which, on heating, produce a β alumina ceramic and then traversing this tube in its axial direction at a uniform speed v through a furnace having a temperature profile increasing in temperature from one end to a maximum sintering temperature between 1600°C and 1900°C and decreasing towards the other end, the length l of the sintering zone which is within 10°C of the maximum temperature in the furnace and the velocity vr at which the tube is traversed being such that the time l/vr during which any point on the tube is in the sintering zone is between 12 seconds and 2 minutes, the temperature profile of the furnace and the rate of traverse of the tube being such that a point on the tube is heated up to the sintering temperature and cooled from the sintering temperature at a rate between 200°C per minute and 2400°C per minute.
Claim 2
Independent Claim
180 words
A method of producing a tube of β alumina ceramic comprising the steps of compressing into the shape of a tube powdered β alumina ceramic or a powdered mixture of materials which, on heating, produce a β alumina ceramic and then traversing this tube in its axial direction at a uniform speed v through a furnace having a temperature profile increasing in temperature from one end to a maximum sintering temperature between 1600°C and 1900°C and decreasing towards the other end, the length l of the sintering zone which is within 10°C of the maximum temperature in the furnace and the velocity vr at which the tube is traversed being such that the time l/vr during which any point on the tube is in the sintering zone is between 12 seconds and 2 minutes, the temperature profile of the furnace and the rate of traverse of the tube being such that a point on the tube is heated up to the sintering temperature and cooled from the sintering temperature at a rate between 200°C per minute and 2400°C per minute.
Claim 3
Dependent Claim
36 words
A method as claimed in claim 1 wherein the powdered mixture is formed of a mixture of 5 to 10% by weight of sodium oxide, 0-5% magnesium oxide or lithium oxide and the balance aluminium oxide.
Claim 4
Dependent Claim
35 words
A method as claimed in claim 1 wherein the powdered mixture is formed of α alumina and compounds of sodium and of magnesium and/or lithium which together will form on heating the required ceramic composition.
Claim 5
Dependent Claim
25 words
A method as claimed in claim 1 wherein the powder is formed of a mixture of α alumina, sodium aluminate, lithium carbonate and magnesium oxide.
Claim 6
Dependent Claim
47 words
A method as claimed in claim 1 wherein said maximum temperature is in the range 1740°-1750°C and wherein said tube has a mass per unit length of 1 to 3 gms per cm and wherein the speed of traverse is between 25 and 100 mm per minute.
Claim 7
Dependent Claim
45 words
A method as claimed in claim 1 wherein said maximum temperature is in the range 1770°-1780°C and wherein said tube has a mass per unit length of 1-3 gms per cm and wherein the speed of traverse is between 25 and 150 mm per minute.
Claim 8
Dependent Claim
45 words
A method as claimed in claim 1 wherein said maximum temperature is in the range 1820°-1830°C and wherein said tube has a mass per unit length of 1-3 gms per cm and wherein the speed of traverse is between 25 and 200 mm per minute.
Claim 9
Dependent Claim
27 words
A method as claimed in claim 1 wherein the furnace is cylindrical and has a diameter between one-fourth and one-half the length l of the sintering zone.
References Cited (Backward Citations)
US1138674A
Cited
US2968551A
Cited
US3533143A
Cited
US3468719A
Cited
US3446677A
Cited
US3475225A
Cited
US3625773A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-13 | 1979-10-13 | 1980-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-13 | 1983-10-13 | 1984-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-13 | 1987-10-13 | 1988-04-13 | $7700.00 | Window Closed / Lapsed |