US4056269A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Homogeneous molded golf ball
Assignee: Kidde Inc
•
Filing: 1972-05-04
•
Granted: 1977-11-01
•
Expires: 1992-05-04
Abstract
Abstract In a homogeneous molded golf ball comprising a filled elastomer highly cross-linked into a three dimensional network with long, flexible cross-links formed of a polymerized cross-linking monomer, the improvement which comprises using as said cross-linking monomer a metal-containing cross-linkable monomer whereby said comonomer simultaneously functions as said filler at least in part. The preferred elastomer is cis-polybutadiene. The metal-containing cross-linkable monomer can be formed in situ or added as such and preferably comprises a salt of at least one metal selected from the group consisting of zinc, magnesium and calcium, and at least one acid selected from the group consisting of methacrylic, acrylic, cinnamic, acotinic, crotonic, vinylacetic, itaconic, styrenesulfonic and benzoylacrylic acids. Additional filler may be added to adjust the density to the desired value. The composition is preferably preheated prior to molding and produces golf balls of superior properties with respect to durability, cannon life, sound and distance properties.
Inventors
- 👤 Duncan H. Pollitt
- 👤 Murray H. Reich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:22
CPC Classifications
C; C08; C08F; C08F279/00; C08F279/02; A; A63; A63B; A63B37/00; A63B37/0003; A63B45/00; Y; Y10; Y10S; Y10S273/00; Y10S273/10
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
130 words
In a homogeneous molded golf ball having the density and click and rebound required in a golf ball and comprising filled cis-polybutadiene elastomer highly cross-linked into a three dimensional network with long, flexible cross-links formed of a polymerized cross-linking monomer, the improvement wherein said cross-linking monomer comprises a polyvalent metal salt of an unsaturated acid and is present in about 0.046 to 0.41 equivalents per mole of elastomer base whereby said comonomer simultaneously functions as said filler at least in part, said ball in addition to said filler-functioning cross-linking monomer containing up to about 30 parts of a further filler per 100 parts by weight of said elastomer, the amount of said further filler being sufficient to impart to said golf ball a weight of about 1.500 to 1.620 ounces.
Claim 2
Dependent Claim
130 words
In a homogeneous molded golf ball having the density and click and rebound required in a golf ball and comprising filled cis-polybutadiene elastomer highly cross-linked into a three dimensional network with long, flexible cross-links formed of a polymerized cross-linking monomer, the improvement wherein said cross-linking monomer comprises a polyvalent metal salt of an unsaturated acid and is present in about 0.046 to 0.41 equivalents per mole of elastomer base whereby said comonomer simultaneously functions as said filler at least in part, said ball in addition to said filler-functioning cross-linking monomer containing up to about 30 parts of a further filler per 100 parts by weight of said elastomer, the amount of said further filler being sufficient to impart to said golf ball a weight of about 1.500 to 1.620 ounces.
Claim 3
Dependent Claim
26 words
A golf ball according to claim 1 wherein said filler is present in up to about 15 parts per 100 parts by weight of said elastomer.
Claim 4
Dependent Claim
51 words
A golf ball according to claim 1 wherein said polyvalent metal salt comprises a salt of at least one metal selected from the group consisting of zinc, magnesium and calcium, and at least one acid selected from the group consisting of methacrylic, acrylic, cinnamic, acotinic, crotonic, vinylacetic, itaconic, and benzoylacrylic acids.
Claim 5
Dependent Claim
30 words
A golf ball according to claim 1 wherein said polyvalent metal salt comprises zinc dimethacrylate present in about 20 to 50 parts per 100 parts by weight of the polybutadiene.
Claim 6
Dependent Claim
30 words
A golf ball according to claim 4 wherein the composition additionally contains up to about 15 parts by weight of zinc oxide based per 100 parts by weight of polybutadiene.
Claim 7
Dependent Claim
83 words
In the process for producing a homogeneous molded golf ball comprising filled cis-polybutadiene elastomer highly cross-linked into a three dimensional network with long flexible cross-links comprising molding an intimate mixture of cis-polybutadiene, a cross-linkable monomer, a metal containing filler, and a free radical catalyst, the improvement which comprises using as said cross-linkable monomer about 0.046 to 0.41 moles per mole of elastomer base of a polyvalent metal salt of an unsaturated acid whereby it simultaneously functions as said filler at least in part.
Claim 8
Dependent Claim
83 words
In the process for producing a homogeneous molded golf ball comprising filled cis-polybutadiene elastomer highly cross-linked into a three dimensional network with long flexible cross-links comprising molding an intimate mixture of cis-polybutadiene, a cross-linkable monomer, a metal containing filler, and a free radical catalyst, the improvement which comprises using as said cross-linkable monomer about 0.046 to 0.41 moles per mole of elastomer base of a polyvalent metal salt of an unsaturated acid whereby it simultaneously functions as said filler at least in part.
Claim 9
Dependent Claim
57 words
The process according to claim 6, wherein said intimate mixture is formed by mixing said elastomer with a cross-linkable monomeric acid and with at least the stoichiometric amount of a metal-containing compound reactive with said monomeric acid under the conditions of mixing or molding whereby said polyvalent metal salt of an unsaturated acid is formed in situ.
Claim 10
Dependent Claim
32 words
The process according to claim 7, wherein said metal-containing compound is used in an excess of the stoichiometric amount up to about 30 parts by weight per 100 parts of the elastomer.
Claim 11
Dependent Claim
32 words
The process according to claim 7, wherein said metal-containing compound is used in an excess of the stoichiometric amount up to about 15 parts by weight per 100 parts of the elastomer.
Claim 12
Dependent Claim
50 words
The process according to claim 6 wherein said polyvalent metal salt comprises a salt of at least one metal selected from the group consisting of zinc, magnesium and calcium, and at least one acid selected from the group consisting of methacrylic, acrylic, cinnamic, acotinic, crotonic, vinylacetic, itaconic and benzoylacrylic acids.
Claim 13
Dependent Claim
61 words
The process according to claim 8 wherein the monomeric acid comprises methacrylic acid and said metal-containing compound is zinc oxide present in amount sufficient to form about 20 to 50 parts of zinc dimethacrylate based on 100 parts by weight of polybutadiene and to leave up to about 15 parts of unreacted zinc oxide per 100 parts by weight of polybutadiene.
Claim 14
Dependent Claim
75 words
A solid unitary golf ball prepared from a composition comprising 100 parts of polybutadiene having a cis 1,4 polybutadiene content of at least 40% and a divalent metal salt of a monethylenically unsaturated carboxylic acid present in sufficient quantity to cross-link said polybutadiene and form said solid unitary golf ball when said composition is cured in a standard golf ball mold at a temperature between 266° and 392° F. for from 1 to 50 minutes.
Claim 15
Dependent Claim
75 words
A solid unitary golf ball prepared from a composition comprising 100 parts of polybutadiene having a cis 1,4 polybutadiene content of at least 40% and a divalent metal salt of a monethylenically unsaturated carboxylic acid present in sufficient quantity to cross-link said polybutadiene and form said solid unitary golf ball when said composition is cured in a standard golf ball mold at a temperature between 266° and 392° F. for from 1 to 50 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-31 | 1981-05-02 | 1981-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-31 | 1985-05-02 | 1985-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-31 | 1989-05-02 | 1989-11-01 | $7700.00 | Window Closed / Lapsed |