Assignee: United Aircraft Products Inc
•
Filing: 1976-09-15
•
Granted: 1977-10-25
•
Expires: 1996-09-15
Abstract
Abstract A plating preparation method in which a nickel part is placed in an electrolyte bath of such acid concentration and such temperature as to promote thorough etching of the part surface and in which an etched part is allowed to soak in the same electrolyte bath for a period of time sufficient to dissolve formed metallic oxides. A coating of a base material is applied to the part following removal from the etching bath, the base material achieving a close intimate contact with the part surface and penetrating and interlocking with recessed areas of such surface.
Inventors
- 👤 Ivan Gene Freshcorn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:42
CPC Classifications
C; C25; C25D; C25D5/00; C25D5/34; C25D5/38; C25D5/40
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
147 words
A method of preparing a nickel alloy part for plating, including the steps of immersing the part in an electrolyte bath, connecting the part as the anode in an electric circuit which when energized causes current flow to take place from said part outward into the bath, energizing said circuit and establishing and maintaining said current flow for a period of time sufficient to etch the part surface, etched metal being oxidized during the period of current flow, discontinuing current flow and after the current flow has been discontinued allowing the part to remain soaking in the same said electrolyte bath for a period of time sufficient to dissolve formed metallic oxides, removing the part from said bath, and while said part is substantially free of metallic oxides depositing on the surface thereof a plating base material penetrating and interlocking with etched surface portions of said part.
Claim 2
Independent Claim
147 words
A method of preparing a nickel alloy part for plating, including the steps of immersing the part in an electrolyte bath, connecting the part as the anode in an electric circuit which when energized causes current flow to take place from said part outward into the bath, energizing said circuit and establishing and maintaining said current flow for a period of time sufficient to etch the part surface, etched metal being oxidized during the period of current flow, discontinuing current flow and after the current flow has been discontinued allowing the part to remain soaking in the same said electrolyte bath for a period of time sufficient to dissolve formed metallic oxides, removing the part from said bath, and while said part is substantially free of metallic oxides depositing on the surface thereof a plating base material penetrating and interlocking with etched surface portions of said part.
Claim 3
Dependent Claim
39 words
A method according to claim 1, wherein said electrolyte bath is composed of water and 40% to 50% by volume of concentrated acid, the bath temperature being established and maintained in a range of 140° F. to 150° F.
Claim 4
Dependent Claim
42 words
A method according to claim 2, wherein the part is allowed to soak in said bath for a period of time on the order of 4 minutes after shutting off the electric current flow and before removing the part from the bath.
Claim 5
Dependent Claim
24 words
A method according to claim 2, wherein the electric current flow is maintained for a period of time on the order of 2 minutes.
Claim 6
Dependent Claim
61 words
A method according to claim 2, wherein the electric current flow is maintained for a period of time on the order of 2 minutes, and wherein the part is allowed to soak in said bath for a period of time on the order of 4 minutes after shutting off the electric current flow and before removing the part from the bath.
Claim 7
Dependent Claim
13 words
A method according to claim 2, wherein said concentrated acid is sulfuric acid.
Claim 8
Dependent Claim
22 words
A method according to claim 2, wherein said deposited base material is substantially pure nickel and is applied in an electrodepositing operation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-24 | 1981-04-25 | 1981-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-24 | 1985-04-25 | 1985-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-24 | 1989-04-25 | 1989-10-25 | $7700.00 | Window Closed / Lapsed |