Patent US4055457A successfully refreshed from Google Patents.
US4055457A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for growing absorption-free alkali metal halide single crystals
Assignee: Solon Technologies Inc
•
Filing: 1976-08-20
•
Granted: 1977-10-25
•
Expires: 1996-08-20
Abstract
Abstract Large ultra-pure, prism-quality essentially single crystal boules and ingots of alkali metal chlorides and alkali metal bromides are grown by the methods of Kyropoulos and Stockbarger. Optically single crystals of these alkali metal halides are clear optical bodies free of haze throughout. A typical Kyropoulos grown boule of KBr of this invention is also absorption-free, and has cleavage or crystallographic planes which deviate from parallel by 1 DEG to 3 DEG per inch. By 'absorption-free' is meant freedom of absorption at 7.2 microns ( mu ) due to nitrate, at 9.5-11 mu due to silicate, and at between 8 and 9 mu due to sulfate, which are the most difficult to control but as the term implies the bodies are also free of infrared absorption for impurities such as CO3-2, PO4-3, OH-, BO2-, SH-, CNO-, HCO3-, etc., which are easily avoided by use of good commercially available growth stock.
Inventors
- 👤 Carl F. Swinehart
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 20:17
CPC Classifications
C; C30; C30B; C30B17/00; C30B11/00; C30B29/00; C30B29/10; C30B29/12
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
152 words
In a Stockbarger or Kyropoulos method of growing an essentially single crystal ingot from a melt consisting of a bromide, chloride or mixture thereof, of an alkali metal of Group 1A of the Periodic Table, said melt contaminated with a silicate impurity, the improvement comprising confining said melt in a siliceous crucible, contacting said melt with a metal silicate-forming scavenger selected from the group consisting of (a) a bromide of a Group IIA metal when said melt is predominantly a bromide, (b) a chloride of a Group IIA metal when said melt is predominantly a chloride, and (c) a rare earth metal selected from europium, ytterbium and samarium added to said melt in melt-soluble form, reacting said scavenger with the silicate impurity in said melt, and removing the silicate impurity by depositing the same as a coating on the crucible to produce an ingot free of infrared absorption due to silicate impurity.
Claim 2
Dependent Claim
152 words
In a Stockbarger or Kyropoulos method of growing an essentially single crystal ingot from a melt consisting of a bromide, chloride or mixture thereof, of an alkali metal of Group 1A of the Periodic Table, said melt contaminated with a silicate impurity, the improvement comprising confining said melt in a siliceous crucible, contacting said melt with a metal silicate-forming scavenger selected from the group consisting of (a) a bromide of a Group IIA metal when said melt is predominantly a bromide, (b) a chloride of a Group IIA metal when said melt is predominantly a chloride, and (c) a rare earth metal selected from europium, ytterbium and samarium added to said melt in melt-soluble form, reacting said scavenger with the silicate impurity in said melt, and removing the silicate impurity by depositing the same as a coating on the crucible to produce an ingot free of infrared absorption due to silicate impurity.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein said melt is selected from the group consisting of potassium chloride, potassium bromide and mixtures thereof.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein said Group IIA metal is selected from the group consisting of barium and calcium.
Claim 5
Dependent Claim
196 words
In a Kyropoulos method of growing essentially single crystal boules successively from a melt contaminated with silicate, nitrate, nitrite and sulfate impurities, said melt consisting of a bromide, chloride or mixtures thereof of an alkali metal of Group IA of the Periodic Table, the improvement comprising confining said melt in a siliceous crucible, maintaining less than about 20 ppm of unwanted Group IA and less than about 10 ppm of Group IIA metal in said melt, contacting said melt with a metal silicate-forming scavenger selected from the group consisting of (a) a bromide of a Group IIA metal when said melt is predominantly a bromide, (b) a chloride of a Group IIA metal when said melt is predominantly a chloride, and (c) a rare earth metal selected from europium, ytterbium and samarium added to said melt in melt-soluble form, reacting said scavenger with the silicate impurity content in said melt, removing silicate impurity from said melt by depositing a silicate containing coating on said crucible, and, contacting said melt with bromine or chlorine in elemental form, so as to grow a haze-free ingot free of infrared absorption bands due to silicate, nitrate, nitrite and sulfate impurities.
Claim 6
Dependent Claim
196 words
In a Kyropoulos method of growing essentially single crystal boules successively from a melt contaminated with silicate, nitrate, nitrite and sulfate impurities, said melt consisting of a bromide, chloride or mixtures thereof of an alkali metal of Group IA of the Periodic Table, the improvement comprising confining said melt in a siliceous crucible, maintaining less than about 20 ppm of unwanted Group IA and less than about 10 ppm of Group IIA metal in said melt, contacting said melt with a metal silicate-forming scavenger selected from the group consisting of (a) a bromide of a Group IIA metal when said melt is predominantly a bromide, (b) a chloride of a Group IIA metal when said melt is predominantly a chloride, and (c) a rare earth metal selected from europium, ytterbium and samarium added to said melt in melt-soluble form, reacting said scavenger with the silicate impurity content in said melt, removing silicate impurity from said melt by depositing a silicate containing coating on said crucible, and, contacting said melt with bromine or chlorine in elemental form, so as to grow a haze-free ingot free of infrared absorption bands due to silicate, nitrate, nitrite and sulfate impurities.
References Cited (Backward Citations)
US475576A
Cited
GB492722A
Cited
GB940917A
Cited
GB1137582A
Cited
GB1123991A
Cited
US3837882A
Cited
US3840651A
Cited
US3969491A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-24 | 1981-04-25 | 1981-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-24 | 1985-04-25 | 1985-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-24 | 1989-04-25 | 1989-10-25 | $7700.00 | Window Closed / Lapsed |