Additives process for producing plated holes in printed circuit elements
Assignee: EIDP Inc
•
Filing: 1976-12-22
•
Granted: 1977-10-18
•
Expires: 1996-12-22
Abstract
Abstract An improved process for preparing printed circuit boards whereby through-holes are introduced into an element comprising a substrate, a photosensitive resist layer, and a superposed, strippable support. The through-holes are catalyzed prior to removal of the strippable support. After exposure the imaged photoresist is developed, the catalyzed-through-holes are electrolessly plated and the printed circuit is prepared using the developed image. Single sided, two or more layered printed circuit boards with plated-through-holes and interconnections can be prepared by this process.
Inventors
- 👤 Robert William Peiffer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 18:14
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1603; C23C18/1607; C23C18/1608; H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/182; H05K3/184; H05K3/40; H05K3/42; H05K3/425; H05K3/427; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/0353; H05K1/0373; H05K2201/00; H05K2201/02; H05K2201/0203; H05K2201/0206; H05K2201/0236; H05K2203/00; H05K2203/05; H05K2203/0502; H05K2203/0525; H05K2203/0562; H05K2203/0577; H05K2203/13; H05K2203/1377; H05K2203/1383; H05K2203/14; H05K2203/1415; H05K3/108; H05K3/426
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
129 words
A process for preparing printed circuit boards having plated through-holes from a photosensitive element which comprises a substrate bearing, in order, a photosensitive layer and a strippable support capable of transmitting actinic radiation, wherein the photosensitive layer is imagewise exposed, the strippable support is removed, the imaged photosensitive layer is developed, and the developed image is converted into a conductive printed circuit, which comprises, either prior to or after exposure, the steps of: 1. introducing through-holes into the element; and then 2. applying to the through-holes an ahderent material which is catalytic to electroless plating or can be made catalytic by a development step; 3. removing the strippable support from the photosensitive layer; and 4. applying electroless plating solution to the catalyzed through-holes to produce an electrically conductive through-hole.
Claim 2
Dependent Claim
129 words
A process for preparing printed circuit boards having plated through-holes from a photosensitive element which comprises a substrate bearing, in order, a photosensitive layer and a strippable support capable of transmitting actinic radiation, wherein the photosensitive layer is imagewise exposed, the strippable support is removed, the imaged photosensitive layer is developed, and the developed image is converted into a conductive printed circuit, which comprises, either prior to or after exposure, the steps of: 1. introducing through-holes into the element; and then 2. applying to the through-holes an ahderent material which is catalytic to electroless plating or can be made catalytic by a development step; 3. removing the strippable support from the photosensitive layer; and 4. applying electroless plating solution to the catalyzed through-holes to produce an electrically conductive through-hole.
Claim 3
Dependent Claim
18 words
A process according to claim 1 wherein the substrate has a printed circuit pattern on its reverse side.
Claim 4
Dependent Claim
19 words
A process according to claim 1 wherein the adherent material is applied to the holes from the support surface.
Claim 5
Dependent Claim
32 words
A process according to claim 1 wherein the photosensitive element is prepared by coating the substrate with a liquid to form a photosensitive layer and laminating to said layer the strippable support.
Claim 6
Dependent Claim
24 words
A process according to claim 1 wherein the photosensitive element is prepared by laminating the surface of the supported photosensitive layer to the substrate.
Claim 7
Dependent Claim
15 words
A process according to claim 5 wherein the photosensitive layer is an adherent photohardenable layer.
Claim 8
Dependent Claim
92 words
A process according to claim 6 wherein the support is removed in step (3) without transfer thereto of either exposed or underexposed areas of the layer; after step (3) and prior to step (4) the imaged layer is developed by applying to the surface of the layer and the holes therein finely divided material catalytic to electroless plating which adheres to the underexposed areas to produce a catalytic image; and the electroless plating solution is applied in step (4) to the catalytic image and hole surface to produce an electrically conductive circuit.
Claim 9
Dependent Claim
51 words
A process according to claim 1 wherein the photosensitive element comprises a substrate having a surface which is electrically conductive or catalytic to electroless plating bearing a photosensitive resist forming layer which upon imagewise exposure to actinic radiation imagewise produces areas which are removable from the layer, and a strippable support.
Claim 10
Dependent Claim
83 words
A process according to claim 8 wherein the substrate surface is electrically conductive and wherein the image layer is developed with or subsequent to step (3) by removing the removable image areas to form a resist image on the substrate; electroless plating solution is applied in step (4) to the holes and exposed substrate surface to form an electrically conductive surface thereon; the resist image is removed to expose protected electrically conductive substrate areas; and the protected electrically conductive substrate areas are removed.
Claim 11
Dependent Claim
64 words
A process according to claim 8 wherein substrate surface is catalytic to electroless plating and wherein the image layer is developed during or subsequent to step (3) by removing the removable image areas to form a resist image on the catalytic substrate; electroless plating solution is applied in step (4) to the holes and catalytic substrate surface to form an electrically conductive surface thereon.
Claim 12
Dependent Claim
58 words
A process according to claim 9 wherein the electrically conductive surface is copper or a copper clad substrate and wherein after step (4) and before removing the resist image depositing additional copper on the exposed copper surface by immersing in a plating bath; and after removing the resist image etching away the unplated copper areas of the substrate.
Claim 13
Dependent Claim
126 words
A process for preparing multilayered printed circuit boards with plated-through-holes using photohardenable elements having an adherent, photohardenable layer and a strippable support that transmits actinic radiation which comprises: 1. laminating the photohardenable surface of a photohardenable element to a substrate to form a laminated element; 2. exposing the laminated element imagewise through the support to actinic radiation; 3. removing the strippable support; 4. applying finely devided catalytic material to the exposed surface to form a catalytic image; and 5. treating the catalytic image with an electroless plating solution to form a printed circuit substrate; 6. laminating to the resultant printed circuit substrate the photohardenable surface of a photohardenable element; then in either order; 7. exposing the laminated element imagewise through the support to actinic radiation; and
Claim 14
Dependent Claim
126 words
A process for preparing multilayered printed circuit boards with plated-through-holes using photohardenable elements having an adherent, photohardenable layer and a strippable support that transmits actinic radiation which comprises: 1. laminating the photohardenable surface of a photohardenable element to a substrate to form a laminated element; 2. exposing the laminated element imagewise through the support to actinic radiation; 3. removing the strippable support; 4. applying finely devided catalytic material to the exposed surface to form a catalytic image; and 5. treating the catalytic image with an electroless plating solution to form a printed circuit substrate; 6. laminating to the resultant printed circuit substrate the photohardenable surface of a photohardenable element; then in either order; 7. exposing the laminated element imagewise through the support to actinic radiation; and
Claim 15
Dependent Claim
67 words
introducing activated through-holes into the laminated element and applying to the holes an adhesive or an adherent material catalytic to electroless plating; then 9. removing the strippable support; 10. applying finely divided catalytic material to the exposed surface and the holes to form a catalytic image; and 11. treating the catalytic image and holes with an electroless plating solution to form a conductive printed circuit and holes.
Claim 16
Dependent Claim
67 words
introducing activated through-holes into the laminated element and applying to the holes an adhesive or an adherent material catalytic to electroless plating; then 9. removing the strippable support; 10. applying finely divided catalytic material to the exposed surface and the holes to form a catalytic image; and 11. treating the catalytic image and holes with an electroless plating solution to form a conductive printed circuit and holes.
Claim 17
Dependent Claim
23 words
A process according to claim 12 wherein steps 1 through 5 are repeated at least once prior to the initiation of step 6.
Claim 18
Dependent Claim
22 words
A process according to claim 12 wherein holes are introduced into the photohardenable element prior to lamination to the printed circuit substrate.
Claim 19
Dependent Claim
96 words
A process for preparing two-sided printed circuit boards having plated-through-holes from a photosensitive element which comprises a substrate bearing in order on each side a photosensitive layer and a strippable support capable of transmitting actinic radiation wherein the photosensitive layers are exposed imagewise, the strippable supports are removed, the imaged photosensitive layers are developed, and the developed images are converted into a conductive printed circuit, which comprises, either prior to or after exposure, the steps of: 1. introducing through-holes into the element; and then 2. applying to the through-holes an adherent material catalytic to electroless plating;
Claim 20
Dependent Claim
96 words
A process for preparing two-sided printed circuit boards having plated-through-holes from a photosensitive element which comprises a substrate bearing in order on each side a photosensitive layer and a strippable support capable of transmitting actinic radiation wherein the photosensitive layers are exposed imagewise, the strippable supports are removed, the imaged photosensitive layers are developed, and the developed images are converted into a conductive printed circuit, which comprises, either prior to or after exposure, the steps of: 1. introducing through-holes into the element; and then 2. applying to the through-holes an adherent material catalytic to electroless plating;
Claim 21
Dependent Claim
24 words
removing the strippable supports from the photosensitive layers; and 4. applying electroless plating solution to the catalyzed through-holes to produce an electrically conductive through-hole.
Claim 22
Dependent Claim
24 words
removing the strippable supports from the photosensitive layers; and 4. applying electroless plating solution to the catalyzed through-holes to produce an electrically conductive through-hole.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-17 | 1981-04-18 | 1981-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-17 | 1985-04-18 | 1985-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-17 | 1989-04-18 | 1989-10-18 | $7700.00 | Window Closed / Lapsed |