US4054466A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Tannin treatment of aluminum
Assignee: MAN-GILL CHEMICAL COMPANY AN OH CORP
•
Filing: 1976-02-09
•
Granted: 1977-10-18
•
Expires: 1996-02-09
Abstract
Abstract Disclosed are a composition and process useful for the treatment of an aluminum surface comprising contacting the surface with an aqueous solution containing at least 0.000025 weight percent of a vegetable tannin, which solution exhibits a pH of at least 3. Best results can be obtained via a two-stage tanin treatment in which the treating solution of the first stage also contains titanium and fluoride in dissolved form.
Inventors
- 👤 Peter F. King
- 👤 Gary A. Reghi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:37
CPC Classifications
C; C23; C23C; C23C22/00; C23C22/05; C23C22/06; C23C22/48; C23C22/56; C23C22/34; C23C22/68
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
67 words
A process for the treatment of an aluminum surface to transform the surface to improve both the corrosion resistance of the surface and the adhesion of an organic finish to be subsequently applied to the treated surface comprising contacting the surface with an aqueous solution consisting essentially of at least 0.000025 weight percent of a vegetable tannin which solution exhibits a pH of from 3 to 9.
Claim 2
Dependent Claim
67 words
A process for the treatment of an aluminum surface to transform the surface to improve both the corrosion resistance of the surface and the adhesion of an organic finish to be subsequently applied to the treated surface comprising contacting the surface with an aqueous solution consisting essentially of at least 0.000025 weight percent of a vegetable tannin which solution exhibits a pH of from 3 to 9.
Claim 3
Dependent Claim
35 words
The process of claim 1 wherein the tannin concentration is at least about 0.002 weight percent, the temperature of the solution is at least 90° F and the contact time is at least 0.1 seconds.
Claim 4
Dependent Claim
23 words
The process of claim 2 wherein the solution temperature is between 90° and 150° F and the pH is from 4 to 8.
Claim 5
Dependent Claim
17 words
The process of claim 1 wherein said tannin is an extract of a naturally occurring tannin substance.
Claim 6
Dependent Claim
12 words
The process of claim 1 wherein the solution is substantially phosphate free.
Claim 7
Dependent Claim
42 words
In a process for preparing an aluminum surface to receive an organic finish wherein the surface is first cleaned, water rinsed, treated and water rinsed again, the improvement comprising contacting the surface with the solution of claim 1 to accomplish said treatment.
Claim 8
Dependent Claim
34 words
The process of claim 1 wherein the aqueous solution additionally contains fluoride ion, free or complexed, in an amount sufficient to improve the corrosion resistance and adhesion of an organic finish to the surface.
Claim 9
Dependent Claim
33 words
The process of claim 1 wherein the aqueous solution additionally contains a titanium compound in an amount sufficient to further improve the corrosion resistance and adhesion of an organic finish to the surface.
Claim 10
Dependent Claim
34 words
The process of claim 8 wherein the aqueous solution additionally contains fluoride ion, free or complexed, in an amount sufficient to improve the corrosion resistance and adhesion of an organic finish to the surface.
Claim 11
Dependent Claim
85 words
In a process for preparing an aluminum surface to receive an organic finish comprising cleaning, treating and post-treating, the improvement comprising contacting the surface with an aqueous composition consisting essentially of at least 0.000025 weight percent of a vegetable tannin which composition exhibits a pH of from 3 to 9 to accomplish said treatment and thereafter contacting the surface with a second composition consisting essentially of at least 0.000025 weight percent vegetable tannin and exhibiting a pH of 3 to 9 to accomplish said post-treatment.
Claim 12
Dependent Claim
85 words
In a process for preparing an aluminum surface to receive an organic finish comprising cleaning, treating and post-treating, the improvement comprising contacting the surface with an aqueous composition consisting essentially of at least 0.000025 weight percent of a vegetable tannin which composition exhibits a pH of from 3 to 9 to accomplish said treatment and thereafter contacting the surface with a second composition consisting essentially of at least 0.000025 weight percent vegetable tannin and exhibiting a pH of 3 to 9 to accomplish said post-treatment.
Claim 13
Dependent Claim
12 words
The process of claim 10 comprising at least one intervening water rinse.
Claim 14
Dependent Claim
41 words
The process of claim 10 wherein with respect to the treating step, the tannin concentration is at least about 0.002 weight percent, the temperature of the solution is at least 90° F and the contact time is at least 0.1 seconds.
Claim 15
Dependent Claim
24 words
The process of claim 12 wherein the treating solution temperature is between 90° and 150° F and the pH is from 4 to 8.
Claim 16
Dependent Claim
17 words
The process of claim 10 wherein each tannin is an extract of a naturally occurring tannin substance.
Claim 17
Dependent Claim
12 words
The process of claim 10 wherein the solutions are substantially phosphate free.
Claim 18
Dependent Claim
35 words
The process of claim 10 wherein the aqueous treating solution additionally contains fluoride ion, free or complexed, in an amount sufficient to improve the corrosion resistance and adhesion of an organic finish to the surface.
Claim 19
Dependent Claim
34 words
The process of claim 10 wherein the aqueous treating solution additionally contains a titanium compound in an amount sufficient to further improve the corrosion resistance and adhesion of an organic finish to the surface.
Claim 20
Dependent Claim
34 words
The process of claim 17 complexed, the aqueous solution additionally contains fluoride ion, free or comlexed, in an amount sufficient to improve the corrosion resistance and adhesion of an organic finish to the surface.
Claim 21
Dependent Claim
44 words
An aqueous phosphate-free composition exhibiting a pH of from 3 to 9 and consisting essentially of a vegetable tannin and a soluble titanium compound in amounts sufficient to improve the corrosion resistance and organic finish adhesion of an aluminum surface contacted with the composition.
Claim 22
Dependent Claim
44 words
An aqueous phosphate-free composition exhibiting a pH of from 3 to 9 and consisting essentially of a vegetable tannin and a soluble titanium compound in amounts sufficient to improve the corrosion resistance and organic finish adhesion of an aluminum surface contacted with the composition.
Claim 23
Dependent Claim
30 words
The composition of claim 19 further comprising fluoride ion in an amount sufficient to imrove the corrosion resistance and organic finish adhesion of an aluminum surface contacted with the composition.
References Cited (Backward Citations)
US2146840A
Cited
US2502441A
Cited
US2854368A
Cited
US3443992A
Cited
DE2446492A1
Cited
FR2246653A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-17 | 1981-04-18 | 1981-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-17 | 1985-04-18 | 1985-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-17 | 1989-04-18 | 1989-10-18 | $7700.00 | Window Closed / Lapsed |