Process for improving the adhesion of hot melts to metal substrates

Claim 2

A process for adhering a filled copoly(esteramide) to a metal substrate which comprises: a. applying to the metal substrate a primer comprising an etherified methylolmelamine with a degree of methylolation in the range of about 5 to 6, a degree of etherification with a C 1 to C 6 alkanol or cycloalkanol in the range of about 3 to 6, and a degree of methylation of at least about 2 to provide a coating weight in the range of 1 to 166 g. per sq. meter; b. heating the substrate to a temperature in the range of about 150° to about 300° C. to convert the etherified methylolmelamine from the liquid to the solid state; and c. applying the filled copoly(ester-amide) as a hot melt to the formed surface at a temperature in the range of about 150° to 300° C.

Claim 3

The process of claim 1 wherein the etherified methylolmelamine is a methoxymethylmelamine.

Claim 4

The process of claim 1 wherein the copoly(ester-amide) comprises a crystalline and an amorphous segment.

Claim 5

The process of claim 1 wherein the filled copoly(ester-amide) comprises: a. from about 70 to about 30 parts by weight of a poly(ester-amide) block copolymer melting in the range of about 155° to about 225° C. having from about 30 to about 70 percent by weight of crystalline polyester segments derived from at least one aliphatic or alicyclic diol having from 2 to 10 carbon atoms and at least one alicyclic or aromatic dicarboxylic acid having from 8 to 20 carbon atoms, and from about 70 to about 30 percent by weight of amorphous polyamide segments derived from an aliphatic polycarboxylic acid containing at least 40 weight percent of a C 18 to C 54 polycarboxylic acid and an aliphatic or alicyclic primary diamine containing 2 to 10 carbon atoms; and b. from about 30 to about 70 parts by weight of finely divided inorganic particulate filler.

Claim 6

The process of claim 4 wherein the finely divided inorganic particulate filler is a spheroidal metal powder selected from the group consisting of aluminum, iron, mild steel, stainless steel and zinc.

Claim 7

The process of claim 1 wherein the coating weight of the primer is in the range of 5 to 25 g. per sq. meter.

Claim 8

A coated article comprising a metal substrate, a primer and a filled copoly(ester-amide); wherein the primer is a liquid etherified methylolmelamine with a degree of methylolation in the range of about 5 to 6, a degree of etherification with a C 1 to C 6 alkanol or cycloalkanol in the range of about 3 to 6, and a degree of methylation of at least about 2, which has been applied to provide a coating weight in the range of 1 to 166 g. per sq. meter and advanced to the solid state.

Claim 9

A coated article comprising a metal substrate, a primer and a filled copoly(ester-amide); wherein the primer is a liquid etherified methylolmelamine with a degree of methylolation in the range of about 5 to 6, a degree of etherification with a C 1 to C 6 alkanol or cycloalkanol in the range of about 3 to 6, and a degree of methylation of at least about 2, which has been applied to provide a coating weight in the range of 1 to 166 g. per sq. meter and advanced to the solid state.

Claim 10

The coated article of claim 7 wherein the etherified methylolmelamine is a methoxymethylmelamine.

Claim 11

The coated article of claim 7 wherein the copoly(ester-amide) comprises a crystalline and an amorphous segment.

Claim 12

The coated article of claim 7 wherein the filled copoly(ester-amide) comprises: a. from about 70 to about 30 parts by weight of a poly(ester-amide) block copolymer melting in the range of about 155° to about 225° C. having from about 30 to about 70 percent by weight of crystalline polyester segments derived from at least one aliphatic or alicyclic diol having from 2 to 10 carbon atoms and at least one alicyclic or aromatic dicarboxylic acid having from 8 to 20 carbon atoms, and from about 70 to about 30 percent by weight of amorphous polyamide segments derived from an aliphatic polycarboxylic acid containing at least 40 weight percent of a C 18 to C 54 polycarboxylic acid and an aliphatic or alicyclic primary diamine containing 2 to 10 carbon atoms; and b. from about 30 to about 70 parts by weight of finely divided inorganic particulate filler.

Claim 13

The coated article of claim 10 wherein the finely divided inorganic particulate filler is a spheroidal metal powder selected from the group consisting of aluminum, iron, mild steel, stainless steel and zinc.

Claim 14

The coated article of claim 10 wherein the polyester block of the poly(ester-amide) is selected from the group consisting of poly(ethyleneterephthalate), co-poly(butylene terephthalate)-(ethylene terephthalate), co-poly(ethylene-terephthalate)-(ethylene isophthalate) and co-poly(ethyleneterephthalate)-(propylene terephthalate) and wherein the diamine of the amide block of the poly(ester-amide) is hexamethylene diamine.

Claim 15

The coated article of claim 10 wherein the coating weight of the primer is in the range of 5 to 25 g. per sq. meter.

Claim 16

The coated article of claim 7 wherein the coating weight of the primer is in the range of 5 to 25 g. per sq. meter.

Claim 17

A coated article comprising a metal substrate, a primer and a filled copoly(ester-amide); wherein the primer comprises an etherified methylolmelamine with a degree of methylolation in the range of about 5 to 6, a degree of etherification with a C 1 to C 6 alkanol or cycloalkanol in the range of about 3 to 6, and a degree of methylation of at least about 2, which has been applied to provide a coating weight in the range of 1 to 166 g. per sq. meter and advanced to the solid state; and wherein the filled copoly(ester-amide) comprises: a. from about 70 to about 30 parts by weight of a poly(ester-amide) block copolymer of inherent viscosity in the range of about 0.35 to about 0.95 and of melting point in the range of about 155° to about 225° C., having from about 30 to about 70 percent by weight of crystalline polyester segments selected from the group consisting of poly(ethylene-terephthalate), co-poly(butylene terephthalate)-(ethylene terephthalate), co-poly(ethylene-terephthalate)-(ethylene isophthalate) and co-poly(ethylene terephthalate)-(propylene terephthalate which prior to incorporation in the poly(ester-amide), have an inherent viscosity in the range of about 0.05 to about 0.70 and a melting point in the range of about 180° to about 270° C., and from about 70 to about 30 percent by weight of amorphous polyamide segments derived from a C 36 dibasic acid and analiphatic or alicyclic diamine containing from 2 to 10 carbon atoms, the inherent viscosity being determined at 25° C. with an 0.5 gram solution in 100 ml. of a solvent mixture of 60 parts by weight of phenol and 40 parts by weight of symm-tetrachloroethane; and b. from about 30 to about 70 parts by weight of spheroidal aluminum powder of particle size in the range of about 4 to about 100 microns.

Claim 18

A coated article comprising a metal substrate, a primer and a filled copoly(ester-amide); wherein the primer comprises an etherified methylolmelamine with a degree of methylolation in the range of about 5 to 6, a degree of etherification with a C 1 to C 6 alkanol or cycloalkanol in the range of about 3 to 6, and a degree of methylation of at least about 2, which has been applied to provide a coating weight in the range of 1 to 166 g. per sq. meter and advanced to the solid state; and wherein the filled copoly(ester-amide) comprises: a. from about 70 to about 30 parts by weight of a poly(ester-amide) block copolymer of inherent viscosity in the range of about 0.35 to about 0.95 and of melting point in the range of about 155° to about 225° C., having from about 30 to about 70 percent by weight of crystalline polyester segments selected from the group consisting of poly(ethylene-terephthalate), co-poly(butylene terephthalate)-(ethylene terephthalate), co-poly(ethylene-terephthalate)-(ethylene isophthalate) and co-poly(ethylene terephthalate)-(propylene terephthalate which prior to incorporation in the poly(ester-amide), have an inherent viscosity in the range of about 0.05 to about 0.70 and a melting point in the range of about 180° to about 270° C., and from about 70 to about 30 percent by weight of amorphous polyamide segments derived from a C 36 dibasic acid and analiphatic or alicyclic diamine containing from 2 to 10 carbon atoms, the inherent viscosity being determined at 25° C. with an 0.5 gram solution in 100 ml. of a solvent mixture of 60 parts by weight of phenol and 40 parts by weight of symm-tetrachloroethane; and b. from about 30 to about 70 parts by weight of spheroidal aluminum powder of particle size in the range of about 4 to about 100 microns.

Claim 19

The coated article of claim 15 wherein the coating weight of the primer is in the range of 5 to 25 g. per sq. meter.