Coating composition and method for improving propellant tear strength
Assignee: United States Department of the Navy
•
Filing: 1976-09-16
•
Granted: 1977-10-11
•
Expires: 1996-09-16
Abstract
Abstract A typical rocket motor includes a motor casing containing a cast propellant bonded to the casing and provided with a port through which combustion gases are delivered to the motor nozzle. During storage and operation, mechanical stresses in the propellant may produce tears resulting in motor malfunctions. Tear strength can be increased by reactively forming on selected port surface areas a thin-film cross-linked polymeric gel coating formed essentially of a highly functional polyglycol adipate and a polyfunctional isocyanate. Cross-linking with the propellant can be achieved by controlling the hydroxyl to isocyanate ratios of the coating and the propellant. The coating is particularly useful on XLDB (cross-linked, composite-modified double base) and on CMDB (composite-modified double-base) propellants.
Inventors
- 👤 Donald E. Elrick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 05:20
CPC Classifications
F; F02; F02K; F02K9/00; F02K9/08; F02K9/10; F02K9/18; F02K9/32; F02K9/34; F02K9/346
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
123 words
A method of increasing the tear strength of the propellant of a rocket motor in which the propellant is a molded structure formed with an axial gas-conducting port, said method including the steps of: dissolving in a volatile solvent stoichiometric quantities of a polyglycol adipate and an isocyanate with said quantities being adjusted to provide a ratio of 1-2 isocyanate groups to one hydroxyl group, applying said solution as a coating on selected areas of said port surfaces, evaporating said solvent, and aging said coating sufficiently to achieve an essentially complete reaction between said hydroxyl and isocyanate groups for forming on said selected surface areas a tear-inhibiting polymeric gel, said polyglycol adipate having a relatively high functionality for assuring a cross-linked protective coating.
Claim 2
Independent Claim
123 words
A method of increasing the tear strength of the propellant of a rocket motor in which the propellant is a molded structure formed with an axial gas-conducting port, said method including the steps of: dissolving in a volatile solvent stoichiometric quantities of a polyglycol adipate and an isocyanate with said quantities being adjusted to provide a ratio of 1-2 isocyanate groups to one hydroxyl group, applying said solution as a coating on selected areas of said port surfaces, evaporating said solvent, and aging said coating sufficiently to achieve an essentially complete reaction between said hydroxyl and isocyanate groups for forming on said selected surface areas a tear-inhibiting polymeric gel, said polyglycol adipate having a relatively high functionality for assuring a cross-linked protective coating.
Claim 3
Dependent Claim
41 words
The method of claim 1 wherein said polyglycol adipate is trifunctional and said isocyanate is selected from a group of difunctional and trifunctional isocyanates consisting of hexamethylene isocyanate, a hexamethylene isocyanate Trimer, 2, 4, 4-trimethylhexamethylene diisocyanate and 3-isocyanatomethyl-3, 5, 5-trimethylcyclohexyl isocyanate.
Claim 4
Dependent Claim
31 words
The method of claim 2 wherein said molded propellant structure is further provided with radially extending slots and wherein said selected areas of solution application consist essentially of said slot surfaces.
Claim 5
Dependent Claim
21 words
The method of claim 1 wherein said propellant includes a polymer system formed by a reaction of hydroxyl and isocyanate groups.
Claim 6
Dependent Claim
37 words
The method of claim 4 wherein the ratio of isocyanate to hydroxyl groups of said propellant binder system is less than one whereby excess isocyanate groups of said coating can reactively cross-link with said propellant hydroxyl groups.
Claim 7
Dependent Claim
95 words
A polymeric coating for use on the port surfaces of a rocket motor propellant having an axially-extending gas-conducting port, said propellant including an oxidizer material and a binder formed of a plasticizer and a polymer system, the latter being formed by a reaction product of polyglycol adipate and a diisocyanate, said coating comprising: a cross-linked polymeric gel formed by reacting an essentially trifunctional polyglycol adipate with a stoichiometric quantity of an isocyanate selected from a group of difunctional and trifunctional isocyanates consisting of hexamethylene isocyanate trimer, 2, 4, 4-trimethylhexamethylene diisocyanate and 3-isocyanatomethyl-3, 5, 5-trimethyleyclohexyl isocyanate.
Claim 8
Dependent Claim
95 words
A polymeric coating for use on the port surfaces of a rocket motor propellant having an axially-extending gas-conducting port, said propellant including an oxidizer material and a binder formed of a plasticizer and a polymer system, the latter being formed by a reaction product of polyglycol adipate and a diisocyanate, said coating comprising: a cross-linked polymeric gel formed by reacting an essentially trifunctional polyglycol adipate with a stoichiometric quantity of an isocyanate selected from a group of difunctional and trifunctional isocyanates consisting of hexamethylene isocyanate trimer, 2, 4, 4-trimethylhexamethylene diisocyanate and 3-isocyanatomethyl-3, 5, 5-trimethyleyclohexyl isocyanate.
Claim 9
Dependent Claim
121 words
A rocket motor comprising: a casing, a molded propellant structure contained in said casing, said structure being formed of an ignitable propellant material provided with an axially-extending gas-conducting port and said propellant material including an oxidizer material and a binder formed by a plasticizer material and a polymer system, the latter being a reaction product of a polyglycol adipate and a diisocyanate, and a cross-linked polymeric gel coating formed in situ on at least selected areas of said port surface, said coating being formed by reacting a trifunctional polyglycol adipate with a stoichiometric quantity of an isocyanate selected from a group of difunctional and trifunctional isocyanates consisting of a hexamethylene isocyanate trimer, 2, 4, 4-trimethylhexamethylene diisocyanate and 3-isocyanatomethyl-3, 5, 5-trimethylcyclohexyl isocyanate.
Claim 10
Dependent Claim
121 words
A rocket motor comprising: a casing, a molded propellant structure contained in said casing, said structure being formed of an ignitable propellant material provided with an axially-extending gas-conducting port and said propellant material including an oxidizer material and a binder formed by a plasticizer material and a polymer system, the latter being a reaction product of a polyglycol adipate and a diisocyanate, and a cross-linked polymeric gel coating formed in situ on at least selected areas of said port surface, said coating being formed by reacting a trifunctional polyglycol adipate with a stoichiometric quantity of an isocyanate selected from a group of difunctional and trifunctional isocyanates consisting of a hexamethylene isocyanate trimer, 2, 4, 4-trimethylhexamethylene diisocyanate and 3-isocyanatomethyl-3, 5, 5-trimethylcyclohexyl isocyanate.
Claim 11
Dependent Claim
51 words
The rocket motor of claim 7 wherein said polymer system of said propellant has excess hydroxyl groups, said gel being formed by reacting stoichiometric quantities having a ratio of isocyanate to hydroxyl groups of about 1-2 whereby said isocyanate groups can reactively cross-link with said excess hydroxyl groups of the propellant.
Claim 12
Dependent Claim
36 words
The rocket motor of claim 7 wherein said coating is selectively restricted to those portions of said port surface subjected to greater than average stresses and to other portions weakened by the presence of surface blemishes.
Claim 13
Dependent Claim
40 words
The rocket motor of claim 7 wherein said plasticizer of said propellant is a nitrate ester and the tear strength of the propellant is low due to the relative quantities of the nitrate ester and polymer in said propellant binder.
Claim 14
Dependent Claim
26 words
The rocket motor of claim 9 wherein said axial port is provided with a plurality of radially-extending slots, said selected portions including surfaces of said slots.
References Cited (Backward Citations)
US3215028A
Cited
US3447980A
Cited
US3445306A
Cited
US3558285A
Cited
US3960088A
Cited
US3713395A
Cited
US3961476A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-10 | 1981-04-11 | 1981-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-10 | 1985-04-11 | 1985-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-10 | 1989-04-11 | 1989-10-11 | $7700.00 | Window Closed / Lapsed |