Non-settling process for coating a phosphor slurry on the inner surface of a cathode ray tube faceplate

Claim 2

A non-settling process for forming on an inner viewing surface of a color cathode ray tube faceplate a coating of an aqueous slurry composed of a photosensitized organic binder and a suspension of phosphor particles, which coating exhibits a high degree of coating weight uniformity, a relatively high phosphor coating weight, and suppressed radial streaking, said process comprising: supporting the faceplate such that the central axis of the faceplate has a substantial horizontal component; slowly rotating the faceplate about the central axis thereof while dispensing a stream of phosphor slurry onto the central region of the faceplate inner surface such that, due to gravitational forces and the slow rotation of the faceplate through the descending slurry stream, the slurry is suffused to the perimeter of the faceplate inner surface without any significant settling out of phosphor particles onto the faceplate; and levigating the coating by rotating the coated faceplate at a moderate angular velocity for a brief time interval, the joint effect of which moderate velocity and interval being to level and thin down the coating to a predetermined thickness while suppressing the formation of radial streaks in the coating radially outwardly of irregularities in or on the faceplate inner surface.

Claim 3

The method defined by claim 1 wherein the angular velocity of said faceplate during the slurry dispensation and suffusion operation is between about 5 and 30 revolutions per minute and the dispense interval is between about 10-20 seconds.

Claim 4

The method defined by claim 1 wherein during said levigation operation the faceplate is spun at an angular velocity of 100-200 revolutions per minute for a time interval which is between about 3-10 seconds.

Claim 5

The process defined by claim 1 wherein the angle of the faceplate axis to the vertical on the concave side of the faceplate is slightly greater than 90°.

Claim 6

The process defined by claim 4 wherein said angle is preferably about 100°.

Claim 7

The process defined by claim 1 including collecting excess slurry drained from the faceplate in the slurry dispensation operation and feeding it directly back for redispensation without the addition of a make-up slurry which is substantially different in phosphor content, viscosity or particle size distribution from that of the dispensed slurry.

Claim 8

The process defined by claim 1 wherein the slurry employed is super dense, having a phosphor content of 36% to 45% (by weight) and a viscosity of 40 to 60 centipoise.

Claim 9

A non-settling process for forming on an inner viewing surface of a color cathode ray tube faceplate a coating of an aqueous slurry composed of a photosensitized organic binder and a suspension of phosphor particles, which coating exhibits a high degree of coating weight uniformity, a relatively high phosphor coating weight, and suppressed radial streaking, said process comprising: supporting the faceplate such that the central axis of the faceplate has a substantial horizontal component; slowly rotating the faceplate about the central axis thereof while dispensing a stream of phosphor slurry onto the central region of the faceplate inner surface such that, due to gravitational forces and the slow rotation of the faceplate through the descending slurry stream, the slurry is suffused to the perimeter of the faceplate inner surface without any significant settling out of phosphor particles onto the faceplate; slowly rotating the faceplate for a predetermined delay interval effective to permit any tangential "sags" formed the dispensed coating during the dispensation and suffusion operation to even out; and levigating the coating by rotating the coated faceplate at a moderate angular velocity for a brief time interval, the joint effect of which moderate velocity and interval being to level and thin down the coating to a predetermined thickness while suppressing the formation of radial streaks in the coating radially outwardly of irregularities in or on the faceplate inner surface.

Claim 10

A non-settling process for forming on an inner viewing surface of a color cathode ray tube faceplate a coating of an aqueous slurry composed of a photosensitized organic binder and a suspension of phosphor particles, which coating exhibits a high degree of coating weight uniformity, a relatively high phosphor coating weight, and suppressed radial streaking, said process comprising: supporting the faceplate such that the central axis of the faceplate has a substantial horizontal component; slowly rotating the faceplate about the central axis thereof while dispensing a stream of phosphor slurry onto the central region of the faceplate inner surface such that, due to gravitational forces and the slow rotation of the faceplate through the descending slurry stream, the slurry is suffused to the perimeter of the faceplate inner surface without any significant settling out of phosphor particles onto the faceplate; slowly rotating the faceplate for a predetermined delay interval effective to permit any tangential "sags" formed the dispensed coating during the dispensation and suffusion operation to even out; and levigating the coating by rotating the coated faceplate at a moderate angular velocity for a brief time interval, the joint effect of which moderate velocity and interval being to level and thin down the coating to a predetermined thickness while suppressing the formation of radial streaks in the coating radially outwardly of irregularities in or on the faceplate inner surface.

Claim 11

The method defined by claim 8 wherein said delay interval is between about 3-15 seconds and wherein the speed of rotation of the faceplate during the delay interval is between about 5 and 30 RPM.

Claim 12

The method defined by claim 9 wherein said speed of faceplate rotation during said delay interval is the same as that employed during the dispensation and suffusion operation.

Claim 13

The method defined by claim 8 wherein during said levigating operation the faceplate is spun at an angular velocity of 100-200 revolutions per minute for a time interval which is between about 3-10 seconds.

Claim 14

The process defined by claim 8 including collecting excess slurry drained from the faceplate in the slurry dispensation operation and feeding it directly back for redispensation without the addition of a make-up slurry which is substantially different in phosphor content or particle size distribution from that of the dispensed slurry.

Claim 15

A non-settling process for forming on an inner viewing surface of a color cathode ray tube faceplate a coating of a super dense aqueous slurry composed of a photosensitized organic binder and a suspension of phosphor particles, which coating exhibits a high degree of coating weight uniformity and a relatively high phosphor coating weight, said process comprising: supporting the faceplate such that the central axis of the faceplate has a substantial horizontal component; slowly rotating the faceplate about the central axis thereof while dispensing onto the central region of the faceplate inner surface a stream of phosphor slurry having 36% to 45% (by weight) of phosphor material and a viscosity of 40 to 60 centipoise such that, due to gravitational forces and the slow rotation of the faceplate through the descending slurry stream, the slurry is suffused to the perimeter of the faceplate inner surface without any significant settling out of phosphor particles onto the faceplate; and levigating the coating by rotating the coated faceplate at a predetermined angular velocity for a predetermined time interval to level and thin down the coating to a predetermined thickness, the super density of the phosphor slurry increasing the phosphor coating weight in the resultant slurry coating.

Claim 16

A non-settling process for forming on an inner viewing surface of a color cathode ray tube faceplate a coating of a super dense aqueous slurry composed of a photosensitized organic binder and a suspension of phosphor particles, which coating exhibits a high degree of coating weight uniformity and a relatively high phosphor coating weight, said process comprising: supporting the faceplate such that the central axis of the faceplate has a substantial horizontal component; slowly rotating the faceplate about the central axis thereof while dispensing onto the central region of the faceplate inner surface a stream of phosphor slurry having 36% to 45% (by weight) of phosphor material and a viscosity of 40 to 60 centipoise such that, due to gravitational forces and the slow rotation of the faceplate through the descending slurry stream, the slurry is suffused to the perimeter of the faceplate inner surface without any significant settling out of phosphor particles onto the faceplate; and levigating the coating by rotating the coated faceplate at a predetermined angular velocity for a predetermined time interval to level and thin down the coating to a predetermined thickness, the super density of the phosphor slurry increasing the phosphor coating weight in the resultant slurry coating.

Claim 17

A non-settling process for forming on an inner viewing surface of a color cathode ray tube faceplate a coating of an aqueous slurry composed of a photosensitized organic binder and a suspension of phosphor particles, which coating exhibits a high degree of coating weight uniformity and a relatively high phosphor coating weight, said process comprising: supporting the faceplate such that the central axis of the faceplate has a substantial horizontal component; slowly rotating the faceplate about the central axis thereof while dispensing a stream of phosphor slurry onto the central region of the faceplate inner surface such that, due to gravitational force and the slow rotation of the faceplate through the descending slurry stream, the slurry is suffused to the perimeter of the faceplate inner surface without any significant settling out of phosphor particles onto the faceplate; levigating the coating by rotating the coated faceplate at a predetermined angular velocity for a predetermined time interval to level and thin down the coating to a predetermined thickness; and collecting the excess slurry drained from the faceplate during the slurry dispensation operation and feeding it directly back for redispensation without the addition of a make-up slurry differing substantially from the dispensed slurry in phosphor content, viscosity, phosphor-to-binder ratio or particle size distribution.

Claim 18

A non-settling process for forming on an inner viewing surface of a color cathode ray tube faceplate a coating of an aqueous slurry composed of a photosensitized organic binder and a suspension of phosphor particles, which coating exhibits a high degree of coating weight uniformity and a relatively high phosphor coating weight, said process comprising: supporting the faceplate such that the central axis of the faceplate has a substantial horizontal component; slowly rotating the faceplate about the central axis thereof while dispensing a stream of phosphor slurry onto the central region of the faceplate inner surface such that, due to gravitational force and the slow rotation of the faceplate through the descending slurry stream, the slurry is suffused to the perimeter of the faceplate inner surface without any significant settling out of phosphor particles onto the faceplate; levigating the coating by rotating the coated faceplate at a predetermined angular velocity for a predetermined time interval to level and thin down the coating to a predetermined thickness; and collecting the excess slurry drained from the faceplate during the slurry dispensation operation and feeding it directly back for redispensation without the addition of a make-up slurry differing substantially from the dispensed slurry in phosphor content, viscosity, phosphor-to-binder ratio or particle size distribution.

Claim 19

A non-settling process for forming on an inner viewing surface of a color cathode ray tube faceplate a coating of a super dense aqueous slurry composed of a photosensitized organic binder and a suspension of phosphor particles, which coating exhibits a high degree of coating weight uniformity, a relatively high phosphor coating weight, and suppressed radial streaking, said process comprising: supporting the faceplate such that the central axis of the faceplate has a substantial horizontal component; slowly rotating the faceplate about the central axis thereof while dispensing onto the central region of the faceplate inner surface a stream of phosphor slurry having 36%-45% (by weight) of phosphor material and a viscosity of 40-60 centipoise such that, due to gravitational forces and the slow rotation of the faceplate through the descending slurry stream, the slurry is suffused to the perimeter of the faceplate inner surface without any significant settling out of phosphor particles onto the faceplate; slowly rotating the faceplate for a predetermined delay interval effective to permit any tangential "sags" formed in the dispensed coating during the dispensation and suffusion operation to even out; levigating the coating by rotating the coated faceplate at a moderate angular velocity for a brief time interval, the joint effect of which moderate velocity and interval being to level and thin down the coating to a predetermined thickness while suppressing the formation of radial streaks in the coating radially outwardly of irregularities in or on the faceplate inner surface; and collecting the excess slurry drained from the faceplate during the slurry dispensation operation and feeding it directly back for redispensation without the addition of a make-up slurry differing substantially from the dispensed slurry in phosphor content, viscosity, phosphor-to-binder ratio or particle size distribution.

Claim 20

A non-settling process for forming on an inner viewing surface of a color cathode ray tube faceplate a coating of a super dense aqueous slurry composed of a photosensitized organic binder and a suspension of phosphor particles, which coating exhibits a high degree of coating weight uniformity, a relatively high phosphor coating weight, and suppressed radial streaking, said process comprising: supporting the faceplate such that the central axis of the faceplate has a substantial horizontal component; slowly rotating the faceplate about the central axis thereof while dispensing onto the central region of the faceplate inner surface a stream of phosphor slurry having 36%-45% (by weight) of phosphor material and a viscosity of 40-60 centipoise such that, due to gravitational forces and the slow rotation of the faceplate through the descending slurry stream, the slurry is suffused to the perimeter of the faceplate inner surface without any significant settling out of phosphor particles onto the faceplate; slowly rotating the faceplate for a predetermined delay interval effective to permit any tangential "sags" formed in the dispensed coating during the dispensation and suffusion operation to even out; levigating the coating by rotating the coated faceplate at a moderate angular velocity for a brief time interval, the joint effect of which moderate velocity and interval being to level and thin down the coating to a predetermined thickness while suppressing the formation of radial streaks in the coating radially outwardly of irregularities in or on the faceplate inner surface; and collecting the excess slurry drained from the faceplate during the slurry dispensation operation and feeding it directly back for redispensation without the addition of a make-up slurry differing substantially from the dispensed slurry in phosphor content, viscosity, phosphor-to-binder ratio or particle size distribution.

Claim 21

The method defined by claim 15 wherein during said levigation operation the faceplate is spun at an angular velocity of 100-200 revolutions per minute for a time interval which is between about 3-10 seconds.

Claim 22

The method defined by claim 16 wherein the angle of the faceplate axis to the vertical on the concave side of the faceplate is slightly greater than 90°.

Claim 23

The method defined by claim 17 wherein the angular velocity of said faceplate during the slurry dispensation and suffusion operation is between about 5 and 30 revolutions per minute and the dispense interval is between about 10-20 seconds.

Claim 24

The method defined by claim 18 wherein the slurry employed is super dense, having a phosphor content of 36% to 45% (by weight) and a viscosity of 40 to 60 centipoise.

Claim 25

The method defined by claim 19 wherein said delay interval is between about 3-15 seconds and wherein the speed of rotation of the faceplate during the delay interval is the same as that employed during the dispensation and suffusion operation.