Techniques for producing an acousto-optical component or a wide-band ultrasonic component
Assignee: Siemens AG
•
Filing: 1975-12-16
•
Granted: 1977-10-04
•
Expires: 1995-12-16
Abstract
Abstract An acousto-optical component or other high frequency and wide-band ultrasonic component comprises a piezoelectric transducer and a crystalline or glass sound medium which are bonded together by a multi-layer metal molecular adhesion bond. During fabrication, the surfaces of the piezoelectric body and the sound medium which are to be connected are first polished to a degree of smoothness which is well below that of a Newton ring. These surfaces are then completely cleansed and a first metal layer having a thickness of 0.5-2 nm is vapor deposited onto each the cleansed surfaces. Next, a second metal layer having a thickness of 5-20 nm is vapor deposited onto each of the first layers. The transducer is then applied, by molecular adhesion, to the sound medium. To form a strong and reliable bond, only moderate pressures of about 250 to 1500 psi are necessary. A metal layer having a thickness of 0.3-0.6 μm is vapor deposited over an extending portion of the multi-layer bond as a terminal for connection to a high frequency supply. Subsequently, the transducer is ground to a desired thickness in order to obtain a desired resonant frequency and a second electrode is applied to another surface of the piezoelectric body for connection to the high frequency supply.
Inventors
- 👤 Hans Eschler
- 👤 Rudolf Oberbacher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:16
CPC Classifications
H; H10; H10N; H10N30/00; H10N30/01; H10N30/07; H10N30/074; H10N30/076; G; G02; G02F; G02F1/00; G02F1/29; G02F1/33; G10; G10K; G10K11/00; G10K11/18; G10K11/26; G10K11/32; Y; Y10; Y10T; Y10T29/00; Y10T29/42; Y10T29/49; Y10T29/49002; Y10T29/49005
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
158 words
A process for producing an ultrasonic component which comprises a piezoelectric transducer and a sound medium, comprising the steps of: smoothing a surface of the sound medium and a surface of the piezoelectric material to a degree of smoothness which is well below that of a Newton ring; cleaning the smoothed surfaces; applying a first metal layer having a thickeness in the range of 0.5-2 nm to each of the cleansed surfaces; applying a second metal layer having a thickness in the range of 5-20 nm to each of the first metal layers; bonding the second metal layers together by molecular adhesion with a portion of the metal layers of the sound medium remaining exposed; applying a third metal layer having a thickness in the range of 0.3-0.6 μm to the exposed portion of the metal layers of the sound medium and to the piezoelectric material; and adjusting the resonant frequency of the transducer to a desired frequency.
Claim 2
Dependent Claim
158 words
A process for producing an ultrasonic component which comprises a piezoelectric transducer and a sound medium, comprising the steps of: smoothing a surface of the sound medium and a surface of the piezoelectric material to a degree of smoothness which is well below that of a Newton ring; cleaning the smoothed surfaces; applying a first metal layer having a thickeness in the range of 0.5-2 nm to each of the cleansed surfaces; applying a second metal layer having a thickness in the range of 5-20 nm to each of the first metal layers; bonding the second metal layers together by molecular adhesion with a portion of the metal layers of the sound medium remaining exposed; applying a third metal layer having a thickness in the range of 0.3-0.6 μm to the exposed portion of the metal layers of the sound medium and to the piezoelectric material; and adjusting the resonant frequency of the transducer to a desired frequency.
Claim 3
Dependent Claim
15 words
The process of claim 1, wherein the step of smoothing is further defined as polishing.
Claim 4
Dependent Claim
26 words
The process of claim 1, wherein the steps of applying the first, second and third metal layers are further defined as vapor depositing such metal layers.
Claim 5
Dependent Claim
39 words
The process of claim 1, wherein the step of adjusting the resonant frequency of the transducer is further defined by the step of: reducing the thickness of the piezoelectric transducer to a thickness which provides the desired resonant frequency.
Claim 6
Dependent Claim
27 words
The process of claim 4, wherein the step of reducing the thickness of the piezoelectric transducer is further defined as grinding the transducer to a desired thickness.
Claim 7
Dependent Claim
27 words
The process of claim 5, wherein the step of grinding is further defined as grinding the piezoelectric material to a thickness in the range of 20-50 μm.
Claim 8
Dependent Claim
25 words
The process of claim 1, wherein the step of applying the first metal layer is further defined as vapor depositing titanium on each smoothed surface.
Claim 9
Dependent Claim
25 words
The process of claim 1, wherein the step of applying the first metal layers is further defined as vapor depositing chrome on each smoothed surface.
Claim 10
Dependent Claim
25 words
The process of claim 1, wherein the step of applying the first metal layers is further defined as vapor depositing platinum on each smoothed surface.
Claim 11
Dependent Claim
26 words
The process of claim 1, wherein the step of applying the second metal layer is further defined as vapor depositing gold on each first metal layer.
Claim 12
Dependent Claim
28 words
The process of claim 1, wherein the step of applying a third layer is further defined as vapor depositing gold on the exposed portion of the metal layers.
Claim 13
Dependent Claim
31 words
The process of claim 1, wherein the step of applying the first metal layers is further defined as applying each of the first metal layers at a thickness of 1 nm.
Claim 14
Dependent Claim
34 words
The process of claim 1, wherein the step of applying the second metal layers is further defined as applying each of the second metal layers at a thickness in the range of 5-20 nm.
Claim 15
Dependent Claim
22 words
The process of claim 1, and further comprising the step of: applying a metal electrode to another surface of the piezoelectric material.
Claim 16
Dependent Claim
211 words
A process for the production of an ultrasonic component which includes a peizoelectric transducer and a sound medium, comprising the steps of: polishing a surface of the piezoelectric material to a degree of smoothness which is less than that of a Newton ring; polishing a surface of the ultrasonic medium to a degree of smoothness which is less than that of a Newton ring; cleaning each of the polished surfaces; vapor depositing a first metal layer on each of the cleansed surfaces of a thickness in the range of 0.5-2 nm and of a material selected from the group consisting of titanium, chrome, and platinum; vapor depositing a layer of gold of a thickness in the range of 5-20 nm over each of the first metal layers; bonding the gold layers together by molecular adhesion with the piezoelectric material and the sound medium positioned to leave a portion of the metal layers carried on the sound medium exposed; vapor depositing a gold layer of a thickness in the range of 0.3-06 μm on the exposed portion of the metal layers carried on the sound medium; grinding the thickness of the piezoelectric material to obtain a desired resonant frequency; and vapor depositing a metal layer on another surface of the piezoelectric material.
Claim 17
Dependent Claim
211 words
A process for the production of an ultrasonic component which includes a peizoelectric transducer and a sound medium, comprising the steps of: polishing a surface of the piezoelectric material to a degree of smoothness which is less than that of a Newton ring; polishing a surface of the ultrasonic medium to a degree of smoothness which is less than that of a Newton ring; cleaning each of the polished surfaces; vapor depositing a first metal layer on each of the cleansed surfaces of a thickness in the range of 0.5-2 nm and of a material selected from the group consisting of titanium, chrome, and platinum; vapor depositing a layer of gold of a thickness in the range of 5-20 nm over each of the first metal layers; bonding the gold layers together by molecular adhesion with the piezoelectric material and the sound medium positioned to leave a portion of the metal layers carried on the sound medium exposed; vapor depositing a gold layer of a thickness in the range of 0.3-06 μm on the exposed portion of the metal layers carried on the sound medium; grinding the thickness of the piezoelectric material to obtain a desired resonant frequency; and vapor depositing a metal layer on another surface of the piezoelectric material.
Claim 18
Dependent Claim
25 words
The process of claim 15, wherein the step of vapor depositing the first metal layers is further defined as depositing a thickness of 1 nm.
Claim 19
Dependent Claim
25 words
The process of claim 15, wherein the step of vapor depositing the second metal layers is further defined as depositing a thickness of 5-20 nm.
Claim 20
Dependent Claim
24 words
The process of claim 15, wherein the step of grinding is further defined as grinding the piezoelectric material to a thickness of 20-50 μm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-03 | 1981-04-04 | 1981-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-03 | 1985-04-04 | 1985-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-03 | 1989-04-04 | 1989-10-04 | $7700.00 | Window Closed / Lapsed |