Furan-phenolic resin coated sand for collapsible foundry molds
Assignee: Unilever Bestfoods North America
•
Filing: 1975-10-16
•
Granted: 1977-09-27
•
Expires: 1995-10-16
Abstract
Abstract A resin for coating sand and a resin-coated sand produced therefrom wherein the resin is prepared by incorporating furan into a phenolic novolak resin. In the preferred practice, the resin is produced by reaction of furfuryl alcohol with a phenolic compound at an acid pH to give a furfuryl-phenolic intermediate in a first step, and then, in a second step, reacting the furfuryl-phenolic intermediate with a lower aliphatic aldehyde to produce the resin. The resin-coated sands of the present invention provide unexpectedly improved shakeout and collapsibility characteristics in the shell process.
Inventors
- 👤 Robert Laitar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 23:18
CPC Classifications
B; B22; B22C; B22C1/00; B22C1/16; B22C1/20; B22C1/22; B22C1/2233; B22C1/224; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2998
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
116 words
A resin coated sand comprising: 1. particles of sand coated with from about 1% to about 8% by weight of the sand of a furan-modified novolak resin prepared by a. reacting of furfuryl alcohol with a phenol at an acid pH; with the mole ratio of furfuryl alcohol to the phenol being within the range of 0.04 to 0.9, to produce a furfuryl-phenolic intermediate, and b. reacting of said intermediate with a C 1 to C 3 aliphatic aldehyde at an acid pH, with the molar ratio of aldehyde to the total of the phenol and furfuryl alcohol being within the range of 0.5 to 0.85 c. and separating the resin; and 2. a curing agent.
Claim 2
Dependent Claim
116 words
A resin coated sand comprising: 1. particles of sand coated with from about 1% to about 8% by weight of the sand of a furan-modified novolak resin prepared by a. reacting of furfuryl alcohol with a phenol at an acid pH; with the mole ratio of furfuryl alcohol to the phenol being within the range of 0.04 to 0.9, to produce a furfuryl-phenolic intermediate, and b. reacting of said intermediate with a C 1 to C 3 aliphatic aldehyde at an acid pH, with the molar ratio of aldehyde to the total of the phenol and furfuryl alcohol being within the range of 0.5 to 0.85 c. and separating the resin; and 2. a curing agent.
Claim 3
Dependent Claim
19 words
A resin coated sand as defined in claim 1 wherein the phenol is phenol and the aldehyde is formaldehyde.
Claim 4
Dependent Claim
33 words
A resin coated sand as defined in claim 1 wherein the furfuryl alcohol is reacted with the phenol at a temperature within the range of about 40 ° C to about 100° C.
Claim 5
Dependent Claim
26 words
A resin coated sand as defined in claim 1 wherein the intermediate is reacted with the aldehyde at a temperature of at least 60 ° C.
Claim 6
Dependent Claim
29 words
A resin coated sand as defined in claim 1 wherein the molar ratio of furfuryl alcohol to the phenol is within the range of about 0.05 to about 0.30.
Claim 7
Dependent Claim
27 words
A resin coated sand as defined in claim 1 wherein the reaction of the intermediate with the aldehyde is carried out at an acid pH below 6.
Claim 8
Dependent Claim
46 words
A resin coated sand as defined in claim 1 wherein the reaction of the phenol and furfuryl alcohol and the reaction of the intermediate with the aldehyde are carried out in the presence of an acid catalyst to maintain the pH of the reaction below 6.0.
Claim 9
Dependent Claim
152 words
A resin coated sand comprising: 1. particles of sand coated with from about 1% to about 8% by weight of the sand of a novolak resin prepared by a. reacting a furan compound selected from the group consisting of furfuryl alcohol and furfural with a phenol in the presence of a catalyst to promote a condensation reaction of the furan compound with the phenol, with the mole ratio of the furan compound to the phenol being within the range of 0.04 to 0.9, to produce a furan-phenolic intermediate, b. reacting said intermediate with a C 1 to C 3 aliphatic aldehyde in the presence of a catalyst to promote a condensation reaction between the aldehyde and the intermediate, with the mole ratio of the aldehyde to the total of the phenol and furan compound being within the range of 0.5 to 0.85, c. and separating the resin; and 2. a curing agent.
Claim 10
Dependent Claim
152 words
A resin coated sand comprising: 1. particles of sand coated with from about 1% to about 8% by weight of the sand of a novolak resin prepared by a. reacting a furan compound selected from the group consisting of furfuryl alcohol and furfural with a phenol in the presence of a catalyst to promote a condensation reaction of the furan compound with the phenol, with the mole ratio of the furan compound to the phenol being within the range of 0.04 to 0.9, to produce a furan-phenolic intermediate, b. reacting said intermediate with a C 1 to C 3 aliphatic aldehyde in the presence of a catalyst to promote a condensation reaction between the aldehyde and the intermediate, with the mole ratio of the aldehyde to the total of the phenol and furan compound being within the range of 0.5 to 0.85, c. and separating the resin; and 2. a curing agent.
Claim 11
Dependent Claim
16 words
A resin coated sand as defined in claim 8 wherein the furan compound is furfuryl alcohol.
Claim 12
Dependent Claim
15 words
A resin coated sand as defined in claim 8 wherein the furan compound is furfural.
Claim 13
Dependent Claim
186 words
A resin coated sand comprising: 1. particles of sand coated with from about 1% to about 8% by weight of a resin prepared by: a. providing a furan-containing resin selected from the group consisting of: i. a furan resin prepared by reaction of furfuryl alcohol with a C 1 to C 3 aliphatic aldehyde, and ii. a furan modified resin prepared by reaction of a phenol and a C 1 to C 3 aliphatic aldehyde to produce a resole resin and then reacting the resole resin with furfuryl alcohol; and b. blending with the furan-containing resin with a novolak resin prepared by reaction of a phenol with a C 1 to C 3 aliphatic aldehyde, with the ratio of the toal of the aldehyde contained in the furan-containing resin and the novolak resin to the phenol of the novolak resin and the furfuryl alcohol of the furan-containing resin being within the range of 0.5 to 0.85 and the ratio of furfuryl alcohol of the furan-containing resin to the phenol of the novolak resin is within the range of 0.04 to 0.9; and 2. a curing agent.
Claim 14
Dependent Claim
186 words
A resin coated sand comprising: 1. particles of sand coated with from about 1% to about 8% by weight of a resin prepared by: a. providing a furan-containing resin selected from the group consisting of: i. a furan resin prepared by reaction of furfuryl alcohol with a C 1 to C 3 aliphatic aldehyde, and ii. a furan modified resin prepared by reaction of a phenol and a C 1 to C 3 aliphatic aldehyde to produce a resole resin and then reacting the resole resin with furfuryl alcohol; and b. blending with the furan-containing resin with a novolak resin prepared by reaction of a phenol with a C 1 to C 3 aliphatic aldehyde, with the ratio of the toal of the aldehyde contained in the furan-containing resin and the novolak resin to the phenol of the novolak resin and the furfuryl alcohol of the furan-containing resin being within the range of 0.5 to 0.85 and the ratio of furfuryl alcohol of the furan-containing resin to the phenol of the novolak resin is within the range of 0.04 to 0.9; and 2. a curing agent.
Claim 15
Dependent Claim
14 words
A resin coated sand as defined in claim 11 wherein the aldehyde is formaldehyde.
References Cited (Backward Citations)
CA477489A
Cited
US2453704A
Cited
US2566851A
Cited
US2745816A
Cited
US2861977A
Cited
US2834741A
Cited
GB824261A
Cited
US2970121A
Cited
US3299167A
Cited
US3312650A
Cited
US3549584A
Cited
US3725333A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-26 | 1981-03-28 | 1981-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-26 | 1985-03-28 | 1985-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-26 | 1989-03-28 | 1989-09-27 | $7700.00 | Window Closed / Lapsed |