Strippable composite of polymeric materials for use in insulated electrical conductors, a method of forming the same and products thereof
Assignee: Vulkor Inc
•
Filing: 1975-08-28
•
Granted: 1977-09-27
•
Expires: 1995-08-28
Abstract
Abstract A composite of polymeric materials which are adheringly joined to each other and which can be easily and cleanly separated by stripping apart with a low pulling force whereupon the contacting surfaces of their interface separate cleanly without retention of any residue on one from the other, and which comprises the combination of a previously cured body of a copolymer of ethylene and propylene adjoined to a subsequently cured body of an elastomeric blend of a copolymer of ethylene and propylene admixed with chlorosulfonated polyethylene. The combination of materials is especially advantageous when used in electrically conducting wire and cable constructions as a composite of an electrical insulation and an overlying strippable semiconductive layer.
Inventors
- 👤 Thaddeus Dominick Misiura
- 👤 Joseph Edward Vostovich
- 👤 Ralph Edward Wahl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:10
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/44; H01B3/441; C; C09; C09D; C09D5/00; C09D5/20; H01B9/00; H01B9/02; H01B9/027; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24851; Y10T428/2486; Y10T428/28; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294; Y10T428/2942; Y10T428/2947; Y10T428/31504; Y10T428/31678; Y10T428/31692; Y10T428/31699; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/31917; Y10T428/3192
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
152 words
An easily and cleanly strippable composite of cured polymeric materials comprising a body of a copolymer of ethylene and propylene having an ethylene content of not more than about 50% by weight with a surface adheringly joined to a contacting surface of a body comprising an elastomeric blend of about 20 to about 40 parts by weight of a copolymer of ethylene and propylene admixed with about 60 to about 80 parts by weight of chlorosulfonated polyethylene, said contacting surfaces of the bodies of polymeric materials being adheringly joined at their contacting surfaces by applying the body of the elastomeric blend while in an uncured condition to the body of the copolymer of ethylene and propylene in a cured condition and thereafter curing said body of the elastomer blend while a surface thereof is in adjoining physical contact with a surface of the cured body of the copolymer of ethylene and propylene.
Claim 2
Dependent Claim
152 words
An easily and cleanly strippable composite of cured polymeric materials comprising a body of a copolymer of ethylene and propylene having an ethylene content of not more than about 50% by weight with a surface adheringly joined to a contacting surface of a body comprising an elastomeric blend of about 20 to about 40 parts by weight of a copolymer of ethylene and propylene admixed with about 60 to about 80 parts by weight of chlorosulfonated polyethylene, said contacting surfaces of the bodies of polymeric materials being adheringly joined at their contacting surfaces by applying the body of the elastomeric blend while in an uncured condition to the body of the copolymer of ethylene and propylene in a cured condition and thereafter curing said body of the elastomer blend while a surface thereof is in adjoining physical contact with a surface of the cured body of the copolymer of ethylene and propylene.
Claim 3
Dependent Claim
39 words
The easily and cleanly strippable composite of cured polymeric materials of claim 1, wherein said elastomeric blend comprises about 35 parts by weight of copolymer of ethylene and propylene admixed with about 65 parts by weight of chlorosulfonated polyethylene.
Claim 4
Dependent Claim
38 words
The easily and cleanly strippable composite of cured polymeric materials of claim 1, wherein said polymeric material of the body of a copolymer of ethylene and propylene comprising approximately equal parts by weight of copolymerized ethylene and propylene.
Claim 5
Dependent Claim
142 words
An easily and cleanly strippable composite of cured polymeric materials comprising a body of a copolymer of ethylene and propylene in approximately equal parts by weight with a surface adheringly joined to a contacting surface of a body comprising an elastomeric blend of about 20 to about 40 parts by weight of a copolymer of ethylene and propylene admixed with about 60 to about 80 parts by weight of chlorosulfonated polyethylene, said contacting surfaces of the bodies of polymeric materials being adheringly joined by applying the body of the elastomeric blend while in an uncured condition to the body of the copolymer of ethylene and propylene in a cured condition and thereafter curing said body of the elastomeric blend while a surface thereof is in adjoining physical contact with a surface of the cured body of the copolymer of ethylene and propylene.
Claim 6
Dependent Claim
142 words
An easily and cleanly strippable composite of cured polymeric materials comprising a body of a copolymer of ethylene and propylene in approximately equal parts by weight with a surface adheringly joined to a contacting surface of a body comprising an elastomeric blend of about 20 to about 40 parts by weight of a copolymer of ethylene and propylene admixed with about 60 to about 80 parts by weight of chlorosulfonated polyethylene, said contacting surfaces of the bodies of polymeric materials being adheringly joined by applying the body of the elastomeric blend while in an uncured condition to the body of the copolymer of ethylene and propylene in a cured condition and thereafter curing said body of the elastomeric blend while a surface thereof is in adjoining physical contact with a surface of the cured body of the copolymer of ethylene and propylene.
Claim 7
Independent Claim
141 words
A method of preparing an easily and cleanly strippable composite or cured polymeric materials comprising a body of a copolymer of ethylene and propylene having an ethylene content of not more than about 50% by weight with a surface adhereingly joined to a contacting surface of a body comprising an elastomeric blend of about 20 to about 40 parts by weight of a copolymer of ethylene and propylene admixed with about 60 to about 80 parts by weight of chlorosulfonated polyethylene, comprising curing a body of said copolymer of ethylene and propylene, applying to a surface of said cured body of copolymer of ethylene and propylene a body comprising said elastomeric blend in an uncured condition, and while the surfaces of said bodies of cured and uncured polymeric materials are in adjoining physical contact, curing said body of uncured elastomeric blend.
Claim 8
Independent Claim
141 words
A method of preparing an easily and cleanly strippable composite or cured polymeric materials comprising a body of a copolymer of ethylene and propylene having an ethylene content of not more than about 50% by weight with a surface adhereingly joined to a contacting surface of a body comprising an elastomeric blend of about 20 to about 40 parts by weight of a copolymer of ethylene and propylene admixed with about 60 to about 80 parts by weight of chlorosulfonated polyethylene, comprising curing a body of said copolymer of ethylene and propylene, applying to a surface of said cured body of copolymer of ethylene and propylene a body comprising said elastomeric blend in an uncured condition, and while the surfaces of said bodies of cured and uncured polymeric materials are in adjoining physical contact, curing said body of uncured elastomeric blend.
Claim 9
Dependent Claim
43 words
The method of preparing an easily and cleanly strippable composite of cured polymeric materials of claim 5, wherein said elastomeric blend comprises about 35 parts by weight of copolymer of ethylene and propylene admixed with about 65 parts by weight of chlorosulfonated polyethylene.
Claim 10
Dependent Claim
42 words
The method of preparing an easily and cleanly strippable composite of cured polymeric materials of claim 5, wherein the polymeric material of the body of a copolymer of ethylene and propylene comprising approximately equal parts by weight to copolymerized ethylene and propylene.
References Cited (Backward Citations)
US2635975A
Cited
US2888424A
Cited
US3079370A
Cited
US2897100A
Cited
US3551284A
Cited
JPS4415467Y1
Cited
US3592728A
Cited
US3840694A
Cited
US3793476A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-26 | 1981-03-28 | 1981-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-26 | 1985-03-28 | 1985-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-26 | 1989-03-28 | 1989-09-27 | $7700.00 | Window Closed / Lapsed |