Method of measuring vapor deposited coating thickness
Assignee: Jones and Laughlin Steel Inc
•
Filing: 1972-10-10
•
Granted: 1977-09-27
•
Expires: 1992-10-10
Abstract
Abstract The temperature of a substrate to be vacuum vapor coated is measured immediately before its is passed over a source of coating metal vapor and immediately after the vapor has condensed on it. Costing conditions are controlled to maintain the difference between those temperatures at a value which is related to the thickness of the condensed coating by a heat balance equation.
Inventors
- 👤 John F. Butler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:40
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/56; C23C14/562; C23C14/54; C23C14/542
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
349 words
A method of vacuum vapor coating a thin metal substrate in strip form with a metal coating of a desired thickness without heating the substrate over about 1000° F comprising: measuring the temperature of the substrate immediately before coating; moving the substrate past a source which contains a pool of liquid coating metal which gives off metal vapor at its surface so as to condense coating metal on the substrate, to form a coating of said metal on said substrate, to supply heat to the substrate, and to increase the temperature of the substrate; immediately thereafter measuring the increase in temperature of the substrate resulting therefrom under conditions where temperature equilibrium through the substrate thickness is reached in less than 0.1 second and substrate heat loss is negligible; adjusting coating conditions to obtain the desired metal coating thickness in accordance with the equation, ##EQU4## t c is the thickness of the coating in mils, C st is the average heat capacity of the substrate for temperatures between T o and T f in BTU's per pound per degree F., T f is the final temperature of the substrate immediately after coating in degrees F., T o is the temperature of the substrate immediately before coating in degrees F., ρ st is the density of the substrate in pounds per cubic inch, t st is the thickness of the substrate in mils, ρ c is the density of the coatng metal in pounds per cubic inch, C k is the heat of condensation of the coating metal at T c in BTU's per pound, C c is the average heat capacity of the solid coating metal for temperatures between T f and T o in BTU's per pound per degree F., and T c is the temperature of condensation of the coating metal in degrees F.; and measuring the increase in temperature of the substrate caused by radiation from the vapor source, subtracting said temperature increase caused by radiation from T f , as defined above, to obtain a value, and using said value for T f in the equation.
Claim 2
Independent Claim
349 words
A method of vacuum vapor coating a thin metal substrate in strip form with a metal coating of a desired thickness without heating the substrate over about 1000° F comprising: measuring the temperature of the substrate immediately before coating; moving the substrate past a source which contains a pool of liquid coating metal which gives off metal vapor at its surface so as to condense coating metal on the substrate, to form a coating of said metal on said substrate, to supply heat to the substrate, and to increase the temperature of the substrate; immediately thereafter measuring the increase in temperature of the substrate resulting therefrom under conditions where temperature equilibrium through the substrate thickness is reached in less than 0.1 second and substrate heat loss is negligible; adjusting coating conditions to obtain the desired metal coating thickness in accordance with the equation, ##EQU4## t c is the thickness of the coating in mils, C st is the average heat capacity of the substrate for temperatures between T o and T f in BTU's per pound per degree F., T f is the final temperature of the substrate immediately after coating in degrees F., T o is the temperature of the substrate immediately before coating in degrees F., ρ st is the density of the substrate in pounds per cubic inch, t st is the thickness of the substrate in mils, ρ c is the density of the coatng metal in pounds per cubic inch, C k is the heat of condensation of the coating metal at T c in BTU's per pound, C c is the average heat capacity of the solid coating metal for temperatures between T f and T o in BTU's per pound per degree F., and T c is the temperature of condensation of the coating metal in degrees F.; and measuring the increase in temperature of the substrate caused by radiation from the vapor source, subtracting said temperature increase caused by radiation from T f , as defined above, to obtain a value, and using said value for T f in the equation.
Claim 3
Dependent Claim
18 words
The method of claim 1 in which the coating condition adjusted is the speed of the moving substrate.
Claim 4
Dependent Claim
22 words
The method of claim 1 in which the coating condition adjusted is the heat input to the source of coating metal vapor.
Claim 5
Dependent Claim
91 words
The method of claim 3 in which the source of coating metal vapor is a plurality of units aligned transversely of the path of travel of the substrate so that each unit supplies vapor to a separate portion of the substrate, and comprising separately measuring the temperatures of at least two portions of the substrate immediately before coating and immediately after coating and separately adjusting the heat inputs to each of the units to provide a predetermined ratio between the quantities T f -T o for each portion of the substrate.
Claim 6
Dependent Claim
16 words
The method of claim 1 in which the metal substrate thickness is less than 0.05 inch.
Claim 7
Dependent Claim
48 words
The method of claim 1 in which measuring the increase in temperature of the substrate caused by radiation from the vapor source is accomplished by measuring the temperature difference before and after passing the substrate over an empty vapor source unit which has been heated to evaporation temperature.
Claim 8
Dependent Claim
19 words
The method of claim 1 in which the increase in temperature of the substrate is up to 350° F.
Claim 9
Dependent Claim
12 words
The method of claim 1 in which the metal coating comprises aluminum.
Claim 10
Dependent Claim
33 words
The method of claim 8 in which said steel substrate temperature increase minus said steel substrate temperature increase caused by radiation from the vapor source is from about 20° to about 100° F.
Claim 11
Dependent Claim
12 words
The method of claim 1 in which the metal coating comprises zinc.
Claim 12
Dependent Claim
12 words
The method of claim 1 in which the metal substrate comprises steel.
Claim 13
Dependent Claim
12 words
The method of claim 11 in which the metal coating comprises aluminum.
Claim 14
Dependent Claim
12 words
The method of claim 11 in which the metal coating comprises zinc.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-26 | 1981-03-28 | 1981-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-26 | 1985-03-28 | 1985-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-26 | 1989-03-28 | 1989-09-27 | $7700.00 | Window Closed / Lapsed |