Water reducible short oil alkyd resins and process of making same
Assignee: Valspar Corp
•
Filing: 1975-04-21
•
Granted: 1977-09-27
•
Expires: 1995-04-21
Abstract
Abstract Water reducible alkyd resin composition comprising the reaction product of from about 10-15 wt. %, based on total weight of reactants, of a polyethylene glycol, from about 20-25 wt. % of a triglyceride, e.g., soya oil, based on total wt. % of reactants, from about 18 to 23 wt. %, based on total weight of reactants, of a polyol, e.g., glycerine, and from about 43-48 wt. %, based on total weight of reactants, of an aromatic dicarboxylic acid, e.g., isophthalic, and process of making same; said alkyd resin being highly useful for coating formulations.
Inventors
- 👤 Michael A. Tobias
- 👤 Carlos J. Martinez
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:23
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/66; C08G63/668; C08K; C08K5/00; C08K5/16; C08K5/34; C09; C09D; C09D167/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678; Y10T428/31681
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
125 words
A water reducible short oil alkyd resin consisting essentially of the reaction product of from about 10-15 wt. % based on the total weight of the reactants of a polyethylene glycol having a molecular weight between about 200-2000; from about 20-25 wt. % based on the total weight of the reactants of a triglyceride having from about 30-60 carbon atoms; from about 18-23 wt. % based on the total weight of the reactants of a polyol having from about 2 to about 6 hydroxy groups; and from about 43-48 wt. % based on the total weight of the reactants of an aromatic dicarboxylic acid or anhydride having from about 8-12 carbon atoms; said resin having an alcoholic acid number between about 45 and about 65.
Claim 2
Dependent Claim
125 words
A water reducible short oil alkyd resin consisting essentially of the reaction product of from about 10-15 wt. % based on the total weight of the reactants of a polyethylene glycol having a molecular weight between about 200-2000; from about 20-25 wt. % based on the total weight of the reactants of a triglyceride having from about 30-60 carbon atoms; from about 18-23 wt. % based on the total weight of the reactants of a polyol having from about 2 to about 6 hydroxy groups; and from about 43-48 wt. % based on the total weight of the reactants of an aromatic dicarboxylic acid or anhydride having from about 8-12 carbon atoms; said resin having an alcoholic acid number between about 45 and about 65.
Claim 3
Dependent Claim
42 words
The resin of claim 1 wherein the polyethylene glycol has a molecular weight of from about 380-420; the triglyceride is selected from the group consisting of Safflower Oil and Soya Oil; the polyol is glycerine; and the dicarboxylic acid is isophthalic acid.
Claim 4
Dependent Claim
42 words
The resin of claim 1 wherein the polyethylene glycol has a molecular weight of from about 570-630; the triglyceride is selected from the group consisting of Safflower Oil and Soya Oil; the polyol is glycerine; and the dicarboxylic acid is isophthalic acid.
Claim 5
Dependent Claim
11 words
The resin of claim 3 wherein the triglyceride is Soya Oil.
Claim 6
Dependent Claim
42 words
The resin of claim 1 wherein the polyethylene glycol has a molecular weight of from about 1300-1600; the triglyceride is selected from the group consisting of Safflower Oil and Soya Oil; the polyol is glycerine; and the dicarboxylic acid is isophthalic acid.
Claim 7
Dependent Claim
11 words
The resin of claim 5 wherein the triglyceride is Safflower Oil.
Claim 8
Dependent Claim
27 words
The resin of claim 1 comprising the following reactants: polyethylene glycol having a molecular weight between about 400-1500, Soya Oil or Safflower Oil, glycerine and isophthalic acid.
Claim 9
Dependent Claim
160 words
A process for the preparation of a water reducible short oil alkyd resin consisting essentially of initially reacting a polyethylene glycol having a molecular weight between about 200-2000 in an amount between about 10-15 wt. % based on the total weight of the reactants; a C 30 -C 60 triglyceride in an amount between about 18-23 wt. % based on the total weight of the reactants; and a polyol having from about 2-6 hydroxy groups in an amount between about 15-20 wt. % based on the total weight of the reactants at a temperature between about 200° C. and 230° C. for about 30-40 minutes; and subsequently reacting the product with a C 8 -C 12 dicarboxylic acid or anhydride in an amount between about 43-48 wt. % based on the total weight of the reactants at a temperature between about 215° C. and about 225° C., until an alcoholic acid number between about 45 and about 65 is attained.
Claim 10
Dependent Claim
160 words
A process for the preparation of a water reducible short oil alkyd resin consisting essentially of initially reacting a polyethylene glycol having a molecular weight between about 200-2000 in an amount between about 10-15 wt. % based on the total weight of the reactants; a C 30 -C 60 triglyceride in an amount between about 18-23 wt. % based on the total weight of the reactants; and a polyol having from about 2-6 hydroxy groups in an amount between about 15-20 wt. % based on the total weight of the reactants at a temperature between about 200° C. and 230° C. for about 30-40 minutes; and subsequently reacting the product with a C 8 -C 12 dicarboxylic acid or anhydride in an amount between about 43-48 wt. % based on the total weight of the reactants at a temperature between about 215° C. and about 225° C., until an alcoholic acid number between about 45 and about 65 is attained.
Claim 11
Dependent Claim
60 words
The process of claim 8 wherein the polyethylene glycol has a molecular weight between about 350-1500, the triglyceride is selected from the group consisting of Soya Oil and Safflower Oil; the aromatic dicarboxylic component is selected from the group consisting of isophthalic acid and phthalic anhydride, and the polyol is selected from the group consisting of glycerine and propylene glycol.
Claim 12
Dependent Claim
18 words
The process of claim 9 wherein the polyol is glycerine; and the aromatic dicarboxylic component is isophthalic acid.
Claim 13
Dependent Claim
14 words
A paint vehicle containing a water reducible alkyd resin as defined in claim 1.
Claim 14
Dependent Claim
13 words
A paint vehicle as defined in claim 11 containing a suitable crosslinking agent.
References Cited (Backward Citations)
US2634245A
Cited
US3001961A
Cited
US3077459A
Cited
US3379548A
Cited
US3297605A
Cited
US3224992A
Cited
US3223659A
Cited
US3310512A
Cited
US3437615A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-26 | 1981-03-28 | 1981-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-26 | 1985-03-28 | 1985-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-26 | 1989-03-28 | 1989-09-27 | $7700.00 | Window Closed / Lapsed |