Electrical temperature measuring resistor structure, particularly for resistance thermometers
Assignee: WC Heraus GmbH and Co KG
•
Filing: 1976-06-14
•
Granted: 1977-09-20
•
Expires: 1996-06-14
Abstract
Abstract A substrate carrier of electrically non-conductive material has a strip of resistance platinum applied thereto; in order to avoid the use of an intermediate temperature coefficient of expansion matching layer, the substrate carrier, for example of aluminum oxide, beryllium oxide, or a magnesium silicate, has less than thirty parts per million (ppm) Fe, less than 15 ppm Cr, less than 45 ppm Pb and less than 70 ppm Si in a form capable of reacting with platinum, the sum of the impurities by these metals, if all, or more than one are present, not exceeding 20 ppm; the average thermal coefficient of expansion of the substrate does not deviate from the mean thermal coefficient of expansion of the thermometer grade platinum by more than ± 30%; the platinum layer has a thickness of from 0.1 to 10 μm, and is applied at a temperature in the range of between about 1000° C to 1400° C during 60 minutes in an atmosphere containing oxygen, for example free air.
Inventors
- 👤 Walter Reichelt
- 👤 Gunter Sauer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 03:09
CPC Classifications
G; G01; G01K; G01K7/00; G01K7/16; G01K7/18; H; H01; H01C; H01C17/00; H01C17/06; H01C17/075; H01C17/08; H01C17/12; H01C7/00; H01C7/22
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
136 words
Electrical measuring resistor structure for use in resistance thermometers having a carrier (1) of electrically non-conductive material and a strip of platinum resistance layer (2) applied to the carrier in a predetermined pattern, and comprising the improvement wherein the carrier comprises a substrate (1) which includes less than 30 parts per million (ppm) Fe, less than 15 ppm Cr, less than 45 ppm Pb and less than 70 ppm Si in a form which can react with the platinum and wherein the sum of said named materials, if more than one is present, does not exceed 20 ppm; the platinum layer has a thickness of between 0.1 and 10 μm; and the mean thermal coefficient of expansion of the substrate differs from the coefficient of expansion of the thermal platinum by less than about ± 30%.
Claim 2
Dependent Claim
136 words
Electrical measuring resistor structure for use in resistance thermometers having a carrier (1) of electrically non-conductive material and a strip of platinum resistance layer (2) applied to the carrier in a predetermined pattern, and comprising the improvement wherein the carrier comprises a substrate (1) which includes less than 30 parts per million (ppm) Fe, less than 15 ppm Cr, less than 45 ppm Pb and less than 70 ppm Si in a form which can react with the platinum and wherein the sum of said named materials, if more than one is present, does not exceed 20 ppm; the platinum layer has a thickness of between 0.1 and 10 μm; and the mean thermal coefficient of expansion of the substrate differs from the coefficient of expansion of the thermal platinum by less than about ± 30%.
Claim 3
Dependent Claim
24 words
Structure according to claim 1, wherein the substrate comprises at least one of: aluminum oxide, beryllium oxide, thorium oxide, magnesium oxide, a magnesium silicate.
Claim 4
Dependent Claim
31 words
Structure according to claim 1, further comprising a cover layer (3) for protection of the strip of platinum (2) and the substrate, said cover being high temperature and mechanical wear resistant.
Claim 5
Dependent Claim
22 words
Structure according to claim 3, wherein the cover layer (3) comprises metal oxides of at least one: aluminum, beryllium, thorium, rare earths.
Claim 6
Dependent Claim
11 words
Structure according to claim 1, wherein the substrate comprises aluminum oxide.
Claim 7
Dependent Claim
19 words
Structure according to claim 1, wherein the platinum layer has a thickness of between 1 to 5 μ m.
Claim 8
Dependent Claim
43 words
Structure according to claim 1, wherein the substrate (1) with the strip of platinum (2) applied, is heated in an oxygen-containing atmosphere to a temperature in the range of between about 1000° to 1400° C. for a period of at least 60 minutes.
Claim 9
Dependent Claim
31 words
Structure according to claim 1, wherein the substrate (1) during application of the strip (2) of platinum is at a temperature in the range of about between 500° to 900° C.
Claim 10
Dependent Claim
21 words
Structure according to claim 1, wherein the substrate (1) before application of the strip (2) of platinum is heat-treated in air.
Claim 11
Dependent Claim
39 words
Structure according to claim 1, wherein the substrate (1) with the strip (2) of platinum applied thereto is heated in air to a temperature of between about 1050° to about 1150° C. for a period of about 3 hours.
Claim 12
Dependent Claim
76 words
Structure according to claim 2, further comprising a metal oxide cover layer (3) including at least one of: aluminum oxide, beryllium oxide, thorium oxide, an oxide of a rare earth; the platinum strip (2) has a thickness of between 1 to 5 μm, and the substrate (1) with the strip of platinum (2) applied thereto is heated in air to a temperature of between about 1050° to 1150° C. for a period of about 3 hours.
Claim 13
Dependent Claim
11 words
Structure according to claim 11, wherein the substrate comprises aluminum oxide.
Claim 14
Dependent Claim
141 words
Method to make a resistor structure, particularly for resistance thermometers having a substrate (1) which includes less than 30 parts per million (ppm) Fe, less than 15 ppm Cr, less than 45 ppm Pb and less than 70 ppm Si in a form which can react with the platinum and wherein the sum of said named materials, if more than one is present, does not exceed 20 ppm; the platinum layer has a thickness of between 0.1 and 10 μm; and the mean thermal coefficient of expansion of the substrate differs from the coefficient of expansion of the thermal platinum by less than about ±30%; and wherein the substrate (1) with the strip of platinum (2) applied thereto is heated to a temperature in the range of about 1000° to 1400° C. in an atmosphere containing oxygen for about 1 hour.
Claim 15
Dependent Claim
141 words
Method to make a resistor structure, particularly for resistance thermometers having a substrate (1) which includes less than 30 parts per million (ppm) Fe, less than 15 ppm Cr, less than 45 ppm Pb and less than 70 ppm Si in a form which can react with the platinum and wherein the sum of said named materials, if more than one is present, does not exceed 20 ppm; the platinum layer has a thickness of between 0.1 and 10 μm; and the mean thermal coefficient of expansion of the substrate differs from the coefficient of expansion of the thermal platinum by less than about ±30%; and wherein the substrate (1) with the strip of platinum (2) applied thereto is heated to a temperature in the range of about 1000° to 1400° C. in an atmosphere containing oxygen for about 1 hour.
Claim 16
Dependent Claim
28 words
Method according to claim 13, wherein the substrate, during deposition of the strip of platinum (2) has a temperature in the range of about 500° to 900° C.
Claim 17
Dependent Claim
21 words
Method according to claim 14, wherein the strip of platinum is applied by vapor deposition by means of electron beam heating.
Claim 18
Dependent Claim
25 words
Method according to claim 13, further comprising the step of heat-treating the substrate (1) before application of the strip of platinum (2) thereto in air.
Claim 19
Dependent Claim
53 words
Method according to claim 15, wherein the platinum strip (2) has a thickness of between 1 to 5 μ and the substrate (1) with the strip of platinum applied thereto is heated in air to a temperature of between about 1050° to 1150° C. for a period of time of about 3 hours.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-19 | 1981-03-21 | 1981-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-19 | 1985-03-21 | 1985-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-19 | 1989-03-21 | 1989-09-20 | $7700.00 | Window Closed / Lapsed |