Process for producing a highly oriented polyester undrawn yarn

Claim 2

In a process for producing a highly oriented polyester undrawn yarn, in which said yarn is spun from a spinneret to a first take-up, the steps which comprise: melt-spinning a polyester from a spinneret, solidifying the melt-spun yarn and taking up the solidified yarn at a take-up velocity from about 2,500 to 4,500 m/min, wherein the spinning length defined by the distance from said spinneret to said first take-up is within the range from about (d + 2)/4 (in meters) to about (A/1.2)/(Faero/x) (in meters), wherein d is the filament denier of the undrawn yarn, A is the tension (in grams) of the filament in an elongation range under constant tension of a stress-strain curve, Faero/x is the rate of increase of the yarn tension per meter following the yarn solidification point by an air resistance which is equal to 0.229 × 10 -4 .D 0 .39 ·V 1 .39, wherein D is the solidified filament diameter (in cm) and V is the velocity of the solidified filament (in cm/sec), wherein the filament denier of the undrawn yarn is within the range from about 2 to 6.

Claim 3

A process according to claim 1, wherein the spinning length is within the range from about (d + 2)/4 (meter) to about (A/1.4)/(Faero/x) (meter).

Claim 4

In a process for producing a highly oriented polyester undrawn yarn having a filament denier of about 2 to 6, in which said yarn is spun from a spinneret to a first take-up roller, the steps which comprise melt-spinning a polyester from a spinneret, solidifying the melt-spun yarn, passing the solidified yarn through a guide arranged to cause the yarn to bend through an angle of at least about 5°, and taking up the solidified yarn at a take-up velocity from about 2,500 to 4,500 m/min, wherein the spinning length defined by the distance from said spinneret to said first take-up roller is within the range from about (d + 2)/4 (in meters) to the lower value of either (A/1.2)/(Faero/x) (in meters) or B/(Faero/x) in meters), wherein d is the filament denier of the undrawn yarn, A is the tension (in grams) of the filament in the elongation range under a constant tension of a stress-strain curve, B is the maximum allowable tension (in grams) of the undrawn filament when a maximum allowable tension at said guide is 0.3 g/d, and Faero/x is the rate of increase of yarn tension per meter following the yarn solidifying point by an air resistance which is equal to 0.229 × 10 -4 ·D 0 .39 ·V 1 .39, wherein D is the diameter of the solidified filament (in cm) and V is the velocity of the solidified filament (in cm/sec).

Claim 5

In a process for producing a highly oriented polyester undrawn yarn having a filament denier of about 2 to 6, in which said yarn is spun from a spinneret to a first take-up roller, the steps which comprise melt-spinning a polyester from a spinneret, solidifying the melt-spun yarn, passing the solidified yarn through a guide arranged to cause the yarn to bend through an angle of at least about 5°, and taking up the solidified yarn at a take-up velocity from about 2,500 to 4,500 m/min, wherein the spinning length defined by the distance from said spinneret to said first take-up roller is within the range from about (d + 2)/4 (in meters) to the lower value of either (A/1.2)/(Faero/x) (in meters) or B/(Faero/x) in meters), wherein d is the filament denier of the undrawn yarn, A is the tension (in grams) of the filament in the elongation range under a constant tension of a stress-strain curve, B is the maximum allowable tension (in grams) of the undrawn filament when a maximum allowable tension at said guide is 0.3 g/d, and Faero/x is the rate of increase of yarn tension per meter following the yarn solidifying point by an air resistance which is equal to 0.229 × 10 -4 ·D 0 .39 ·V 1 .39, wherein D is the diameter of the solidified filament (in cm) and V is the velocity of the solidified filament (in cm/sec).