Silver halide activated photochromic plastics
Assignee: American Optical Corp
•
Filing: 1976-03-17
•
Granted: 1977-09-20
•
Expires: 1996-03-17
Abstract
Abstract Photochromic plastic materials are disclosed which comprise a polymeric matrix containing a multiplicity of activated silver halide particles less than 1000 Angstroms in size. The matrix may contain a retained amount of plasticizer which optimizes the desirable photochromic properties and may be sealed to prevent loss of plasticizer. The materials are made by forming activated silver halide particles in the presence of a film forming polymer dissolved in a plasticizer and removing the plasticizer to produce a supple, shape-retaining element.
Inventors
- 👤 Nori Y. C. Chu
- 👤 Peter G. Piusz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 07:38
CPC Classifications
C; C09; C09K; C09K9/00; G; G03; G03C; G03C1/00; G03C1/705
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
79 words
A photochromic plastic element comprising a plurality of photosensitive silver halide particles less than 1000 A in particle size containing activating ions which act as hole traps, said particles being dispersed within a cast, shape-retaining, light-transmissive matrix comprising at least one polymer having the ability to inhibit ripening of silver halide particles produced in solution, said matrix containing an effective amount of a plasticizer to produce an environment suitable for repetitive activations and deactivations of the silver halide particles.
Claim 2
Dependent Claim
79 words
A photochromic plastic element comprising a plurality of photosensitive silver halide particles less than 1000 A in particle size containing activating ions which act as hole traps, said particles being dispersed within a cast, shape-retaining, light-transmissive matrix comprising at least one polymer having the ability to inhibit ripening of silver halide particles produced in solution, said matrix containing an effective amount of a plasticizer to produce an environment suitable for repetitive activations and deactivations of the silver halide particles.
Claim 3
Dependent Claim
21 words
The photochromic element of claim 1 wherein said light-transmissive matrix includes an amount of plasticizer effective to render said matrix non-brittle.
Claim 4
Dependent Claim
19 words
The photochromic element of claim 2 further comprising means for sealing said material to prevent loss of said plastisizer.
Claim 5
Dependent Claim
62 words
The photochromic element of claim 1 wherein the Ag + ion in said silver halide particles is replaced with up to 50 ion percent of an ion chosen from the group consisting of Li + Na + K + Rb + Cs + Tl + Ca ++ Mg ++ Sr ++ Ba ++ Zn ++ Be ++ Cu ++ and mixtures thereof.
Claim 6
Dependent Claim
44 words
The photochromic element of claim 1 wherein the Ag + ion in said silver halide particles is replaced with up to 10 ion percent of an ion chosen from the group consisting of Cu + Fe ++ Cd ++ S -- and mixtures thereof.
Claim 7
Dependent Claim
24 words
The photochromic element of claim 1 wherein the silver halide particle is chosen from the group consisting of AgCl, AgBr, AgI, and mixtures thereof.
Claim 8
Dependent Claim
26 words
The photochromic element of claim 1 wherein said silver halide particles contain copper ions, said matrix comprises polyvinylpyrrolidone, and said polyvinylpyrrolidone contains water as a plasticizer.
Claim 9
Dependent Claim
16 words
The photochromic element of claim 1 wherein said matrix contains a plasticizer having hydroxy functional groups.
Claim 10
Dependent Claim
22 words
The photochromic element of claim 8 wherein said plasticizer is chosen from the group consisting of glycerin, ethylene glycol, and polyethylene glycol.
Claim 11
Dependent Claim
17 words
The photochromic element of claim 1 encased in a transparent material to form a photochromic optical device.
Claim 12
Dependent Claim
27 words
The photochromic element of claim 1 wherein said polymer is chosen from the group consisting of polyvinylpyrrolidone, polyvinylalcohol, polyacrylic acids, polymethacrylic acids, polyalkylenamines, polyalkylenimines, and mixtures thereof.
Claim 13
Dependent Claim
86 words
A process for producing a photochromic plastic element comprising the steps of: forming photosensitive silver halide crystals containing activating ions which act as hole traps, said crystals being less than 1000 A in particle size and being formed in a solution of a light transmissive polymer capable of acting as a ripening inhibitor for the formation of silver halide grains and dissolved in a plasticizer therefor; casting said solution; and removing an effective amount of said plasticizer to form a cast, non-brittle, shape retaining photochromic element.
Claim 14
Dependent Claim
86 words
A process for producing a photochromic plastic element comprising the steps of: forming photosensitive silver halide crystals containing activating ions which act as hole traps, said crystals being less than 1000 A in particle size and being formed in a solution of a light transmissive polymer capable of acting as a ripening inhibitor for the formation of silver halide grains and dissolved in a plasticizer therefor; casting said solution; and removing an effective amount of said plasticizer to form a cast, non-brittle, shape retaining photochromic element.
Claim 15
Dependent Claim
26 words
The process of claim 12 wherein said polymer is chosen from the group consisting of polyvinylpyrrolidone, polyvinylalcohol, polyacrylic acids, polymethacrylic acids, polyalkylenamines, polyalkylenimines, and mixtures thereof.
Claim 16
Dependent Claim
18 words
The process of claim 12 further comprising the step of encasing said element to prevent loss of plasticizer.
Claim 17
Dependent Claim
30 words
The process of claim 12 wherein said forming step is effected by adding a solubilized halide salt, a solubilized silver salt, and a solubilized copper salt together in said solution.
Claim 18
Dependent Claim
55 words
The process of claim 12 wherein the crystals formed contain an ion chosen from the group consisting of Cu + Li + Na + K + Rb + Cs + Tl + Cu ++ Ca ++ Mg ++ Sr ++ Ba ++ Zn ++ Cd ++ Be ++ Fe ++ S -- and mixtures thereof.
Claim 19
Dependent Claim
10 words
The process of claim 12 wherein said plasticizer is water.
Claim 20
Dependent Claim
21 words
The process of claim 13 wherein said plasticizer is chosen from the group consisting of plasticizers which contain hydroxy functional groups.
Claim 21
Dependent Claim
23 words
The process of claim 18 wherein said plasticizer is chosen from the group consisting of glycerin, ethylene glycols, polyethylene glycols, and mixtures thereof.
Claim 22
Dependent Claim
19 words
The process of claim 12 wherein said solution comprises water and a water soluble plasticiizer compatible with said polymer.
Claim 23
Dependent Claim
115 words
Process for producing a photochromic plastic element comprising the steps of: forming a solution of a polymer chosen from the group consisting of polyvinylpyrrolidone and polyvinylalcohol, water, and a plasticizer chosen from the group consisting of glycerin, ethylene glycol, and polyethylene glycol; adding solutions containing Ag + ions, halides chosen from the group consiting of Br - Cl - I - and an activating ion chosen from the group consisting of Cu + Cd ++ Fe ++ S -- and mixtures thereof to form activated, photosensitive silver halide crystals having a particle size less than 1000 A in said polymer solution; and removing the water from the solution to form a non-brittle, shape-retaining plastic element.
Claim 24
Dependent Claim
115 words
Process for producing a photochromic plastic element comprising the steps of: forming a solution of a polymer chosen from the group consisting of polyvinylpyrrolidone and polyvinylalcohol, water, and a plasticizer chosen from the group consisting of glycerin, ethylene glycol, and polyethylene glycol; adding solutions containing Ag + ions, halides chosen from the group consiting of Br - Cl - I - and an activating ion chosen from the group consisting of Cu + Cd ++ Fe ++ S -- and mixtures thereof to form activated, photosensitive silver halide crystals having a particle size less than 1000 A in said polymer solution; and removing the water from the solution to form a non-brittle, shape-retaining plastic element.
Claim 25
Dependent Claim
20 words
The process of claim 21 further comprising the step of encasing said plastic element to form a photochromic optical device.
Claim 26
Dependent Claim
87 words
Process for producing a photochromic element comprising the steps of: forming an aqueous solution of at least one light transmissive water soluble polymer; adding aqueous solutions containing silver ions, halide ions, and copper ions to form activated, photosensitive silver halide particles less than 1000A particle size in said polymer solution; removing the water from the solution to form a plastic element containing an effective amount of water to maximize the photochromic properties of said element; and encasing said photochromic plastic element to prevent further loss of water.
Claim 27
Dependent Claim
87 words
Process for producing a photochromic element comprising the steps of: forming an aqueous solution of at least one light transmissive water soluble polymer; adding aqueous solutions containing silver ions, halide ions, and copper ions to form activated, photosensitive silver halide particles less than 1000A particle size in said polymer solution; removing the water from the solution to form a plastic element containing an effective amount of water to maximize the photochromic properties of said element; and encasing said photochromic plastic element to prevent further loss of water.
Claim 28
Dependent Claim
26 words
The process of claim 23 wherein said polymer is chosen from the group consisting of polyvinylpyrrolidone, polyvinylalcohol, polyacrylic acids, polymethacrylic acids, polyalkylenamines, polyalkylenimines, and mixtures thereof.
References Cited (Backward Citations)
CA888622A
Cited
US3479186A
Cited
US3508810A
Cited
US3540793A
Cited
US3723349A
Cited
US3666352A
Cited
US3716489A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-19 | 1981-03-21 | 1981-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-19 | 1985-03-21 | 1985-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-19 | 1989-03-21 | 1989-09-20 | $7700.00 | Window Closed / Lapsed |