Glass bonding of manganese-zinc ferrite
Assignee: Individual
•
Filing: 1976-06-21
•
Granted: 1977-09-20
•
Expires: 1996-06-21
Abstract
Abstract A method of minimizing or eliminating reactions between a surface of manganese zinc ferrite and a glass bonding composition applied thereto is disclosed, wherein a barrier layer is formed upon the manganese zinc ferrite surface prior to the application of the glass bonding composition. The barrier layer is a chromium layer about 3 - 170 microinches thick. The resulting product is suitable for use in radio frequency recording apparatus, and especially for multi-core magnetic heads.
Inventors
- 👤 Robert L. Huntt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:26
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/127; G11B5/187; G11B5/23; G11B5/235; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/4902; Y10T29/49021; Y10T29/49032; Y10T29/49055; Y10T29/49057
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
142 words
A process for increasing the wear resistance of a magnetic recording/reproducing head, said head comprising a core of magnetic hot-pressed manganese-zinc ferrite material having opposing pole faces defining at least one gap, while also minimizing or eliminating reaction between the manganese-zinc ferrite pole faces and a glass bonding composition applied thereto, said process comprising first forming a layer of chromium on the pole faces by R.F. sputtering the chromium thereon, each chromium layer being of a thickness of at least 25% of the width of said gap, and thereafter glass bonding the resulting chromium layers together by applying a high lead glass bonding composition at least 3 microinches thick to the area of the gap and firing the glass bonding agent at a temperature of no greater than about 700° C. to adhere the chromium layers together with the glass bonding agent.
Claim 2
Dependent Claim
142 words
A process for increasing the wear resistance of a magnetic recording/reproducing head, said head comprising a core of magnetic hot-pressed manganese-zinc ferrite material having opposing pole faces defining at least one gap, while also minimizing or eliminating reaction between the manganese-zinc ferrite pole faces and a glass bonding composition applied thereto, said process comprising first forming a layer of chromium on the pole faces by R.F. sputtering the chromium thereon, each chromium layer being of a thickness of at least 25% of the width of said gap, and thereafter glass bonding the resulting chromium layers together by applying a high lead glass bonding composition at least 3 microinches thick to the area of the gap and firing the glass bonding agent at a temperature of no greater than about 700° C. to adhere the chromium layers together with the glass bonding agent.
Claim 3
Dependent Claim
25 words
A process according to claim 1, wherein the high lead glass bonding agent is fired at a temperature of no greater than about 500° C.
Claim 4
Dependent Claim
28 words
A process according to claim 2, wherein said glass bonding composition is bonded to said chromium layers at a temperature of about 400° C. to about 500° C.
Claim 5
Dependent Claim
27 words
A process according to claim 1, wherein the total thickness of said chromium layers and said glass bonding composition layer is about 10 to about 500 microinches.
Claim 6
Dependent Claim
20 words
A process according to claim 4, wherein each chromium layer has a thickness of about 3 to about 170 microinches.
Claim 7
Dependent Claim
16 words
Process according to claim 5, wherein each chromium layer is about 5 to 100 microinches thick.
Claim 8
Dependent Claim
16 words
Process according to claim 6, wherein each chromium layer is about 10 to 70 microinches thick.
Claim 9
Dependent Claim
23 words
Process according to claim 1, wherein each of said chromium layers and the glass bonding composition layer are of substantially the same thickness.
Claim 10
Dependent Claim
26 words
Process according to claim 1, wherein the total thickness of said chromium layers and said glass bonding composition layer is about 40 to about 200 microinches.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-19 | 1981-03-21 | 1981-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-19 | 1985-03-21 | 1985-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-19 | 1989-03-21 | 1989-09-20 | $7700.00 | Window Closed / Lapsed |